石灰石资源全利用混凝土在桥梁工程中的应用研究
Application Research on Concrete with Total Utilization Limestone Resource for Bridge Engineering
2015年第3期
石灰石资源;混凝土;桥梁;徐变;强度
Limestone resource; Concrete; Bridge; Creep; Strength
2015年第3期
1000-4637(2015)03-05-04
湖南省科技计划发展项目(2006sk4017)
刘 春1,何智海2
1.宁德师范学院艺术系,352000;2.绍兴文理学院土木工程学院,312000

刘 春1,何智海2

浏览量:
1000
摘 要:针对混凝土桥梁工程的低徐变要求,开展了采用石灰石资源一条龙生产碎石、机制砂和石灰石粉配制的石灰石资源全利用混凝土的试验和应用研究。结果表明,该混凝土早期强度高于桥梁主梁常用的商品混凝土,但其发展速度较慢,后期强度反而略低于常用商品混凝土;采用复配减缩型高效减水剂有效解决了石灰石资源全利用混凝土徐变较大的技术难题,并在实际桥梁工程中得到了成功应用。 Abstract: According to the requirement of low creep of bridge engineering, the experimental and application research of concrete with total utilization of limestone resources which was prepared by the aggregate, machine-made sand and limestone powder from the limestone resources were studied. The results indicate that the early strength of concrete with total utilization of limestone resources is higher than that of the ready-mixed concrete commonly used for bridge girders, but the strength development speed is relatively slow, so the later strength of the concrete is slightly lower than that of the ready-mixed concrete; shrinkage-reducing superplasticizer can solve the technical problem of concrete with total utilization of limestone resources with higher creep, which has been successfully applied for the practical bridge engineering.
英文名 : Application Research on Concrete with Total Utilization Limestone Resource for Bridge Engineering
刊期 : 2015年第3期
关键词 : 石灰石资源;混凝土;桥梁;徐变;强度
Key words : Limestone resource; Concrete; Bridge; Creep; Strength
刊期 : 2015年第3期
DOI :
文章编号 : 1000-4637(2015)03-05-04
基金项目 : 湖南省科技计划发展项目(2006sk4017)
作者 : 刘 春1,何智海2
单位 : 1.宁德师范学院艺术系,352000;2.绍兴文理学院土木工程学院,312000

刘 春1,何智海2

摘要
参数
结论
参考文献
引用本文

摘   要:针对混凝土桥梁工程的低徐变要求,开展了采用石灰石资源一条龙生产碎石、机制砂和石灰石粉配制的石灰石资源全利用混凝土的试验和应用研究。结果表明,该混凝土早期强度高于桥梁主梁常用的商品混凝土,但其发展速度较慢,后期强度反而略低于常用商品混凝土;采用复配减缩型高效减水剂有效解决了石灰石资源全利用混凝土徐变较大的技术难题,并在实际桥梁工程中得到了成功应用。

Abstract: According to the requirement of low creep of bridge engineering, the experimental and application research of concrete with total utilization of limestone resources which was prepared by the aggregate, machine-made sand and limestone powder from the limestone resources were studied. The results indicate that the early strength of concrete with total utilization of limestone resources is higher than that of the ready-mixed concrete commonly used for bridge girders, but the strength development speed is relatively slow, so the later strength of the concrete is slightly lower than that of the ready-mixed concrete; shrinkage-reducing superplasticizer can solve the technical problem of concrete with total utilization of limestone resources with higher creep, which has been successfully applied for the practical bridge engineering.


关键词:
石灰石资源;混凝土;桥梁;徐变;强度
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加
(1)采用石灰石资源一条龙生产的碎石、机制砂和石灰石粉配制出石灰石资源全利用混凝土,其早期强度高于桥梁主梁常用的商品混凝土,但其发展速度较慢,后期强度反而略低于常用商品混凝土。
(2)采用复配减缩型高效减水剂配制石灰石资源全利用混凝土有效解决了其徐变较大的技术难题,并在实际混凝土桥梁主梁工程中得到了成功应用。该混凝土质量稳定,综合效益显著,值得大力推广使用。
[1] 陈剑雄, 李鸿芳, 陈寒斌, 等. 掺超细石灰石粉和钛矿渣粉高强混凝土研究[J]. 建筑材料学报, 2005, 8(6): 672-676.
[2] 刘数华, 阎培渝. 石灰石粉在复合胶凝材料中的水化性能[J]. 硅酸盐学报, 2008, 36(10): 1401-1405.
[3] 刘江红, 刘运华, 何智海. 石灰石资源在混凝土中的应用研究[J]. 混凝土, 2011(1): 103-105.
[4] 中华人民共和国住房和城乡建设部. JGJ/T 318-2014 石灰石粉在混凝土中应用技术规程[S]. 北京: 中国建筑工业出版社,2014.
[5] 中华人民共和国住房和城乡建设部. GB/T 50082-2009 普通混凝土长期性能和耐久性能试验方法标准[S]. 北京: 中国建筑工业出版社,2010.
[6] Bentz D P, Geikerb M R, Hansenb K K. Shrinkage-reducing admixtures and early-age desiccation in cement pastes and mortars[J]. Cement and Concrete Research, 2001, 31:1075-1085.
[7] 卞荣兵,马存前,刘姝,等. 新型混凝土减缩剂评价研究[J]. 建筑材料学报, 2005,8(5): 436-439.
[8] 何智海, 钱春香, 钱桂枫, 等. 等强度下混凝土组分对徐变性能的影响[J]. 功能材料, 2011, 42(5): 925-927.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州