C30镁渣混凝土的碳化特性试验研究
Carbonization Test Study on C30 Magnesium Slag Concrete
2015年第4期
混凝土;碳化;镁渣
Concrete; Carbonization; Magnesium slag
2015年第4期
1000-4637(2015)04-86-04
国家自然科学基金项目(51368047);教育部“长江学者和创新团队发展计划”项目(IRT1067)
李 峥,崔自治
宁夏大学土木与水利工程学院,银川 750021

李 峥,崔自治

浏览量:
1000
摘 要:为了实现合理利用粉煤灰、镁渣等工业废渣,提高混凝土抗碳化性能,以镁渣掺量、镁渣消解时间和粉煤灰掺量为因素,设计正交试验L9(34)方案及单因素试验方案,试验研究镁渣混凝土的碳化规律。试验表明,镁渣具有增加碱性储备和补偿收缩变形的双重效应,能显著提高C30混凝土的抗碳化性能,碳化深度与镁渣掺量呈幂指数关系,与碳化时间呈双曲线关系。镁渣和粉煤灰都是影响混凝土碳化性能的重要因素,镁渣消解时间的影响很小,是次要因素。就碳化而言,可以取消镁渣消解环节,简化镁渣混凝土的生产工艺。 Abstract: In order to realize the reasonable utilization of industrial residue such as fly ash, magnesium slag and so on and enhance the carbonation performance of concrete, taking magnesium slag content, magnesium slag digestion time and fly ash content as factors, the orthogonal test L9(34) and the single factor test scheme were designed to research the carbonization law of magnesium slag concrete. The result shows that: magnesium slag has double effects increasing alkaline reserve and compensating shrinkage deformation, and can significantly improve the carbonation performance of C30 concrete; the carbonation depth is the exponential relationship with magnesium slag content, the hyperbolic relationship with carbonization time. Magnesium slag and fly ash are important factors affecting carbonization performance of concrete. The magnesium slag digesting time which is a minor factor has little effect on carbonation. In terms of carbonization, magnesium slag digestion can be cancelled to simplify the production process of magnesium slag concrete.
英文名 : Carbonization Test Study on C30 Magnesium Slag Concrete
刊期 : 2015年第4期
关键词 : 混凝土;碳化;镁渣
Key words : Concrete; Carbonization; Magnesium slag
刊期 : 2015年第4期
DOI :
文章编号 : 1000-4637(2015)04-86-04
基金项目 : 国家自然科学基金项目(51368047);教育部“长江学者和创新团队发展计划”项目(IRT1067)
作者 : 李 峥,崔自治
单位 : 宁夏大学土木与水利工程学院,银川 750021

李 峥,崔自治

摘要
参数
结论
参考文献
引用本文

摘   要:为了实现合理利用粉煤灰、镁渣等工业废渣,提高混凝土抗碳化性能,以镁渣掺量、镁渣消解时间和粉煤灰掺量为因素,设计正交试验L9(34)方案及单因素试验方案,试验研究镁渣混凝土的碳化规律。试验表明,镁渣具有增加碱性储备和补偿收缩变形的双重效应,能显著提高C30混凝土的抗碳化性能,碳化深度与镁渣掺量呈幂指数关系,与碳化时间呈双曲线关系。镁渣和粉煤灰都是影响混凝土碳化性能的重要因素,镁渣消解时间的影响很小,是次要因素。就碳化而言,可以取消镁渣消解环节,简化镁渣混凝土的生产工艺。

Abstract: In order to realize the reasonable utilization of industrial residue such as fly ash, magnesium slag and so on  and enhance the carbonation performance of concrete, taking magnesium slag content, magnesium slag digestion time and fly ash content as factors, the orthogonal test L9(34) and the single factor test scheme were designed to research the carbonization law of magnesium slag concrete. The result shows that: magnesium slag has double effects increasing alkaline reserve and compensating shrinkage deformation, and can significantly improve the carbonation performance of C30 concrete; the carbonation depth is the exponential relationship with magnesium slag content, the hyperbolic relationship with carbonization time. Magnesium slag and fly ash are important factors affecting carbonization performance of concrete. The magnesium slag digesting time which is a minor factor has little effect on carbonation. In terms of carbonization, magnesium slag digestion can be cancelled to simplify the production process of magnesium slag concrete.

关键词:
混凝土;碳化;镁渣
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加
(1)镁渣能提高C30混凝土的抗碳化性能,碳化深度与镁渣掺量呈幂指数关系,与碳化时间呈双曲线关系。
(2)镁渣和粉煤灰掺量都是影响混凝土抗碳化性能的重要因素,镁渣消解时间的影响很小,是次要因素。
(3)镁渣水化生成的Mg(OH)2和 Ca(OH)2具有使混凝土碱性储备增加和收缩变形减小的双重效应,该双重效应是其显著减小混凝土碳化深度的主要机制。
[1] 周万良,方坤河,詹炳根.掺粉煤灰/矿粉混凝土抗碳化性能研究[J].混凝土与水泥制品,2012(12):14-19.
[2] 朱红英,杜应吉,刘明珍,等.粉煤灰不同掺量对混凝土碳化的影响[J].中国农村水利水电,2012(4):150-152.
[3] 阿茹罕,阎培渝.不同粉煤灰掺量混凝土的碳化特性[J].硅酸盐学报,2011,39(1):7-12.
[4] SISOMPHON K, FRANKE L. Carbonation rates of concretes containing high volume of pozzolanic materials[J]. Cem Concr Res, 2007,37(12):1647-1653.
[5] 吕丹丹,刘元珍,李珠.碳化作用下玻化微珠保温混凝土碳化深度及强度变化试验研究[J].混凝土与水泥制品,2014(6):28-31.
[6] 牛荻涛,孙丛涛.混凝土碳化与氯离子侵蚀共同作用研究[J].硅酸盐学报,2013,41(8):1090-1099. 
[7] 孙炳全,刘国志,刘玉莲.混凝土碳化灰色预测模型研究[J].建筑材料学报,2012,15(1):42-47.
[8] 杨毅,杜应吉,曹靖.基于拓扑优化方法确定混凝土碳化保护区域[J].人民黄河,2013,35(1):112-114.
[9] 南峰,伍永华,田荣.利用镁渣制备混凝土膨胀剂[J].西安建筑科技大学学报,2003(7):34-38.
[10] 李姗姗,崔自治.镁渣对C30混凝土干燥收缩的作用效应研究[J].中国农村水利水电,2014(6):158-160.
[11] 崔自治,杨建森.镁渣活化措施试验研究[J].宁夏大学学报,2008,29(3):229-231.
[12] 周健,崔自治,周康,等.镁渣取代部分细骨料对混凝土抗压强度的作用效应研究[J].混凝土,2012(9):54-56.
[13] 崔自治,周康,李潇,等.镁渣细骨料混凝土的强度特性研究[J].混凝土,2013(6):67-69.
[14] 中华人民共和国住房和城乡建设部. GB/T 50082-2009普通混凝土长期性能和耐久性能试验方法标准[S].北京:中国建筑工业出版社,2009:61-63.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州