扩链剂改性聚羧酸系高性能减水剂的试验研究
Experimental Research on Chain Extender Modified Polycarboxylic High Performance Water Reducer
2015年第9期
扩链剂;聚羧酸系;高性能减水剂;改性;分散性;多功能
Chain extender; Polycarboxylic; High performance water reducer; Modification; Dispersiveness; Multi-function
2015年第9期
1000-4637(2015)09-01-05
山西省科技攻关项目(20130321034-03)
王茂桑1,黄世谋2,李宪军1
山西省建筑科学研究院,太原 030001;2.三门峡职业技术学院,472000

王茂桑1,黄世谋2,李宪军1

浏览量:
1000
摘 要:对四种聚羧酸系高性能减水剂进行了扩链剂改性研究,并优化出最佳改性工艺。结果表明,改性后的聚羧酸系高性能减水剂A对水泥的分散性能仅起到抵消缓释作用,B、C、D对水泥的分散性能有很大的提高,尤其是对保坍性能较差的减水剂;改性后的减水剂对混凝土的流变性能与水泥净浆流动度的变化规律基本一致,对混凝土的含气量、抗压强度、渗透性能和外观质量有了明显改善,而且降低了成本;同时,从分子链结构搭配的角度分析了扩链剂的改性机理。 Abstract: Four kinds of polycarboxylic high performance water reducer were modified by chain extender, and the best modification technology was optimized. The results show that the modified polycarboxylic high performance water reducer A only plays release effect on the dispersiveness of cement, while the modified polycarboxylic high performance water reducer B, C and D can greatly improve the dispersiveness of the cement, especially to the water reducer with poor slump performance. Furthermore, the influence of the modified water reducer on rheological properties of concrete has the same rule as that of the modified water reducer on the fluidity of cement paste. In addition, gas content, compressive strength, permeability and appearance quality of the concrete are obviously improved and the cost is also reduced. Finally, the modification mechanism of chain extender is analyzed from the point of the molecular chain structure.
英文名 : Experimental Research on Chain Extender Modified Polycarboxylic High Performance Water Reducer
刊期 : 2015年第9期
关键词 : 扩链剂;聚羧酸系;高性能减水剂;改性;分散性;多功能
Key words : Chain extender; Polycarboxylic; High performance water reducer; Modification; Dispersiveness; Multi-function
刊期 : 2015年第9期
DOI :
文章编号 : 1000-4637(2015)09-01-05
基金项目 : 山西省科技攻关项目(20130321034-03)
作者 : 王茂桑1,黄世谋2,李宪军1
单位 : 山西省建筑科学研究院,太原 030001;2.三门峡职业技术学院,472000

王茂桑1,黄世谋2,李宪军1

摘要
参数
结论
参考文献
引用本文

摘   要:对四种聚羧酸系高性能减水剂进行了扩链剂改性研究,并优化出最佳改性工艺。结果表明,改性后的聚羧酸系高性能减水剂A对水泥的分散性能仅起到抵消缓释作用,B、C、D对水泥的分散性能有很大的提高,尤其是对保坍性能较差的减水剂;改性后的减水剂对混凝土的流变性能与水泥净浆流动度的变化规律基本一致,对混凝土的含气量、抗压强度、渗透性能和外观质量有了明显改善,而且降低了成本;同时,从分子链结构搭配的角度分析了扩链剂的改性机理。

Abstract: Four kinds of polycarboxylic high performance water reducer were modified by chain extender, and the best modification technology was optimized. The results show that the modified polycarboxylic high performance water reducer A only plays release effect on the dispersiveness of cement, while the modified polycarboxylic high performance water reducer B, C and D can greatly improve the dispersiveness of the cement, especially to the water reducer with poor slump performance. Furthermore, the influence of the modified water reducer on rheological properties of concrete has the same rule as that of the modified water reducer on the fluidity of cement paste. In addition, gas content, compressive strength, permeability and appearance quality of the concrete are obviously improved and the cost is also reduced. Finally, the modification mechanism of chain extender is analyzed from the point of the molecular chain structure. 

关键词:
扩链剂;聚羧酸系;高性能减水剂;改性;分散性;多功能
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加
(1)通过对三个聚羧酸系高性能减水剂生产厂家的四个产品进行了改性研究,优化出的改性工艺为:扩链剂最佳掺量为0.8%,反应温度应控制在40~60℃之间,反应时间应控制在20~50min之间。
(2)聚羧酸系高性能减水剂A属于缓释型减水剂,改性起到抵消缓释作用,聚羧酸系高性能减水剂B、C、D改性后对水泥净浆的分散性能都有很大的提高。四种减水剂改性后对混凝土的含气量、抗压强度、渗透性能和外观质量有了明显提高。在复配过程中可少掺或不掺保坍组分和消泡组分,极大地降低了生产成本。
(3)扩链剂对聚羧酸系高性能减水剂的改性研究尚属首次,其分子结构变化有待验证。改性后的聚羧酸系高性能减水剂对砂中较高含泥量未见不良影响,还需进一步研究,对混凝土碳化性能等耐久性指标也有待系统研究。该研究对聚羧酸系高性能减水剂母液多功能化、高性能化具有深远意义。
[1] 王玲,田培,白杰,等. 我国混凝土减水剂的现状及未来[J].混凝土与水泥制品,2008(5):1-7.
[2] 沙建芳,刘宏,徐海源,等.聚羧酸减水剂民用化存在问题及对策[J].混凝土,2013(1):89-93.
[3] 周忠群,陈小平,申迎华,等.新型聚羧酸系高效减水剂的合成及应用性能[J].混凝土,2011(5):70-72.
[4] 徐兆付,夏咏梅,张磊.聚羧酸系水泥减水剂的合成及性能[J] .应用化工,2008,37(8):847-850.
[5] 虞亚丽,刘俊平,霍利利.无热源聚羧酸减水剂聚合工艺以及性能研究[J].混凝土,2014(11):84-86.
[6] 王玉娇,胡若飞,鲁俊. 聚羧酸型减水剂低温合成工艺研究[J] .应用化工,2014,43(2):225-227.
[7] 雷道斌.对日本混凝土外加剂发展现状的思考[J].混凝土, 2001(11):18-20.
[8] 彭雄义,易聪华,张智,等.聚羧酸系减水剂对水泥分散和水化产物的影响[J].建筑材料学报,2010,13(5):578-583.
[9] HAMADA D, HAMAI T, SHONAKA M. New superplasticizer providing ultimate workability[J]. Pro, JCI,2006,28(1):185-190.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州