ECC拉伸性能与弯曲性能的试验研究
Experimental Study on the Tensile and Bending Properties of ECC
2019年第12期
纤维增强水泥基复合材料;拉伸性能;弯曲性能;哑铃型单轴拉伸试验;薄板四点弯曲试验
ECC; Tensile properties; Bending properties; Uniaxial tensile test; Four-point bending test
2019年第12期
10.19761/j.1000-4637.2019.12.061.05
2018年江苏省研究生科研创新计划项目(KYCX18_2558)
孔 燕1,邵永健1,杜 亮1,傅少华1,李国建2
1.苏州科技大学土木工程学院,215011;2.中亿丰建设集团股份有限公司,苏州 215131

孔 燕1,邵永健1,杜 亮1,傅少华1,李国建2

孔燕,邵永健,杜亮,等.ECC拉伸性能与弯曲性能的试验研究[J].混凝土与水泥制品,2019(12):61-65.

KONG Y,SHAO Y J,DU L,et al.Experimental Study on the Tensile and Bending Properties of ECC[J].China Concrete and Cement Products,2019(12):61-65.

浏览量:
1000
摘 要:设计了10组ECC试件,并进行了哑铃型单轴拉伸和薄板四点弯曲试验,研究了粉煤灰掺量、水胶比和PVA纤维体积率对ECC拉伸性能与弯曲性能的影响。结果表明,增加粉煤灰掺量,ECC试件抗拉强度和抗弯强度均先增大后减小,当粉煤灰掺量为1.2时,ECC的受拉应变-硬化特性最明显,极限拉应变可稳定达到4.7%以上;增大水胶比,ECC的抗拉强度和抗弯强度降低,但极限拉应变增大且受拉应变-硬化特性明显;增大PVA体积率可明显提高ECC的抗拉强度、极限拉应变和抗弯强度。 Abstract: The uniaxial tension and four-point bending tests of 10 groups of ECC specimens were carried out to study the effects of fly ash content, water-binder ratio and PVA fiber volume ratio on tensile properties and bending properties of ECC. The results show that the tensile strength and bending strength of ECC specimens increase first and then decrease with the increase of fly ash content, and when fly ash content is 1.2, the tensile strain-hardening characteristics of ECC are obvious, and the most obvious ultimate tensile strain could be more than 4.7%. With the increase of water-binder ratio, the tensile strength and bending strength of ECC decrease, but the ultimate tensile strain increases and the tensile strain-hardening characteristics are obvious. The tensile strength, ultimate tensile strain and bending strength of ECC could be improved obviously with the increase of PVA volume ratio.
英文名 : Experimental Study on the Tensile and Bending Properties of ECC
刊期 : 2019年第12期
关键词 : 纤维增强水泥基复合材料;拉伸性能;弯曲性能;哑铃型单轴拉伸试验;薄板四点弯曲试验
Key words : ECC; Tensile properties; Bending properties; Uniaxial tensile test; Four-point bending test
刊期 : 2019年第12期
DOI : 10.19761/j.1000-4637.2019.12.061.05
文章编号 :
基金项目 : 2018年江苏省研究生科研创新计划项目(KYCX18_2558)
作者 : 孔 燕1,邵永健1,杜 亮1,傅少华1,李国建2
单位 : 1.苏州科技大学土木工程学院,215011;2.中亿丰建设集团股份有限公司,苏州 215131

孔 燕1,邵永健1,杜 亮1,傅少华1,李国建2

孔燕,邵永健,杜亮,等.ECC拉伸性能与弯曲性能的试验研究[J].混凝土与水泥制品,2019(12):61-65.

KONG Y,SHAO Y J,DU L,et al.Experimental Study on the Tensile and Bending Properties of ECC[J].China Concrete and Cement Products,2019(12):61-65.

