三相导电混凝土强度及导电性能试验研究
Experimental Research on Strength of Graphite Conductive Concrete and Conductivity
2015年第9期
导电混凝土;抗压强度;导电性能;电阻率;灰关联分析
Conductive concrete; Compressive strength; Conductivity; Resistivity; Gray correlation analysis
2015年第9期
1000-4637(2015)09-14-06
钢筋约束混凝土梁柱节点的抗压和抗剪性能研究(2015ZB30)
欧阳平
广州番禺职业技术学院,511483)

欧阳平

浏览量:
1000
摘 要:为优化碳纤维-钢纤维-石墨三相导电混凝土中三种导电材料的组成比例,试验研究了三种材料掺量以及石墨细度对混凝土抗压强度和导电性能的影响,并通过灰关联分析得出三种材料对导电性能影响的显著程度。结果表明,碳纤维掺量越大,混凝土导电性能越好,当碳纤维掺量大于0.8%时,电阻率趋于稳定,当碳纤维掺量为0.4%时强度最大,初步确定碳纤维掺量为0.4%;电阻率与碳纤维掺量之间呈对数规律变化;养护龄期越长,导电性能越差,当龄期超过21d后,导电性能趋于稳定;石墨颗粒越细混凝土强度越低,导电性能越好,其中石墨细度为400目和600目时导电性能极为接近;随着石墨掺量的增大,抗压强度和电阻率逐渐减小,当石墨掺量超过8%时,导电性能趋于稳定。综合确定碳纤维、钢纤维和石墨掺量分别为0.5%、0.8%和5%时,混凝土导电性能最好,同时具有较高的强度;三种导电材料对混凝土导电性能影响的显著程度是:碳纤维>石墨>钢纤维。 Abstract: In order to optimize carbon fiber-steel fiber-graphite conductive concrete composition ratio of the three-conductive material, through experiment, the effects of three graphite materials content and fineness on concrete compressive strength and electrical conductivity are studied in this paper, and through Grey analysis of the three materials, significant degree of influence on conductivity is derived. The results show that the greater the carbon fiber content, the better the performance of concrete conductivity, when the carbon fiber content greater than 0.8%, the resistivity tends to be stable, while the carbon fiber content of 0.4%, the maximum intensity, initially identified carbon fiber content is 0.4%; logarithmically content varies between resistivity and carbon fiber. The longer the curing period, the worse conductivity, and when the age of more than 21d, the conductive properties are stabilized. The finer the graphite particles, the lower the concrete strength, and the better the electrical conductivity, in which the graphite fineness of 400 mesh and 600 mesh, the conductive properties are extremely close. As the graphite content increases, the compressive strength and electrical resistivity decreases, when the graphite content exceeds 8%, the conductivity is stabilized. Comprehensive determining carbon fiber, steel fiber and graphite content with 0.5%, 0.8% and 5%, the best performance concrete conductivity and high strength can be obtained, and a significant degree of three-conductive material on conductive property effects of concrete is: carbon fiber>graphite>steel fiber.
英文名 : Experimental Research on Strength of Graphite Conductive Concrete and Conductivity
刊期 : 2015年第9期
关键词 : 导电混凝土;抗压强度;导电性能;电阻率;灰关联分析
Key words : Conductive concrete; Compressive strength; Conductivity; Resistivity; Gray correlation analysis
刊期 : 2015年第9期
DOI :
文章编号 : 1000-4637(2015)09-14-06
基金项目 : 钢筋约束混凝土梁柱节点的抗压和抗剪性能研究(2015ZB30)
作者 : 欧阳平
单位 : 广州番禺职业技术学院,511483)

欧阳平

摘要
参数
结论
参考文献
引用本文

摘   要:为优化碳纤维-钢纤维-石墨三相导电混凝土中三种导电材料的组成比例,试验研究了三种材料掺量以及石墨细度对混凝土抗压强度和导电性能的影响,并通过灰关联分析得出三种材料对导电性能影响的显著程度。结果表明,碳纤维掺量越大,混凝土导电性能越好,当碳纤维掺量大于0.8%时,电阻率趋于稳定,当碳纤维掺量为0.4%时强度最大,初步确定碳纤维掺量为0.4%;电阻率与碳纤维掺量之间呈对数规律变化;养护龄期越长,导电性能越差,当龄期超过21d后,导电性能趋于稳定;石墨颗粒越细混凝土强度越低,导电性能越好,其中石墨细度为400目和600目时导电性能极为接近;随着石墨掺量的增大,抗压强度和电阻率逐渐减小,当石墨掺量超过8%时,导电性能趋于稳定。综合确定碳纤维、钢纤维和石墨掺量分别为0.5%、0.8%和5%时,混凝土导电性能最好,同时具有较高的强度;三种导电材料对混凝土导电性能影响的显著程度是:碳纤维>石墨>钢纤维。

