混凝土用聚甲醛纤维的耐碱性能研究
Study on Alkali Resistance of Polyacetal Fiber for Concrete
2019年第12期
混凝土;聚甲醛纤维;耐碱性能;对应关系;微观形貌;红外测试
Concrete; Polyoxymethylene fiber; Alkali resistance; Correspondence; Microscopic morphology; Infrared test
2019年第12期
10.19761/j.1000-4637.2019.12.052.04
国家重点研发计划项目(2018YFD1101002-05、2016YFB0303104);国家自然科学基金项目(51578479、51708483)
王天琪1,杨鼎宜2,3,谈永泉1,范志勇1
1.苏州混凝土水泥制品研究院检测中心有限公司,215000;2.扬州大学 建筑科学与工程学院,225127;3.扬州大学 绿色建筑材料研究所,225127

王天琪1,杨鼎宜2,3,谈永泉1,范志勇1

王天琪,杨鼎宜,谈永泉,等.混凝土用聚甲醛纤维的耐碱性能研究[J].混凝土与水泥制品,2019(12):52-55.

WANG T Q,YANG D Y,TAN Y Q,et al.Study on Alkali Resistance of Polyacetal Fiber for Concrete[J].China Concrete and Cement Products,2019(12):52-55.

浏览量:
1000
摘  要:根据不同的水泥碱度设计了6种pH值的NaOH溶液对聚甲醛纤维(POM纤维)进行加速老化试验,同时用基准水泥上层清液做POM纤维的常温浸泡试验,通过测试浸泡前后纤维的直径和强度探究了POM纤维的耐碱性能,并对不同浸泡环境、不同浸泡时间下的纤维进行了微观形貌分析和红外测试,找出了不同浸泡条件下的时间对应关系。试验结果表明,POM纤维在两种浸泡环境下,随着时间的延长,直径逐渐增加,强度减小,POM纤维在pH=14的NaOH溶液中加温浸泡6h相当于在基准水泥上层清液中常温浸泡28d。POM纤维的腐蚀是一个逐层腐蚀的过程,碱溶液最先腐蚀纤维表面和内部杂质,其次腐蚀结构缺陷部分,发生C-O-C和CH2基团位移,导致纤维力学性能下降,但POM纤维整体结构骨架并没有受到严重腐蚀,具有较好的耐碱性能。Abstract:6kindsofNaOHsolutionwithpHaccordingtodifferentcementalkalinityweredesignedtoacceleratetheagingtestofPOMfiber,andthebenchmarkcementsupernatantwasusedtomakePOMfiberatroomtemperatureimmersiontest.ThealkaliresistanceofPOMfiberwasinvestigatedbytestingthediameterandstrengthofthefibersbeforeandaftersoaking.Microscopicmorphologyanalysisandinfraredtestingwereperformedonthefibersunderdifferentsoakingtimesindifferentsoakingenvironmentstofindoutthetimecorrespondenceunderdifferentsoakingconditions.TheresultsshowthatthePOMfibergraduallyincreasesindiameterandstrengthafterprolongingintwokindsofimmersionenvironments.POMfiberisimmersedinNaOHsolutionwithpH=14for6h,whichisequivalenttothereferencecementsupernatantatroomtemperaturefor28d.ThecorrosionofPOMfiberisalayer-by-layercorrosionprocess,thealkalisolutionfirstcorrodesthefibersurfaceandinternalimpurities,andsecondlycorrodesthestructuraldefects,andtheC-O-CandCH2 groupsaredisplaced,resultinginadecreaseinfibermechanicalproperties.However,theoverallstructuralskeletonofthePOMfiberisnotseriouslycorrodedandhasgoodalkaliresistance.
英文名 : Study on Alkali Resistance of Polyacetal Fiber for Concrete
刊期 : 2019年第12期
关键词 : 混凝土;聚甲醛纤维;耐碱性能;对应关系;微观形貌;红外测试
Key words : Concrete; Polyoxymethylene fiber; Alkali resistance; Correspondence; Microscopic morphology; Infrared test
刊期 : 2019年第12期
DOI : 10.19761/j.1000-4637.2019.12.052.04
文章编号 :
基金项目 : 国家重点研发计划项目(2018YFD1101002-05、2016YFB0303104);国家自然科学基金项目(51578479、51708483)
作者 : 王天琪1,杨鼎宜2,3,谈永泉1,范志勇1
单位 : 1.苏州混凝土水泥制品研究院检测中心有限公司,215000;2.扬州大学 建筑科学与工程学院,225127;3.扬州大学 绿色建筑材料研究所,225127

王天琪1,杨鼎宜2,3,谈永泉1,范志勇1

王天琪,杨鼎宜,谈永泉,等.混凝土用聚甲醛纤维的耐碱性能研究[J].混凝土与水泥制品,2019(12):52-55.

WANG T Q,YANG D Y,TAN Y Q,et al.Study on Alkali Resistance of Polyacetal Fiber for Concrete[J].China Concrete and Cement Products,2019(12):52-55.

