环氧树脂与缓蚀剂对钢筋混凝土构件防锈的组合效应研究

摘要：单独使用环氧树脂或缓蚀剂对钢筋混凝土结构中钢筋的防护效果有限。为取得更好的防护效果，本文尝试将缓蚀剂和环氧树脂组合使用，采用半电池电位法测定缓蚀剂和环氧树脂不同涂刷顺序对混凝土构件中钢筋的防护效果。试验结果表明，先涂一层缓蚀剂再覆盖一层环氧树脂对混凝土构件中的钢筋防护效果最佳，能有效降低钢筋的腐蚀电位，使构件中钢筋的腐蚀概率小于5%，因此，缓蚀剂与环氧树脂的组合使用能有效保护钢筋不被腐蚀。

Abstract: The protection cannot show the intact effectiveness when epoxy resin or corrosion inhibitors is used alone on the reinforced steel concrete structure. In this paper, making a combination of epoxy resin and corrosion inhibitors is tried for getting a better protective effect, and half-cell potential method is used to determine the protective effect of epoxy and corrosion for reinforced concrete structure when they are applied in different order. The results show that brushing a layer of corrosion inhibitor then covering a layer of epoxy corrosion inhibitor has a better protection on reinforced steel concrete structure, which can effectively reduce the potential corrosion of the steel and makes the probability of corrosion of steel members less than 5%. Therefore, using the combination of corrosion inhibitor and epoxy resin can effectively protect steel from corrosion.

关键词:

钢筋阻绣；钢筋混凝土；腐蚀；缓蚀剂；环氧树脂

扫二维码用手机看

未找到相应参数组，请于后台属性模板中添加

本研究为在人工海洋环境下，环氧树脂与缓蚀剂单独及不同涂刷顺序的组合使用对钢筋进行保护的试验，主要通过改变两者涂覆的先后顺序来处理条件相同的钢筋混凝土构件，用半电池电位法测定钢筋的腐蚀电位。根据试验结果可知，先涂一层缓蚀剂再覆加一层环氧树脂的试件中钢筋腐蚀电位较其余几组负向电压要小30～50mV。其原理是：外层的环氧树脂属于物理防护，内层的缓蚀剂属于化学防护，当物理防护出现漏洞时，内层的化学防护作为第二道屏障进行了补救。因此，在钢筋表面先进行缓蚀剂化学保护，再涂抹环氧树脂物理保护层，这样组合使用能对试件产生更好的保护效果。

本试验在具体操作过程中，因考虑到环氧树脂和缓蚀剂两种材料涂覆顺序的变化，所以并未对环氧树脂涂层的处理采用国际上普遍的静电喷涂法，因而本试验得出的这种环氧树脂与缓蚀剂的组合效益只限于试验环境下，在实际工程中的应用还有待进一步考证。

[1] 李建华.钢筋缓蚀剂和钢筋混凝土结构电化学除氯的研究[D]. 厦门: 厦门大学, 2007.

[2] 张誉, 蒋利学.混凝土碳化和钢筋锈蚀研究动态[J].福州大学学报: 自然科学版，1996, 24(1): 18-27.

[3] Kumar V. Protection of steel reinforcement for concrete-A review[J]. Corrosion Reviews ,1998,16(4):317-358.

[4] 洪定海.混凝土中钢筋的腐蚀与保护[M].北京：中国铁道出版社，1998.

[5] Sideris K K ,Savva A E. Durability of mixtures containing calcium nitrite based corrosion inhibitor[J].Cement & Concrete Composites,2005,27(2):277-287.

[6] Wombacher F, Maeder U, Marazzani B. Aminoalcohol based mixed corrosion inhibitors[J]. Cement & Concrete Composites,2004,26(3): 209-216.

[7] Douche-Portanguen A, Prince W, Lutz T, Arliguie G. Detection or quantitative analysis Of a corrosion inhibitor, the sodium monofluorophosphate, in concrete [J].Cement & Concrete Composites,2005,27(6):679-687.

[8] 杨万里，吴小蓉. 环氧树脂涂层钢筋的技术原理、发展过程及国内外应用情况[J]. 水运工程，1999,307（8）：1-7.

[9] 杨建森. 氯盐对混凝土中钢筋的腐蚀机理与腐蚀技术[J].混凝土,2001(141）: 52-56.

[10] Neal S Berke. Protection Against Chloride Induced Comosion [J].Concrete International, 1988(12): 25-28.

[11] 刘志.无溶剂超厚膜型环氧重防腐涂层的研制及耐久性能研究[D]. 青岛: 青岛理工大学, 2009.

[12] 施惠生, 郭晓潞, 张贺.保护层厚度对混凝土中钢筋锈蚀的影响[J]. 水泥工程，2009(2):79-83.

[13] ASTM C 876-91.Standard Test Method for Half-Cell Potentials of Uncoated Reinforcing Steel in Concrete[S].

[14] 陈迅捷，欧阳幼玲，钱文勋，等. 不同环境中杂散电流对钢筋混凝土腐蚀影响[J]. 水利水运工程学报， 2014(2): 33.