Abstract: In order to optimize carbon fiber-steel fiber-graphite conductive concrete composition ratio of the three-conductive material, through experiment, the effects of three graphite materials content and fineness on concrete compressive strength and electrical conductivity are studied in this paper, and through Grey analysis of the three materials, significant degree of influence on conductivity is derived. The results show that the greater the carbon fiber content, the better the performance of concrete conductivity, when the carbon fiber content greater than 0.8%, the resistivity tends to be stable, while the carbon fiber content of 0.4%, the maximum intensity, initially identified carbon fiber content is 0.4%; logarithmically content varies between resistivity and carbon fiber. The longer the curing period, the worse conductivity, and when the age of more than 21d, the conductive properties are stabilized. The finer the graphite particles, the lower the concrete strength, and the better the electrical conductivity, in which the graphite fineness of 400 mesh and 600 mesh, the conductive properties are extremely close. As the graphite content increases, the compressive strength and electrical resistivity decreases, when the graphite content exceeds 8%, the conductivity is stabilized. Comprehensive determining carbon fiber, steel fiber and graphite content with 0.5%, 0.8% and 5%, the best performance concrete conductivity and high strength can be obtained, and a significant degree of three-conductive material on conductive property effects of concrete is: carbon fiber>graphite>steel fiber.

关键词:
导电混凝土;抗压强度;导电性能;电阻率;灰关联分析
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加
(1)抗压强度随碳纤维掺量的增大表现出先增大后减小的变化趋势,当掺量为0.4%时,抗压强度最大;碳纤维掺量越大,混凝土电阻率越小,导电性能越好;当碳纤维掺量大于0.8%时,电阻率趋于稳定,综合确定碳纤维掺量为0.4%;混凝土电阻率与碳纤维掺量之间呈现很好的对数规律变化;随着养护龄期的延长,电阻率逐渐增大,导电性能逐渐下降,当龄期超过21d后,导电性能趋于稳定。
(2)石墨目数越大,混凝土强度越低,电阻率越小,当目数为400目和600目时电阻率相差不大;随着石墨掺量的增大,混凝土抗压强度和电阻率逐渐减小,当石墨掺量超过8%时,混凝土导电性能趋于稳定。
(3)当碳纤维、钢纤维和石墨掺量分别为0.5%、0.8%和5%时,三相导电混凝土不仅具有最佳的导电性能,而且具有较高的强度;三种导电材料对混凝土导电性能影响的显著程度是:碳纤维>石墨>钢纤维。
[1] 回国臣,吴献.三相受压导电混凝土物理力学性能试验研究[J].混凝土, 2014(1): 24-27.
[2] 赵若红,钱兴,傅继阳.超低温环境下导电混凝土除冰及其冻融循环性能研究[J].混凝土与水泥制品, 2013(12): 41-43.
[3] 卢珍,物献,杨昆.炭黑碳纤维复相导电混凝土的导电性能研究[J].混凝土, 2014(11): 81-83.
[4] 赵若红,甘可,傅继阳.钢纤维石墨导电混凝土比热的试验研究[J].混凝土与水泥制品, 2014(2): 40-43.
[5] 孙亚飞,高培伟,刘宏伟, 等.复相导电混凝土强度及其导电性能[J].材料科学与工程学报, 2014, 32(3): 372-375.
[6] 徐令娜,赵庆新,李炜, 等.碳纤维炭黑导电混凝土的接地特性研究[J].硅酸盐通报, 2014, 33(12): 3366-3370.
[7] 王凤池, 张满园, 宋文, 等.钢渣混凝土导电及力学性能的试验研究[J].济南大学学报: 自然科学版, 2014, 28(4): 306-310.
[8] 马世宁,刘晓军,张元龙.碳纤维导电混凝道面机场除冰雪的应用研究[J].路基工程, 2011(3): 182-184.
[9] 王福玉.粗骨料碳纤维混凝土导电特性研究[D].郑州: 郑州大学, 2014.
[10] 彭海龙.掺功能材料水泥基材料电性能和磁性能的研究[D].南京: 南京航空航天大学, 2013.
[11] 刘涛.复掺西钢纤维和石墨的水泥基复合材料的压敏性研究[D].武汉: 武汉理工大学, 2013.
[12] 邓聚龙.灰色系统理论教程[M].武汉: 华中理工大学出版社, 1990.
[13] 张岐山,郭喜江,邓聚龙.灰关联熵分析方法[J].系统工程理论与实践, 1996(8): 7-11.
[14] 钱兴,赵若红,傅继阳.低压下钢纤维石墨导电混凝土升温性能研究[J].混凝土与水泥制品, 2013(6): 37-39.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州