砂子级配对砂浆冲蚀磨损性能的影响
Effects of Sand Grading on Erosion Wear Properties of Mortar
2015年第8期
砂浆;级配;冲蚀磨损
Mortar;Grading; Erosion wear
2015年第8期
1000-4637(2015)08-16-04
长江学者和创新团队发展计划资助(IRT1139)
赵彦华,王彦平,王起才
兰州交通大学土木工程学院,730070

赵彦华,王彦平,王起才

浏览量:
1000
摘 要:处在强风沙流地段的混凝土结构会受到强风挟带沙粒的的冲蚀磨损,造成混凝土结构耐久性的降低。本文采用气流挟沙喷射法模拟戈壁风沙流环境,对不同砂子级配砂浆进行冲蚀磨损试验,研究冲蚀参数及砂子级配对砂浆冲蚀磨损性能的影响。试验结果表明,不同砂子级配砂浆在各冲蚀速度下,90°冲蚀时冲蚀率最高,而30°冲蚀时冲蚀率最低,与传统脆性材料的冲蚀规律相一致。砂浆试样所用砂子的级配影响其冲蚀率,砂浆试样所用砂子的级配越小,则其冲蚀率越大,级配越大,则其冲蚀率越小。不同砂子级配砂浆短期内的冲蚀机制主要为选择性冲蚀。 Abstract: The concrete structure are seriously eroded by grains of sand carried by strong winds, causing the durability of concrete construction to reduce. In this paper, the erosion wear test of mortar samples with different sand grading were carried out by grit-blasting experiments, and the effect of impact parameters and sand grading on the mortar erosion wear were investigated. The results show that under different erosion speed for mortar samples with different sand grading, erosion rates were highest at 90° impact, and lowest at 30° impact, which was consistent with traditional brittle material erosion laws. The sand grading affect erosion rate of mortar samples, erosion rates were highest for low sand grading, and lowest for high sand grading. The erosion wear mechanism of mortars is selective erosion wear in the short term.
英文名 : Effects of Sand Grading on Erosion Wear Properties of Mortar
刊期 : 2015年第8期
关键词 : 砂浆;级配;冲蚀磨损
Key words : Mortar;Grading; Erosion wear
刊期 : 2015年第8期
DOI :
文章编号 : 1000-4637(2015)08-16-04
基金项目 : 长江学者和创新团队发展计划资助(IRT1139)
作者 : 赵彦华,王彦平,王起才
单位 : 兰州交通大学土木工程学院,730070

赵彦华,王彦平,王起才

摘要
参数
结论
参考文献
引用本文

摘   要:处在强风沙流地段的混凝土结构会受到强风挟带沙粒的的冲蚀磨损,造成混凝土结构耐久性的降低。本文采用气流挟沙喷射法模拟戈壁风沙流环境,对不同砂子级配砂浆进行冲蚀磨损试验,研究冲蚀参数及砂子级配对砂浆冲蚀磨损性能的影响。试验结果表明,不同砂子级配砂浆在各冲蚀速度下,90°冲蚀时冲蚀率最高,而30°冲蚀时冲蚀率最低,与传统脆性材料的冲蚀规律相一致。砂浆试样所用砂子的级配影响其冲蚀率,砂浆试样所用砂子的级配越小,则其冲蚀率越大,级配越大,则其冲蚀率越小。不同砂子级配砂浆短期内的冲蚀机制主要为选择性冲蚀。

Abstract: The concrete structure are seriously eroded by grains of sand carried by strong winds, causing the durability of concrete construction to reduce. In this paper, the erosion wear test of mortar samples with different sand grading were carried out by grit-blasting experiments, and the effect of impact parameters and sand grading on the mortar erosion wear were investigated. The results show that under different erosion speed for mortar samples with different sand grading, erosion rates were highest at 90° impact, and lowest at 30° impact, which was consistent with traditional brittle material erosion laws. The sand grading affect erosion rate of mortar samples, erosion rates were highest for low sand grading, and lowest for high sand grading. The erosion wear mechanism of mortars is selective erosion wear in the short term.

关键词:
砂浆;级配;冲蚀磨损
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加
(1)砂浆试样的冲蚀率均随着风沙流速度的增大而显著增加。
(2)不同级配砂浆在各冲蚀速度下,90°冲蚀时冲蚀率最高,而30°冲蚀时冲蚀率最低,与脆性材料的冲蚀规律相一致。
(3)砂浆试样所用砂子的级配影响其冲蚀率,砂浆试样所用砂子的级配越小,则其冲蚀率越大,级配越大,则其冲蚀率越小。
(4)砂浆试样经1~2min的冲蚀后,便进入稳态冲蚀阶段。试验表明砂浆短期内的冲蚀机制主要为选择性冲蚀。
[1]李凯崇,蒋富强,薛春晓,等. 兰新铁路十三间房段的戈壁风沙流特征分析[J].铁道工程学报,2010,138(3):15-18.
[2] 蒋富强,李荧,李凯崇,等. 兰新铁路百里风区风沙流结构特性研究[J].铁道学报,2010,32(3):105-110.
[3] 王彦平,居春常,王起才.冲击参数对兰新铁路混凝土结构冲蚀磨损的影响[J].硅酸盐通报,2013,32(4):607-612.
[4] 王彦平,居春常,王起才. 风沙环境下混凝土、砂浆和水泥石的固体颗粒冲蚀磨损试验研究[J].中国铁道科学,2013,34(5):22-27.
[5] Yu W L. Improving the abrasion resistance of hydraulic-concrete containing surface crack by adding silica fume[J].Construction and Building Materials, 2007,21(5):972-977.
[6] 尹延国,胡献国,崔德密.水工混凝土冲击磨损行为与机理研究[J]. 水力发电学报,2001,75(4):57-64.
[7] K.C.Goretta,M.L.Burdt,M.M.Cuber. Solid-particle erosion of Portland cement and concrete[J]. Wear, 1999, 224(1):106-112. 
[8] A.W.Momber. The erosion of cement paste, mortar and concrete by gritblasting[J]. Wear ,2000, 246(1-2):46-54.
[9] A.W.Momber. Damage to Rocks and Cementitious Materials from Solid Impact[J]. Rock Mechanics and Rock Engineering, 2004,37(1):57-82.
[10] 郝贲洪,邢永明,杨诗婷.风沙环境下钢结构表面涂层冲蚀行为与侵蚀机理研究[J]. 摩擦学学报,2010,30(1):26-31.
[11] Goretta K C, Gutierrez M F, Chen N, etc. Solid-particle erosion and strength degradation of Si3N4/BN fibrous monoliths[J]. Wear,2004,256(3/4):233–242.
[12] 邢志国,吕振林,谢辉. SiC/环氧树脂复合材料冲蚀磨损性能的研究[J]. 摩擦学学报,2010,30(3):291-295.
 

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州