熟料粒子和纤维复掺对砂浆收缩性能的影响
Effects of Clinker Particles Mixed with Fiber on Shrinkage Performance of Mortar
2015年第7期
熟料粒子;聚丙烯纤维;水泥砂浆;干燥收缩;正交试验;游程检验
Clinker particles; Polypropylene fiber; Cement mortar; Drying shrinkage; Orthogonal experiment; Run test
2015年第7期
1000-4637(2015)07-50-05
国家自然科学基金资助项目(51168041);宁夏大学大学生创新创业训练项目(15TS220)
郑小军,杨建森,伏利鹏,马瑞洁,刘 源,杨 栩
宁夏大学土木与水利工程学院,银川 750021

郑小军,杨建森,伏利鹏,马瑞洁,刘 源,杨 栩

浏览量:
1000
摘 要:针对目前因水泥细度过细而导致水泥基材料容易出现干缩裂缝问题,采用聚丙烯纤维与水泥熟料粒子复掺,并通过L9(34)正交试验研究熟料粒子水泥对聚丙烯纤维砂浆收缩性能的影响。结果表明,复掺熟料粒子和聚丙烯纤维的砂浆收缩率εt与收缩龄期t之间符合εt=α1·exp(-t/α2)+β0的指数函数关系,且在显著性水平α=0.01下其相关性显著;纤维掺量对砂浆收缩影响最大,熟料粒子掺量次之,粒子粗细第三,纤维长度最小;熟料粒子粒径介于0.315~2.5mm之间且其掺量为20%,纤维掺量为0.3%,纤维长度为12mm时,砂浆的收缩最小,体积稳定性最优。 Abstract: The problem for shrinkage cracking of cement-based materials is easily happened by too fine cement fineness at present, using polypropylene fiber mixed with cement clinker particles, and through an orthogonal experiment L9(34), the influence of cement clinker particles on shrinkage performance of polypropylene fiber mortar is carried out. The results indicate that the relationship between the shrinkage ratio εt of mortar and shrinkage age t conforms to exponential function εt=α1·exp(-t/α2)+β0, which is mixed with clinker particles and polypropylene fiber, and the correlation is significant at a significant level of α=0.01. Fiber dosage has the greatest influence on mortar shrinkage, next comes clinker particles dosage, thirdly comes clinker particle size, finally comes fiber length. The shrinkage ratio of mortar is the smallest and the volume stability is optimum when the size of clinker parameter ranges from 0.315mm to 2.5mm, the dosage of clinker particles is 20%, fiber dosage is 0.3% and its length is 12mm.
英文名 : Effects of Clinker Particles Mixed with Fiber on Shrinkage Performance of Mortar
刊期 : 2015年第7期
关键词 : 熟料粒子;聚丙烯纤维;水泥砂浆;干燥收缩;正交试验;游程检验
Key words : Clinker particles; Polypropylene fiber; Cement mortar; Drying shrinkage; Orthogonal experiment; Run test
刊期 : 2015年第7期
DOI :
文章编号 : 1000-4637(2015)07-50-05
基金项目 : 国家自然科学基金资助项目(51168041);宁夏大学大学生创新创业训练项目(15TS220)
作者 : 郑小军,杨建森,伏利鹏,马瑞洁,刘 源,杨 栩
单位 : 宁夏大学土木与水利工程学院,银川 750021

郑小军,杨建森,伏利鹏,马瑞洁,刘 源,杨 栩

摘要
参数
结论
参考文献
引用本文

摘   要:针对目前因水泥细度过细而导致水泥基材料容易出现干缩裂缝问题,采用聚丙烯纤维与水泥熟料粒子复掺,并通过L9(34)正交试验研究熟料粒子水泥对聚丙烯纤维砂浆收缩性能的影响。结果表明,复掺熟料粒子和聚丙烯纤维的砂浆收缩率εt与收缩龄期t之间符合εt=α1·exp(-t/α2)+β0的指数函数关系,且在显著性水平α=0.01下其相关性显著;纤维掺量对砂浆收缩影响最大,熟料粒子掺量次之,粒子粗细第三,纤维长度最小;熟料粒子粒径介于0.315~2.5mm之间且其掺量为20%,纤维掺量为0.3%,纤维长度为12mm时,砂浆的收缩最小,体积稳定性最优。

