冻融循环下锂渣粉对混凝土渗透性的影响

Effects of Lithium Slag Powder on Permeability of Concrete under Freeze-thaw Cycles

２０15年第3期

混凝土；锂渣粉；冻融循环；电通量

Concrete; Lithium slag powders; Freeze-thaw cycles; Electric flux

２０15年第3期

1000-4637（2015）03-83-04

国家自然科学基金项目（51268055）

张广泰，董海蛟，温勇

新疆大学建筑工程学院，乌鲁木齐 830047

张广泰，董海蛟，温勇

浏览量:

1000

摘要：采用电通量法测定了不同锂渣掺量的混凝土在不同冻融循环次数下的电通量，并研究了电通量与各影响因素之间的函数关系。试验结果表明，随冻融循环次数的增加，混凝土电通量近似呈线性增加。当冻融循环次数为75次时，不同锂渣掺量下的混凝土仍具有较高的抗氯离子渗透性。锂渣粉的加入能明显降低混凝土的氯离子渗透性，随锂渣掺量的增加，混凝土电通量近似呈负指数函数关系下降。同时发现，电通量与初始电流间、电通量与氯离子渗透深度间、初始电流与氯离子渗透深度间均具有较好的线性相关性。 Abstract: Electric flux of concrete with different lithium slag powder content subjected to different freeze-thaw cycle number was determined by the test method of coulomb electric flux, and the function relations between electric flux and different factors were studied. The test results show that electric flux of concrete increases with increasing freeze-thaw cycle number by the linear function. When the freeze-thaw cycle number is 75, the concrete with different lithium slag powder content still has a high resistance to chloride penetration. Addition of lithium slag powder into concrete can significantly reduce its chloride penetration and electric flux decreases with increasing lithium slag powder content by the negative exponential function. In addition, the relationships between electric flux and initial current, electric flux and chloride ion penetration depth, initial current and chloride ion penetration depth all have a good linear correlation.

英文名 : Effects of Lithium Slag Powder on Permeability of Concrete under Freeze-thaw Cycles

刊期 : ２０15年第3期

关键词 : 混凝土；锂渣粉；冻融循环；电通量

Key words : Concrete; Lithium slag powders; Freeze-thaw cycles; Electric flux

刊期 : ２０15年第3期

DOI :

文章编号 : 1000-4637（2015）03-83-04

基金项目 : 国家自然科学基金项目（51268055）

作者 : 张广泰，董海蛟，温勇

单位 : 新疆大学建筑工程学院，乌鲁木齐 830047

张广泰，董海蛟，温勇





摘要

参数

结论

参考文献

引用本文

摘要：采用电通量法测定了不同锂渣掺量的混凝土在不同冻融循环次数下的电通量，并研究了电通量与各影响因素之间的函数关系。试验结果表明，随冻融循环次数的增加，混凝土电通量近似呈线性增加。当冻融循环次数为75次时，不同锂渣掺量下的混凝土仍具有较高的抗氯离子渗透性。锂渣粉的加入能明显降低混凝土的氯离子渗透性，随锂渣掺量的增加，混凝土电通量近似呈负指数函数关系下降。同时发现，电通量与初始电流间、电通量与氯离子渗透深度间、初始电流与氯离子渗透深度间均具有较好的线性相关性。Abstract: Electric flux of concrete with different lithium slag powder content subjected to different freeze-thaw cycle number was determined by the test method of coulomb electric flux, and the function relations between electric flux and different factors were studied. The test results show that electric flux of concrete increases with increasing freeze-thaw cycle number by the linear function. When the freeze-thaw cycle number is 75, the concrete with different lithium slag powder content still has a high resistance to chloride penetration. Addition of lithium slag powder into concrete can significantly reduce its chloride penetration and electric flux decreases with increasing lithium slag powder content by the negative exponential function. In addition, the relationships between electric flux and initial current, electric flux and chloride ion penetration depth, initial current and chloride ion penetration depth all have a good linear correlation.

关键词:

混凝土；锂渣粉；冻融循环；电通量

扫二维码用手机看

[1] 胡汝骥,樊自立,王亚俊,等.近50年新疆气候变化对环境影响评估[J].干旱区地理,2001,24(2):97-103.

[2] 温勇,刘国君,秦志勇,等.锂渣粉对混凝土氯离子渗透性的影响[J].混凝土,2011(8):76-78.

[3] 李伟文,冷发光,邢峰.不同强度等级混凝土氯离子渗透性研究[J].混凝土,2003(5):29-30,62.

[4] EHTA P K, MONTEIRO P J M. Concrete Microstructure, Properties, and Materials[M]. 3 rd ed. New York: The McGraw-Hill Companies, Inc, 2006.

[5] 吴相豪,周金岩,李怀垣.环境因素影响粉煤灰混凝土固化氯离子能力的试验研究[J].粉煤灰,2011(5):280-285.

[6] 叶其业,杜乃红,米胜东.冻融循环后混凝土抗氯离子渗透性能试验研究[J].中国港湾建设,2012(5):33-35.

[7] 王军强.混凝土中冻融循环和氯离子侵蚀的耦合效应试验研究[J].混凝土,2008(11):29-31.

[8] 洪雷,唐晓东.冻融循环对高性能混凝土氯离子渗透性的影响[J].武汉理工大学学报,2010,32(18):41-44.

[9] 洪雷,彭超.单向荷载及冻融循环对氯离子渗透性的影响[J].建筑材料学报,2012,15(2):255-259.

[10] 何松晟,高玮,汪磊.矿物掺合料对混凝土抗氯离子渗透性影响研究[J].武汉工业学院学报,2011(4):80-83.

[11] 曾祖亮.锂渣粉的来源和锂渣粉混凝土的增强抗渗机理探讨[J].四川有色金属,2000(4):49-52.

[12] 河野克哉,市川牧彦,梁承奎,等.混凝土中钢筋锈蚀的氯离子临界浓度及规范[J].混凝土世界,2011(10):34-39.

[13] Khan M I. Nanostructure and microstructure of Cement Concrete Incorporating Multicementious Composites[J].Transp; Res Record,2010,21(41):21-27.

[14] 巴恒静,张武满,邓宏卫.评价高性能混凝土耐久性综合指标——抗氯离子渗透性及其研究现状[J].混凝土,2006(3):3-4,14.

[15] 叶其业,杜乃红,张珩瑜.混凝土氯离子渗透试验研究[J].中国港湾建设,2011(4):35-37.

[16] 孟振亚,刘加平,刘建忠,等.矿物掺合料的掺入对混凝土抗氯离子渗透性能影响的评价与研究[J].混凝土,2010(7):28-30,33.

[17] FELDMAN R F, PRUDENCIOJR L R, CHAN GW. Rapid chloride permeability test on blended cement and other concretes: correlations between charge, initial current and conductivity[J].Construction and Building Materials,1999(13):149-154.

[18] ZHAO T J, ZHOU Z H, ZHU J Q, et al. An alternating test method for concrete permeability[J].Cement and Concrete Research,1998,28(1):7-12.

上一个

矿物掺合料水工混凝土抗氯离子侵蚀性能研究

下一个

高性能混凝土超高泵送施工技术研究

头部文案

冻融循环下锂渣粉对混凝土渗透性的影响

相关文件