建筑垃圾挂浆膜化机制对水泥砂浆性能的影响
Influence of Construction Waste Membrane Treatment on Properties of Cement Mortar
2015年第4期
建筑垃圾再生砂;膜化处理;正交试验;性能影响
Construction waste reclaimed sand; Membrane treatment; Orthogonal experiment; Performance effect
2015年第4期
1000-4637(2015)04-93-04
杨子胜,王奕仁,王爱勤
中原工学院建筑工程学院,郑州450007

杨子胜,王奕仁,王爱勤

浏览量:
1000
摘 要:将二水石膏、胶粉、纤维素醚等原料对建筑垃圾再生砂进行膜化处理制备水泥砂浆,通过正交试验和方差分析研究了二水石膏、胶粉、纤维素醚对其性能的影响,得出了抗压强度效果最好的膜化配比为4%石膏、2%胶粉和0.6%纤维素醚,抗折强度效果最好的膜化配比为4%石膏、1%胶粉和0.2%纤维素醚,三种因素对其吸水率影响不大。试验结果表明,经膜化处理建筑垃圾制备的水泥砂浆的性能要优于未处理的建筑垃圾制备的水泥砂浆。 Abstract: The dihydrate gypsum, powder, cellulose ethers and other raw materials are used for construction waste reclaimed sand membrane treatment and preparation of cement mortar, and the effect of dihydrate gypsum, powder, cellulose ethers on performance of cement mortar is studied by the method of orthogonal level analysis and variance analysis. The results show that the membrane proportion of mortar with the best compressive strength is 4% gypsum, 2% powder and 0.6% cellulose ether, the membrane proportion of mortar with the best flexural strength is 4% gypsum, 1% powder and 0.2% cellulose ethers, three factors have little effect on its absorption. The test results show that the performance of cement mortar treated by membrane treatment is superior to that of cement mortar untreated.
英文名 : Influence of Construction Waste Membrane Treatment on Properties of Cement Mortar
刊期 : 2015年第4期
关键词 : 建筑垃圾再生砂;膜化处理;正交试验;性能影响
Key words : Construction waste reclaimed sand; Membrane treatment; Orthogonal experiment; Performance effect
刊期 : 2015年第4期
DOI :
文章编号 : 1000-4637(2015)04-93-04
基金项目 :
作者 : 杨子胜,王奕仁,王爱勤
单位 : 中原工学院建筑工程学院,郑州450007

杨子胜,王奕仁,王爱勤

摘要
参数
结论
参考文献
引用本文

摘   要:将二水石膏、胶粉、纤维素醚等原料对建筑垃圾再生砂进行膜化处理制备水泥砂浆,通过正交试验和方差分析研究了二水石膏、胶粉、纤维素醚对其性能的影响,得出了抗压强度效果最好的膜化配比为4%石膏、2%胶粉和0.6%纤维素醚,抗折强度效果最好的膜化配比为4%石膏、1%胶粉和0.2%纤维素醚,三种因素对其吸水率影响不大。试验结果表明,经膜化处理建筑垃圾制备的水泥砂浆的性能要优于未处理的建筑垃圾制备的水泥砂浆。Abstract: The dihydrate gypsum, powder, cellulose ethers and other raw materials are used for construction waste reclaimed sand membrane treatment and preparation of cement mortar, and the effect of dihydrate gypsum, powder, cellulose ethers on performance of cement mortar is studied by the method of orthogonal level analysis and variance analysis. The results show that the membrane proportion of mortar with the best compressive strength is 4% gypsum, 2% powder and 0.6% cellulose ether, the membrane proportion of mortar with the best flexural strength is 4% gypsum, 1% powder and 0.2% cellulose ethers, three factors have little effect on its absorption. The test results show that the performance of cement mortar treated by membrane treatment is superior to that of cement mortar untreated.

关键词:
建筑垃圾再生砂;膜化处理;正交试验;性能影响
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加
(1)膜化处理后的建筑垃圾再生砂制备的水泥砂浆其抗压强度、抗折强度和吸水率优于未处理建筑垃圾再生砂制备的水泥砂浆。
(2)石膏、胶粉和纤维素醚三个因素在膜化过程中对水泥砂浆的抗压强度都有显著的影响,采用4%的石膏、2%的胶粉和0.6%的纤维素醚对建筑垃圾再生砂进行膜化处理效果最好。
(3)石膏在膜化过程中对水泥砂浆的抗折强度有显著的影响,而胶粉和纤维素醚对其抗折强度的影响不大。采用4%的石膏、1%的胶粉和0.2%的纤维素醚对建筑垃圾再生砂进行膜化处理效果最好。
(4)石膏、胶粉和纤维素醚三个因素对水泥砂浆吸水率的影响都不大。
[1] 王罗春.建筑垃圾处理与资源化[M].北京:化学工业出版社,2004.
[2] 王瑞敏,王林秀.中国建筑垃圾现状分析及发展前景[J].建筑工程,2011(4):178-179.
[3] 左传长.四川汶川地震灾区建筑垃圾资源化利用设想[J].再生资源与循环经济,2008(9):27-30.
[4] 王培铭,孙振平,蒋正武.商品砂浆的研究与应用[M].北京:机械工业出版社,2006.
[5] 鄢朝勇,叶建军.用固体废弃物配制生态建筑砂浆的试验研究[J].混凝土,2012(9):109-111.
[6] 国家质量技术监督局.GB/T 17671-1999 水泥胶砂强度检验方法(ISO)法[S].北京:中国标准出版社,1999.
[7] 刘凤利,张承志,刘俊华.利用废陶瓷再生粗砂配制再生砂浆的试验研究[J].河南大学学报:自然科学版,2011(4):425-428.
[8] 薛森森.王爱勤.建筑垃圾生产建筑砂浆的配合比优化[J].商品混凝土,2010(12):31-37.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州