摘要
参数
结论
参考文献
引用本文

摘   要:设计了10组ECC试件,并进行了哑铃型单轴拉伸和薄板四点弯曲试验,研究了粉煤灰掺量、水胶比和PVA纤维体积率对ECC拉伸性能与弯曲性能的影响。结果表明,增加粉煤灰掺量,ECC试件抗拉强度和抗弯强度均先增大后减小,当粉煤灰掺量为1.2时,ECC的受拉应变-硬化特性最明显,极限拉应变可稳定达到4.7%以上;增大水胶比,ECC的抗拉强度和抗弯强度降低,但极限拉应变增大且受拉应变-硬化特性明显;增大PVA体积率可明显提高ECC的抗拉强度、极限拉应变和抗弯强度。
Abstract: The uniaxial tension and four-point bending tests of 10 groups of ECC specimens were carried out to study the effects of fly ash content, water-binder ratio and PVA fiber volume ratio on tensile properties and bending properties of ECC. The results show that the tensile strength and bending strength of ECC specimens increase first and then decrease with the increase of fly ash content, and when fly ash content is 1.2, the tensile strain-hardening characteristics of ECC are obvious, and the most obvious ultimate tensile strain could be more than 4.7%. With the increase of water-binder ratio, the tensile strength and bending strength of ECC decrease, but the ultimate tensile strain increases and the tensile strain-hardening characteristics are obvious. The tensile strength, ultimate tensile strain and bending strength of ECC could be improved obviously with the increase of PVA volume ratio.

关键词:
纤维增强水泥基复合材料;拉伸性能;弯曲性能;哑铃型单轴拉伸试验;薄板四点弯曲试验
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加

(1)掺加适量的粉煤灰,可以有效提高抗拉强度和抗弯强度,粉煤灰掺量为1.2时,ECC的受拉应变-硬化特性最明显,极限拉应变可稳定达到4.7%以上,过量粉煤灰的掺入不利于呈现多裂缝开裂特征和应变-硬化特性。
(2)较低的水胶比不利于PVA纤维的乱向分布和应变-硬化特性的呈现,较高的水胶比则会降低ECC抗拉与抗弯强度、基体间黏结性和基体的弹性模量,当水胶比为0.30~0.33时,试件的受拉应变-硬化特性最为明显。
(3)增加PVA体积率,可明显提高ECC的抗拉强度、极限拉应变及抗弯强度,改善应变-硬化特性。PVA纤维体积率为2%时,ECC极限拉应变是基体的47.8倍,抗弯强度是基体的2.1倍。
(4)通过理论推导,给出了计算有效拉应力的公式:?滓te=■(h-c)2,并建立最大弯曲应力与有效拉应力之间的关系,其表达式为:?滓w=2Eh?覫(1-■)3+3?滓te(■)2。

[1] LI V C,WANG S,WU C.Tensile strain-hardening behavior of polyvinyl alcohol engineered cementitious composites(PVA-ECC)[J].ACI Materials Joumal,2001,98(6):483-492.
[2] 陈鹏,王春辉,俞景云,等.采用ECC提高RC梁抗弯性能的试验研究[J].混凝土与水泥制品,2018(4):65-68.
[3] AVESTON J,COOPER G A,KELLY A.The properties of fiber composites[C].IPC Science and Technology Press Ltd,London,1971,15-26.
[4] MAALEJ M,LI V C.Flexural tensile strength ratio in engineered cementitious composites[J].Journal of Materials in Civil Engineering,1994,6(4):513-528.
[5] 陈前均,李晓琴,刘国寿,等.高韧性水泥基复合材料ECC的材性及其有限元应用研究[J].混凝土与水泥制品,2017(12):50-53.
[6] 陆洲导,林晨旭,余江滔,等.可用于无钢筋建造的超强超韧水泥基复合材料[J].同济大学学报:自然科学版,2017,45(6):94-98.
[7] 刘曙光,常智慧,张栋翔,等.PVA-ECC材料在桥梁伸缩缝工程中的应用[J].混凝土与水泥制品,2016(2):85-87.
[8] 中华人民共和国建设部,国家质量监督检验检疫总局.GB/T 50081—2002 普通混凝土力学性能试验方法标准[S].北京:中国建筑工业出版社,2012.
[9] 徐世烺,李贺东.超高韧性水泥基复合材料直接拉伸试验研究[J].土木工程学报,2009,42(9):32-41.
[10] 张黎飞,郑愚,于国友,等.高韧性纤维水泥基薄板弯曲韧性[J].混凝土,2018,339(1):96-101.
 

孔燕,邵永健,杜亮,.ECC拉伸性能与弯曲性能的试验研究[J].混凝土与水泥制品,2019(12):61-65.

KONG Y,SHAO Y J,DU L,et al.Experimental Study on the Tensile and Bending Properties of ECC[J].China Concrete and Cement Products,2019(12):61-65.

 

 

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州