摘要
参数
结论
参考文献
引用本文

摘   要:根据不同的水泥碱度设计了6种pH值的NaOH溶液对聚甲醛纤维(POM纤维)进行加速老化试验,同时用基准水泥上层清液做POM纤维的常温浸泡试验,通过测试浸泡前后纤维的直径和强度探究了POM纤维的耐碱性能,并对不同浸泡环境、不同浸泡时间下的纤维进行了微观形貌分析和红外测试,找出了不同浸泡条件下的时间对应关系。试验结果表明,POM纤维在两种浸泡环境下,随着时间的延长,直径逐渐增加,强度减小,POM纤维在pH=14的 NaOH溶液中加温浸泡6 h相当于在基准水泥上层清液中常温浸泡28 d。POM纤维的腐蚀是一个逐层腐蚀的过程,碱溶液最先腐蚀纤维表面和内部杂质,其次腐蚀结构缺陷部分,发生C-O-C和CH2基团位移,导致纤维力学性能下降,但POM纤维整体结构骨架并没有受到严重腐蚀,具有较好的耐碱性能。
Abstract: 6 kinds of NaOH solution with pH according to different cement alkalinity were designed to accelerate the aging test of POM fiber, and the benchmark cement supernatant was used to make POM fiber at room temperature immersion test. The alkali resistance of POM fiber was investigated by testing the diameter and strength of the fibers before and after soaking. Microscopic morphology analysis and infrared testing were performed on the fibers under different soaking times in different soaking environments to find out the time correspondence under different soaking conditions. The results show that the POM fiber gradually increases in diameter and strength after prolonging in two kinds of immersion environments. POM fiber is immersed in NaOH solution with pH=14 for 6 h, which is equivalent to the reference cement supernatant at room temperature for 28 d. The corrosion of POM fiber is a layer-by-layer corrosion process, the alkali solution first corrodes the fiber surface and internal impurities, and secondly corrodes the structural defects, and the C-O-C and CHgroups are displaced, resulting in a decrease in fiber mechanical properties. However, the overall structural skeleton of the POM fiber is not seriously corroded and has good alkali resistance.

关键词:
混凝土;聚甲醛纤维;耐碱性能;对应关系;微观形貌;红外测试
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加

(1)POM纤维在NaOH溶液中加温浸泡后,随着处理时间延长,纤维的直径逐渐增加,溶胀率增大,强度减小,且溶液浓度越高,纤维腐蚀越严重,但POM纤维在高温强碱溶液中仍可以长时间保持较高的力学性能,其在80 ℃下经pH=14的NaOH溶液处理336 h后,强度保留率在80%左右,力学性能仍较高,具有优异的耐碱性能。
(2)碱溶液对POM纤维的腐蚀是一个从外向内逐层腐蚀的过程,首先对纤维表面和内部杂质腐蚀,其次对纤维结构缺陷部分腐蚀,产生沟槽,之后对纤维剩余凹凸和裂痕加深部分腐蚀,出现明显的分层剥离现象,沟槽裂痕的分布与破坏程度与纤维的力学性能有关。
(5)经过碱处理的POM纤维特征峰透过率增大,峰位从低波数向高波数偏移,无新的基团产生。
 

[1] 王海波.聚乙烯醇纤维(维纶)增强砂浆性能的研究[D].北京:北京工业大学,2003.
[2] 卫志盛,袁书成,董江峰,等.玄武岩纤维再生混凝土硫酸盐侵蚀后力学性能试验研究[J].混凝土与水泥制品,2018(11):64-69.
[3] 李相明,覃俊,何勇,等.高性能聚甲醛纤维的研究进展与应用[J].合成纤维,2008,37(12):5-9.
[4] 赵志远.聚甲醛纤维的耐腐蚀性及其在水过滤用膜支撑材料上的应用研究[D].浙江浙江理工大学,2016.
[5] 文珍稀.聚甲醛纤维的制备与表征[D].上海:东华大学,2011.
[6] 刘露.聚甲醛纤维表面改性及其增强混凝土力学性能的研究[D].武汉:武汉纺织大学,2013.
[7] 国家市场监督管理总局,国家标准化管理委员会.GB/T 21120—2018水泥混凝土和砂浆用合成纤维[S].北京:中国标准出版社,2008.
[8] 中华人民共和国住房和城乡建设部.JG/T 158—2013胶粉聚苯颗粒外墙外保温系统材料[S].北京:中国标准出版社,2013.
[9] CHAE D W,CHOI K R, KIM B C,et al.Effect of Cellulose Pulp on the Mercerizing Behavior and Physical Properties of Lyocell Fibers[J].Textile Research Journal,2003,73(6):541-545.
[10] 林天扬,王春红,SHERAZ,等.碱处理提取竹黄纤维的响应曲面优化[J/OL].复合材料学报,2018:1-10.
[11] 詹怀宇.纤维素化学与物理[M].北京:科学出版社,2005.
[12] 郑明霞,李来庆,郑明月,等.碱处理对玉米秸秆纤维素结构的影响[J].环境科学与技术,2012,35(6):27-31.
[13] 马佳晨,张炉青,张学旭,等.改性水泥基材料用聚乙烯醇纤维耐碱性能研究[J].中国粉体技术,2015,21(2):61-63.
[14] 王天琪,杨鼎宜,骆静静,等.混凝土用聚乙烯醇纤维和聚丙烯纤维耐碱性能对比分析[J].混凝土与水泥制品,2019(5):58-62.
[15] 李惠林,段怡飞.聚甲醛等温热降解[J].四川大学学报:工程科学版,2005,37(4):65-68.
[16] 段怡飞.聚甲醛的热降解和稳定化研究[D].四川:四川大学,2004.

王天琪,杨鼎宜,谈永泉,.混凝土用聚甲醛纤维的耐碱性能研究[J].混凝土与水泥制品,2019(12):52-55.

WANG T Q,YANG D Y,TAN Y Q,et al.Study on Alkali Resistance of Polyacetal Fiber for Concrete[J].China Concrete and Cement Products,2019(12):52-55.

 

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州