Abstract: The problem for shrinkage cracking of cement-based materials is easily happened by too fine cement fineness at present, using polypropylene fiber mixed with cement clinker particles, and through an orthogonal experiment L9(34), the influence of cement clinker particles on shrinkage performance of polypropylene fiber mortar is carried out. The results indicate that the relationship between the shrinkage ratio εt of mortar and shrinkage age t conforms to exponential function εt=α1·exp(-t/α2)+β0, which is mixed with clinker particles and polypropylene fiber, and the correlation is significant at a significant level of α=0.01. Fiber dosage has the greatest influence on mortar shrinkage, next comes clinker particles dosage, thirdly comes clinker particle size, finally comes fiber length. The shrinkage ratio of mortar is the smallest and the volume stability is optimum when the size of clinker parameter ranges from 0.315mm to 2.5mm, the dosage of clinker particles is 20%, fiber dosage is 0.3% and its length is 12mm.          

关键词:
熟料粒子;聚丙烯纤维;水泥砂浆;干燥收缩;正交试验;游程检验
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加
(1)各因素对砂浆收缩率影响的顺序为:纤维掺量最大,熟料粒子掺量次之,熟料粒子粗细第三,纤维长度最小。
(2)配制参数为熟料粒子粒径介于0.315~2.5 mm之间,熟料粒子掺量20%,纤维掺量0.3%,纤维长度12mm的水泥砂浆,其收缩变形最小,体积稳定性最优。
(3)熟料粒子和纤维复掺的水泥砂浆收缩模型符合指数函数εt=α1·exp(-t/α2)+β0的形式,经游程检验其相关关系显著。

[1] 张楠,郭丽娟.我国水泥工业发展状况研究[J].赤峰学院学报:自然科学版,2009,25(2):129-131.

[2] 刘冠国,马虎,曹鹏飞.水泥细度对早龄期混凝土抗裂性能的影响[J].混凝土,2011(12):70-72.
[3] 周世华,杨华全,董芸,等.水泥细度对砂浆体积稳定性的影响[J].水利水电技术,2008,39(10):38-61.
[4] 李悦,刘雄飞.水泥基材料收缩及其导致开裂的研究进展[J].混凝土,2014(3):90-93.
[5] 郭秋兰.建筑材料[M].哈尔滨:哈尔滨工业大学出版社,2013.
[6] Bentza D.P, Garboczi EJ, Haecker CJ,et al.Effects of cement particle size distribution on performance properties of Portland cement-based materials[J]. Cement and Concrete Research,1999,29(10):1663-1671.
[7] 宁超,赵帅,李国忠.改性聚丙烯纤维对水泥砂浆抗干燥收缩性能的影响[J].建筑砌块与砌块建筑,2009(4):49-51.
[8] 马一平,仇建刚,王培铭,等.聚丙烯纤维对水泥砂浆塑性收缩行为的影响[J].建筑材料学报,2005,8(5):499-507.
[9] 李云雁,胡传荣. 试验设计与数据处理[M]. 北京:化学工业出版社,2008.
[10] 唐龙超. 聚丙烯纤维混凝土抗裂性能试验研究[J].科技信息,2013(14):465-466.
[11] 曹双梅,钟颖川,张世海.聚丙烯纤维混凝土及其在环形超长无缝结构中的应用[J].混凝土与水泥制品,2013(7):77-79.
[12] 李伏琦,付诚,张静.聚丙烯纤维对混凝土性能的影响研究[J].全面腐蚀控制,2012,26(8):39-43. 
[13] 禹凯,钱晓倩,张轶伦.聚丙烯纤维对混凝土早期收缩影响的试验研究[J].混凝土,2007(5):64-68.
[14] 吴中伟.混凝土材料学——各种混凝土的组成与结构[J].混凝土及建筑构件,1980(4):1-6.
[15] 吴中伟.混凝土材料学——各种混凝土的组成与结构(续)[J].混凝土及建筑构件,1980(5):1-14.
[16] 刘树华,冷发光,罗季英. 建筑材料试验研究的数学方法[M]. 北京:中国建材出版社,2006.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州