气凝胶保温砂浆导热影响因素及建筑能耗研究
Thermal Conductivity Influence Factors and Building Energy Consumption Analysis of Aerogel Thermal Insulation Mortar
2019年第12期
气凝胶;保温砂浆;导热系数;耗热量;能耗分析
Aerogel; Insulation mortar; Thermal conductivity; Heat loss; Building energy analysis
2019年第12期
10.19761/j.1000-4637.2019.12.070.04
河南省教育厅研究项目(2019-ZZJH-193)。
王修贵1,程 功1,张文静2
1.郑州工商学院工学院,451400;2.郑州煤矿机械制造技工学校,450000

王修贵1,程 功1,张文静2

王修贵,程功,张文静.气凝胶保温砂浆导热影响因素及建筑能耗研究[J].混凝土与水泥制品,2019(12):70-73.

WANG X G,CHENG G,ZHANG W J.Thermal Conductivity Influence Factors and Building Energy Consumption Analysis of Aerogel Thermal Insulation Mortar[J].China Concrete and Cement Products,2019(12):70-73.

浏览量:
1000
摘 要:基于国内外研究现状,根据最佳配合比制备气凝胶保温砂浆,研究相关因素对其导热系数的影响。以郑州市某座高层住宅楼为例,对比分析了气凝胶砂浆保温体系与玻化微珠砂浆保温体系的建筑能耗。研究发现,气凝胶保温砂浆导热系数随着温度的提高而增大,并且与其干表观密度呈现线性增加的趋势;与玻化微珠砂浆保温体系建筑物相比,气凝胶砂浆保温体系建筑物的单位面积耗煤量与单位面积采暖费均降低18%。 Abstract: The aerogel thermal insulation mortar was prepared according to the best mix ratio, and the influence of related factors on its thermal conductivity was studied. Taking a high-rise residential building in Zhengzhou as an example, the aerogel insulation mortar insulation system and glass beads insulation mortar were analyzed. The resuts show that the thermal conductivity of the aerogel insulation mortar increases with the increase of temperature, and its dry apparent density shows a linear increase. Compared with the insulation system of glass beads, the aerogel insulation mortar insulation system has a 18% reduction in coal consumption per unit area and heating cost per unit area, which provides a reference for the study of aerogel thermal insulation mortar.
英文名 : Thermal Conductivity Influence Factors and Building Energy Consumption Analysis of Aerogel Thermal Insulation Mortar
刊期 : 2019年第12期
关键词 : 气凝胶;保温砂浆;导热系数;耗热量;能耗分析
Key words : Aerogel; Insulation mortar; Thermal conductivity; Heat loss; Building energy analysis
刊期 : 2019年第12期
DOI : 10.19761/j.1000-4637.2019.12.070.04
文章编号 :
基金项目 : 河南省教育厅研究项目(2019-ZZJH-193)。
作者 : 王修贵1,程 功1,张文静2
单位 : 1.郑州工商学院工学院,451400;2.郑州煤矿机械制造技工学校,450000

王修贵1,程 功1,张文静2

王修贵,程功,张文静.气凝胶保温砂浆导热影响因素及建筑能耗研究[J].混凝土与水泥制品,2019(12):70-73.

WANG X G,CHENG G,ZHANG W J.Thermal Conductivity Influence Factors and Building Energy Consumption Analysis of Aerogel Thermal Insulation Mortar[J].China Concrete and Cement Products,2019(12):70-73.

摘要
参数
结论
参考文献
引用本文

摘   要:基于国内外研究现状,根据最佳配合比制备气凝胶保温砂浆,研究相关因素对其导热系数的影响。以郑州市某座高层住宅楼为例,对比分析了气凝胶砂浆保温体系与玻化微珠砂浆保温体系的建筑能耗。研究发现,气凝胶保温砂浆导热系数随着温度的提高而增大,并且与其干表观密度呈现线性增加的趋势;与玻化微珠砂浆保温体系建筑物相比,气凝胶砂浆保温体系建筑物的单位面积耗煤量与单位面积采暖费均降低18%。
Abstract: The aerogel thermal insulation mortar was prepared according to the best mix ratio, and the influence of related factors on its thermal conductivity was studied. Taking a high-rise residential building in Zhengzhou as an example, the aerogel insulation mortar insulation system and glass beads insulation mortar were analyzed. The resuts show that the thermal conductivity of the aerogel insulation mortar increases with the increase of temperature, and its dry apparent density shows a linear increase. Compared with the insulation system of glass beads, the aerogel insulation mortar insulation system has a 18% reduction in coal consumption per unit area and heating cost per unit area, which provides a reference for the study of aerogel thermal insulation mortar.

关键词:
气凝胶;保温砂浆;导热系数;耗热量;能耗分析
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加

(1)气凝胶保温砂浆的导热系数随着其干表观密度增大呈现不断增大的趋势,线性回归函数为y=1.140 27×10-4x+0.025 44,相关指数R2=0.988 09,研究范围内可以通过拟合曲线对导热系数进行计算。
(2)气凝胶保温砂浆导热系数随着温度的提高而增大,主要取决于热辐射与气相导热的增强;并且保温砂浆中加入气凝胶有利于改善砂浆内部结构,增强保温砂浆的保温性能。
(3)与玻化微珠保温砂浆保温体系对比,气凝胶保温砂浆保温体系建筑物的单位面积耗煤量与单位面积采暖费均减低18%。

[1] 王飞,刘朝辉,邓智平,等.不同体积掺量的SiO2气凝胶对砂浆性能的影响[J].功能材料,2016,47(4):64-69.
[2] 华治国,朱悦,王吉霖.无机保温砂浆内外组合保温系统结合外墙隔热涂料的热工性能研究[J].混凝土与水泥制品,2017(9):60-62.
[3] 张玉会,刘燕妮 杨建明,等.SiO2气凝胶复合保温材料的热湿性能研究[J].新型建筑材料,2017,44(3):67-71.
[4] 吴炎平,朱群敏,李敏涛.装配式轻钢复合保温外墙板的制备及其在村镇住宅中的节能效果评价[J].混凝土与水泥制品, 2018(1):63-67.
[5] 王俊,王有为,林海燕,等.我国绿色低碳建筑技术应用研究进展[J].建筑科学,2013,29(10):2-9+33.
[6] KIM S,SEO J,CHA J,et al.Chemical retreating for gel-typed aerogel and insulation performance of cement containing aerogel [J].Construction and Building Materials,2013,40(3):501-505.
[7] GlóriaGomes M,FLORES C I,SILV F.Thermal conductivity measurement of thermal insulating mortars with EPS and silica aerogel by steady-state and transient methods[J].Construction and Building Materials,2018,4172:696-705.
[8] 刘婧,王贯明,成铠,等.利用可溶性气凝胶膏对玻化微珠保温砂浆配比的优化设计[J].市政技术,2017,35(6):176-178.
[9] 吴祥松.对混凝土骨料饱和面干表观密度检测方法及应用的探讨[J].水电与新能源,2015(10):25-26.
[10] 张伟平,童菲,邢益善,等.混凝土导热系数的试验研究与预测模型[J].建筑材料学报,2015,18(2):183-189.

王修贵,程功,张文静.气凝胶保温砂浆导热影响因素及建筑能耗研究[J].混凝土与水泥制品,2019(12):70-73.

WANG X G,CHENG G,ZHANG W J.Thermal Conductivity Influence Factors and Building Energy Consumption Analysis of Aerogel Thermal Insulation Mortar[J].China Concrete and Cement Products,2019(12):70-73.

 

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州