纤维EPS吸能防护混凝土材料研究
Study on Fiber EPS Concrete with Energy- absorption Shielding Protection Materials
2015年第2期
EPS混凝土;混杂纤维;力学性能;抗冲击性能
EPS concrete; Hybrid fiber; Mechanical properties; Shock resistance
2015年第2期
1000-4637(2015)02-50-04
国家自然科学基金项目(51202172)
陈友治,陈雍雍,欧阳康,孙 涛,李新平,沈春华摘 要:试验制备了钢纤维、聚丙烯纤维混杂的纤维EPS混凝土,考察了EPS混凝土及纤维EPS混凝土力学性能,以改变荷载速率的方式研究和表征纤维EPS混凝土的抗冲击性能。研究结果表明,EPS混凝土有较好的力
武汉理工大学材料科学与工程学院,430070

陈友治,陈雍雍,欧阳康,孙 涛,李新平,沈春华

浏览量:
1000
摘 要:试验制备了钢纤维、聚丙烯纤维混杂的纤维EPS混凝土,考察了EPS混凝土及纤维EPS混凝土力学性能,以改变荷载速率的方式研究和表征纤维EPS混凝土的抗冲击性能。研究结果表明,EPS混凝土有较好的力学性能,在水胶比为0.26,EPS体积率为40%时,28d龄期抗压强度及抗折强度分别为22.03MPa,4.50MPa;低掺量的混杂纤维对纤维EPS混凝土抗压强度提高较小,但对韧性提高较大;相比普通混凝土,纤维EPS混凝土随着荷载速率增大极限抗压强度明显提高。 Abstract: In this experiment with steel fiber and polypropylene fiber, fiber EPS concrete was made, the mechanical properties of which were analyzed as well as EPS concrete, and anti-impacting properties of fiber EPS concrete were studied and characterized through varying the load rate. The research results show that the EPS concrete has good mechanical properties. When the water/cement ratio is 0.26 and the EPS volume rate is 40%, compressive strength and flexural strength of concrete after 28 days are respectively 22.03MPa and 4.50MPa. Low dosage of hybrid fibers can slightly improve compressive strength of fiber EPS concrete, but largely enhance the toughness of concrete. Compared with normal concrete, the ultimate compressive strength of fiber EPS concrete will be improved significantly with the load rate increased.
英文名 : Study on Fiber EPS Concrete with Energy- absorption Shielding Protection Materials
刊期 : 2015年第2期
关键词 : EPS混凝土;混杂纤维;力学性能;抗冲击性能
Key words : EPS concrete; Hybrid fiber; Mechanical properties; Shock resistance
刊期 : 2015年第2期
DOI :
文章编号 : 1000-4637(2015)02-50-04
基金项目 : 国家自然科学基金项目(51202172)
作者 : 陈友治,陈雍雍,欧阳康,孙 涛,李新平,沈春华摘 要:试验制备了钢纤维、聚丙烯纤维混杂的纤维EPS混凝土,考察了EPS混凝土及纤维EPS混凝土力学性能,以改变荷载速率的方式研究和表征纤维EPS混凝土的抗冲击性能。研究结果表明,EPS混凝土有较好的力
单位 : 武汉理工大学材料科学与工程学院,430070

陈友治,陈雍雍,欧阳康,孙 涛,李新平,沈春华

摘要
参数
结论
参考文献
引用本文

摘   要:试验制备了钢纤维、聚丙烯纤维混杂的纤维EPS混凝土,考察了EPS混凝土及纤维EPS混凝土力学性能,以改变荷载速率的方式研究和表征纤维EPS混凝土的抗冲击性能。研究结果表明,EPS混凝土有较好的力学性能,在水胶比为0.26,EPS体积率为40%时,28d龄期抗压强度及抗折强度分别为22.03MPa,4.50MPa;低掺量的混杂纤维对纤维EPS混凝土抗压强度提高较小,但对韧性提高较大;相比普通混凝土,纤维EPS混凝土随着荷载速率增大极限抗压强度明显提高。

Abstract: In this experiment with steel fiber and polypropylene fiber, fiber EPS concrete was made, the mechanical properties of which were analyzed as well as EPS concrete, and anti-impacting properties of fiber EPS concrete were studied and characterized through varying the load rate. The research results show that the EPS concrete has good mechanical properties. When the water/cement ratio is 0.26 and the EPS volume rate is 40%, compressive strength and flexural strength of concrete after 28 days are respectively 22.03MPa and 4.50MPa. Low dosage of hybrid fibers can slightly improve compressive strength of fiber EPS concrete, but largely enhance the toughness of concrete. Compared with normal concrete, the ultimate compressive strength of fiber EPS concrete will be improved significantly with the load rate increased.


关键词:
EPS混凝土;混杂纤维;力学性能;抗冲击性能
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加
(1)在水胶比为0.26,EPS体积率分别为30%和40%时,EPS混凝土标准养护28d后,其压折比分别为5.00和4.90,与普通混凝土6.07的压折比相比有了很大程度的提高。因此,在EPS体积率为30%~40%时,EPS混凝土具有良好的抗压性能及较好的韧性。
(2)纤维对EPS混凝土有良好的增韧效果。低掺量混杂纤维的掺加对EPS混凝土韧性影响较大,而对其强度的增长效果不明显。
(3)结合EPS工作性及力学性能的增强效果,钢纤维体积掺量为2%,聚丙烯纤维掺量为0.1%时,纤维EPS混凝土拥有最优性能。
(4)EPS颗粒对于冲击能量有很强的吸收作用。荷载速度越快,EPS在瞬时所承担吸收的冲击能越大,具有较好的能量耗散作用。纤维EPS混凝土具有较好的抗冲击性能,具有一定的吸能防护作用,此项性能对人防工程建设具有重要的理论意义和实用价值。
[1] PERRY S H, BISCHOFF P H, YAMURA K. Mix details and Material behaviour of polystyrene aggregate concrete[J]. Magazine of Concrete Research,1991,43(1):71-76.
[2] RAVINDRARAJAH R S,TUCK A J,Properties of hardened concrete containing t reated expanded polystyrene beads[J].Cement and Concrete Composites,1994,16(2):273-277.
[3] 赵晓艳,田稳苓,赵继东,等.EPS轻集料混凝土制备关键技术及其研究进展[J].混凝土,2009(8):59-62.
[4] Bin Mu, Zongjin Li, Jnn peng.Short fiber-reinforced cementitious extruded plate with high percentage of slag and different fibers[J].Cement and Concrete Research,2000(30):1277-1282.
[5] 邓宗才,李建辉,孙俊宏,等.纤维混凝土的抗弯冲击性能[J].公路交通科技,2005,22(6):24-26.
[6] 焦楚杰,孙伟,高培正,等.钢纤维混凝土抗冲击试验研究[J].中山大学学报,2005,44(6):41-44.
[7] D.Boulet,R.Pleau,P.Rougeaud,et al.Flexural behavior of ultra high performance mortars reinforced with different types of steel fibres[J].Fibre-Reinforced Concretes(FRC),Proceedings of the Fifth International RILEM Symposium Lyon.France,2000:759-768.
[8] 梁磊,赵文,李艺,等.增强纤维的加入对混凝土抗冲击性能的影响[J].混凝土与水泥制品,2007(1):44-46.
[9] 袁海庆,陈景涛,朱继东.层布式钢纤维-聚丙烯腈纤维混凝土力学性能实验研究[J].武汉理工大学学报,2003(4):31-34.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州