水泥-白肥-硫酸渣基建筑砌块研究
Study on Cement-White Phosphorus Fertilizer-Sulfate Residue-Based Building Block
2016年第11期
水泥;白肥;硫酸渣;建筑砌块
Cement; White phosphorus fertilizer; Pyrite cinder; Building blocks
2016年第11期
1000-4637(2016)11-69-04
田晗旭,邓跃全,汪彬彬,李光华
西南科技大学材料科学与工程学院,绵阳 621010)

田晗旭,邓跃全,汪彬彬,李光华

浏览量:
1000
摘  要:以水泥和白肥作为复合胶凝体系,研究了水泥-白肥-硫酸渣生产建筑砌块的可行性。当白肥和水泥掺量均为20%~60%时,随白肥与水泥质量比从1∶3逐步上升到3∶1,水泥-白肥-硫酸渣基建筑砌块用水量从240mL逐步上升到342mL,干密度从1816kg/m3逐步下降到1410kg/m3,7d强度呈现先增长后下降趋势,抗压、抗折强度最高值分别为16.7MPa、3.0MPa,其机理为白肥与水泥水化产物Ca(OH)2反应生成羟基磷灰石,与C-S-H协同形成稳定的复合胶凝体系,可应用于砌块生产中,变废为宝。Abstract:Usingcementandwhitephosphorusfertilizerasthecompositioncementingsystem,thefeasibilityofproducingbuildingblocksbasedoncement,whitephosphorusfertilizerandpyritecinderwerestudied.Whencontentsofwhitephosphorusfertilizerandcementinblockswerebothfrom20%to60%,withwhitephosphorusfertilizercementratiorisingfrom1∶3to3∶1gradually,waterconsumptionofthebuildingblocksbasedoncement,whitephosphorusfertilizerandpyritecinderincreasedfrom240mLto342mL,drydensityoftheblocksdecreasedfrom1816kg/m3to1410kg/m3and7dstrengthpresentedafirstgrowingafterdecreasingtend,themaximumsofcompressivestrengthandflexuralstrengthoftheblockswere16.7MPaand3.0MParespectively.ThemechanismisthatwhitephosphorusfertilizerreactwithcementhydrationproductCa(OH)2 togenerateCa10(PO4)6(OH)2,whichcouldformstablecompositegelledsystemcombinedwithC-S-H.Whenappliedsuccessfullyinblocks,thatcouldtransformwasteintotreasure.
英文名 : Study on Cement-White Phosphorus Fertilizer-Sulfate Residue-Based Building Block
刊期 : 2016年第11期
关键词 : 水泥;白肥;硫酸渣;建筑砌块
Key words : Cement; White phosphorus fertilizer; Pyrite cinder; Building blocks
刊期 : 2016年第11期
DOI :
文章编号 : 1000-4637(2016)11-69-04
基金项目 :
作者 : 田晗旭,邓跃全,汪彬彬,李光华
单位 : 西南科技大学材料科学与工程学院,绵阳 621010)

田晗旭,邓跃全,汪彬彬,李光华

摘要
参数
结论
参考文献
引用本文

摘   要:以水泥和白肥作为复合胶凝体系,研究了水泥-白肥-硫酸渣生产建筑砌块的可行性。当白肥和水泥掺量均为20%~60%时,随白肥与水泥质量比从1∶3逐步上升到3∶1,水泥-白肥-硫酸渣基建筑砌块用水量从240mL逐步上升到342mL,干密度从1816kg/m3逐步下降到1410kg/m3,7d强度呈现先增长后下降趋势,抗压、抗折强度最高值分别为16.7MPa、3.0MPa,其机理为白肥与水泥水化产物Ca(OH)2反应生成羟基磷灰石,与C-S-H协同形成稳定的复合胶凝体系,可应用于砌块生产中,变废为宝。

Abstract:Using cement and white phosphorus fertilizer as the composition cementing system, the feasibility of producing building blocks based on cement, white phosphorus fertilizer and pyrite cinder were studied. When contents of white phosphorus fertilizer and cement in blocks were both from 20% to 60%, with white phosphorus fertilizer cement ratio rising from 1∶3 to 3∶1 gradually, water consumption of the building blocks based on cement, white phosphorus fertilizer and pyrite cinder increased from 240mL to 342mL, dry density of the blocks decreased from 1816kg/m3 to 1410kg/m3 and 7d strength presented a first growing after decreasing tend, the maximums of compressive strength and flexural strength of the blocks were 16.7MPa and 3.0MPa respectively. The mechanism is that white phosphorus fertilizer react with cement hydration product Ca(OH)2  to generate Ca10(PO4)6(OH)2, which could form stable composite gelled system combined with C-S-H. When applied successfully in blocks, that could transform waste into treasure.

关键词:
水泥;白肥;硫酸渣;建筑砌块
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加

白肥掺量20%~60%,水泥掺量20%~60%时,随着白肥与水泥质量比从1∶3上升到3∶1,水泥-白肥基砌块用水量从240mL上升到342mL,容重从2039.1kg/m3下降到1796.9kg/m3,干密度从1816.3 kg/m3逐步下降到1410.5kg/m3,强度呈现先增长后下降趋势。其中,抗压强度从13.1MPa上升到最高值16.7MPa,再下降到5.5MPa;抗折强度从2.7MPa上升到最高值3.0MPa,再下降到1.2MPa。当白肥与水泥质量比为1:2时,抗压、抗折强度分别达到其最高值16.7MPa、3.0MPa。这是由于在一定掺量内,白肥与水化产物Ca(OH)2反应生成羟基磷灰石,羟基磷灰石在砌块结构中起胶凝和增强强度的作用,可见水泥-白肥能形成稳定的复合胶凝体系,将其成功应用于建筑砌块中,可变废为宝,明显减少水泥用量,降低成本,有较好的经济效益和环境效益。

[1] 刘啸龙.白肥中磷的回收利用及酸解动力学研究[D].上海:华东理工大学,2015.
[2] 刘一,徐世林.饲料磷酸氢钙副产物的利用[J].四川化工与腐蚀控制,2002,5(2):3-5.
[3] 王延青,冯延利.硫基复合肥添加肥料级磷酸氢钙的工艺技术[J].磷肥与复肥,2002,17(5):56-58.
[4] 李春,徐世林,宿其.从白肥中回收饲料级磷酸氢钙的研究[J].四川化工,1997(1):10-12.
[5] 崔益顺,梁玉祥.饲料磷酸氢钙生产中白肥泥的处理[J].四川化工与腐蚀控制,2001(4):17-18.
[6] 胡宏,解田,杨俊,等.一种肥料级磷酸氢钙生产磷酸二氢钾的方法[P].CN103058158A,2013-4-24.
[7] 李华伟.硫铁矿烧渣资源化开发与利用研究[D].昆明:昆明理工大学,2004.
[8] 杨国清.固体废物处理工程[M].北京:科学出版社,2001.
[9] 刘全军,周兴龙,李华伟,等,硫酸渣综合利用的研究现状与进展[J].云南冶金,2003,32(2),27-29.
[10] 叶志平,何国伟.硫酸渣资源化及其以废治废技术研究[J].华南师范大学学报,2010(2):72-75.
[11] Alp I,Deveci H,Yazic E Y,et al.Potential use of pyrite cin ders as raw material in cement production: Results of industrial scale trial operations[J].Journal of hazardous materials,2009,166(1):144-149.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州