花岗岩环保型透水砖的研制
Preparation of Environmental Permeable Brick with Granite
2015年第8期
花岗岩边角废料;透水砖;透水性能;孔隙率;配合比设计;骨料粒径;生石灰
Leftover waste material of granite; Water permeable brick; Permeability performance; Porosity; Mix design; Aggregate size; Lime
2015年第8期
1000-4637(2015)08-67-06
陈连发1,陈 悦2,李 龙3,陆 洋4
1.吉林化工学院材料科学与工程学院,132022;2.中国电器科学研究院有限公司威凯检测家电 事业部压缩机工程部,广州510663;3.亚泰集团长春建材有限公司吉林市分公司,132022; 4.冀东水泥城建混凝土有限公司,吉林132201

陈连发1,陈 悦2,李 龙3,陆 洋4

浏览量:
1000
摘 要:利用正交试验分析了制备透水砖过程中花岗岩骨料粒径、集灰比、水灰比、生石灰掺量等因素的影响并对其重要性进行排序。研究了各因素与抗压强度、抗折强度、透水系数和孔隙率的关系。讨论了静压成型压力和振动成型时间对孔隙率和透水系数的影响。根据混合材料最优配比参数,完成了制作透水砖的最佳配合比设计方案。试验证明:经加工处理后的花岗岩石材边角废料是制备环保型透水砖的有益材料。 Abstract: The effects of granite aggregate size, aggregate cement ratio, water cement ratio, lime dosage, etc. on performance of water permeable brick were analyzed by using orthogonal test and the importance of these factors were ranked. The relationships of orthogonal factors and the performance such as compressive strength, flexural strength, permeability coefficient and porosity were researched. The influence of static molding pressure and vibration molding time on the porosity and the permeability coefficient was discussed. The best mix design for making permeable brick was completed according to the optimal ratio of mixtures. The test results prove that: the leftover waste material granite after processing is a good material for preparing environmental permeable brick.
英文名 : Preparation of Environmental Permeable Brick with Granite
刊期 : 2015年第8期
关键词 : 花岗岩边角废料;透水砖;透水性能;孔隙率;配合比设计;骨料粒径;生石灰
Key words : Leftover waste material of granite; Water permeable brick; Permeability performance; Porosity; Mix design; Aggregate size; Lime
刊期 : 2015年第8期
DOI :
文章编号 : 1000-4637(2015)08-67-06
基金项目 :
作者 : 陈连发1,陈 悦2,李 龙3,陆 洋4
单位 : 1.吉林化工学院材料科学与工程学院,132022;2.中国电器科学研究院有限公司威凯检测家电 事业部压缩机工程部,广州510663;3.亚泰集团长春建材有限公司吉林市分公司,132022; 4.冀东水泥城建混凝土有限公司,吉林132201

陈连发1,陈 悦2,李 龙3,陆 洋4

摘要
参数
结论
参考文献
引用本文

摘   要:利用正交试验分析了制备透水砖过程中花岗岩骨料粒径、集灰比、水灰比、生石灰掺量等因素的影响并对其重要性进行排序。研究了各因素与抗压强度、抗折强度、透水系数和孔隙率的关系。讨论了静压成型压力和振动成型时间对孔隙率和透水系数的影响。根据混合材料最优配比参数,完成了制作透水砖的最佳配合比设计方案。试验证明:经加工处理后的花岗岩石材边角废料是制备环保型透水砖的有益材料。

Abstract: The effects of granite aggregate size, aggregate cement ratio, water cement ratio, lime dosage, etc. on performance of water permeable brick were analyzed by using orthogonal test and the importance of these factors were ranked. The relationships of orthogonal factors and the performance such as compressive strength, flexural strength, permeability coefficient and porosity were researched. The influence of static molding pressure and vibration molding time on the porosity and the permeability coefficient was discussed. The best mix design for making permeable brick was completed according to the optimal ratio of mixtures. The test results prove that: the leftover waste material granite after processing is a good material for preparing environmental permeable brick.

关键词:
花岗岩边角废料;透水砖;透水性能;孔隙率;配合比设计;骨料粒径;生石灰
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加
(1)影响透水砖孔隙率的重要性因素,依次顺序为集灰比、花岗岩碎石粒径大小、水灰比、生石灰掺量。而影响透水砖透水系数的重要性因素,依次顺序排列为花岗岩碎石粒径大小、集灰比、水灰比、生石灰掺量。因此,影响透水系数最重要的因素就是花岗岩碎石集料颗粒粒径的大小。
(2)当面层粒径取10~15mm、基层粒径取15~20mm、集灰比取4.0、水灰比取0.30、生石灰、粉煤灰等量取代水泥的量分别取为5%、10%、减水剂掺入量为胶凝材料的0.7%、采用静压成型的压力取4MPa、保压时间为2min,即可制备出28d抗压强度值达到25MPa以上,28d抗折强度达到6MPa以上,孔隙率为20%以上,透水系数达到1.5mm/s以上的透水砖。
[1] 左富云. 建筑垃圾在透水砖及城市道路上的应用[D].昆明: 昆明理工大学,2008.
[2] 程娟. 透水混凝土配合比设计及其性能的实验研究[D]. 杭州:浙江工业大学,2006.
[3] 中华人民共和国国家发展和改革委员会.JC/T 945—2005 透水砖行业标准[S].北京:中国建材工业出版社,2005.
[4] 姜德民,徐三元,张友权.彩色透水性混凝土路面砖的研制[J].北方工业大学学报,2004,16(3):85-88.
[5] 霍亮.透水性混凝土路面材料的制备及性能研究[D]. 南京:东南大学,2004.
[6] 阎振甲,何艳君.工业废渣生产建筑材料实用技术[M].北京:化学工业出版社,2003.
[7] 朴应模,李珍淑,李康. PAE-水泥透水性混凝土的空隙率、透水系数及耐酸性能[J].延边大学学报:自然科学版,2004,30(2):118-123.
[8] 饶玲丽,曹建新,张洪波,等.粉煤灰透水砖的制备研究[J]. 新型建筑材料,2006(7):48-50.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州