聚苯颗粒泡沫混凝土性能的影响因素研究
Influencing Factors Research on Performance of Foam Concrete with Polystyrene Particles
2015年第11期
泡沫混凝土;聚苯颗粒;比强度;导热系数;孔结构
Foam concrete; Polystyrene particle; Specific strength; Thermal conductivity; Pore structure
2015年第11期
1000-4637(2015)11-78-03
权娟娟,马 斌
西京学院土木工程学院,西安 710123

权娟娟,马 斌

浏览量:
1000
摘 要:研究了聚苯颗粒掺量为2400mL、2600mL、2800mL时各因素对泡沫混凝土性能的影响,确定了原料最佳配合比。结果表明,以比强度为考核指标时,最佳配合比为:水胶比0.65、泡沫掺量3500mL、聚苯颗粒掺量2800mL;以导热系数为考核指标时,最佳配合比为:水胶比0.55、泡沫掺量2500mL、聚苯颗粒掺量2400mL。孔结构分析表明,掺加聚苯颗粒泡沫混凝土的孔隙率增大和孔隙尺寸降低,都会明显提高其力学性能。 Abstract: The effects of various factors on properties of foam concrete are studied when polystyrene particles dosage is 2400mL, 2600mL and 2800mL, the best mix ratio of raw materials is determined. The results show that with the specific strength as assessment indicators, the best mixing ratio include that water/cement ratio is 0.65, foam dosage is 3500mL, polystyrene particles dosage is 2800mL; with the thermal conductivity as assessment indicators, the best mixing ratio include 0.55 water/cement ratio, 2500mL foam dosage, 2400mL polystyrene particles dosage. Pore structure analysis indicate that by adding polystyrene particles, porosity of foam concrete is increased and pore size of foam concrete is decreased, which can obviously improve its mechanical properties.
英文名 : Influencing Factors Research on Performance of Foam Concrete with Polystyrene Particles
刊期 : 2015年第11期
关键词 : 泡沫混凝土;聚苯颗粒;比强度;导热系数;孔结构
Key words : Foam concrete; Polystyrene particle; Specific strength; Thermal conductivity; Pore structure
刊期 : 2015年第11期
DOI :
文章编号 : 1000-4637(2015)11-78-03
基金项目 :
作者 : 权娟娟,马 斌
单位 : 西京学院土木工程学院,西安 710123

权娟娟,马 斌

摘要
参数
结论
参考文献
引用本文

摘   要:研究了聚苯颗粒掺量为2400mL、2600mL、2800mL时各因素对泡沫混凝土性能的影响,确定了原料最佳配合比。结果表明,以比强度为考核指标时,最佳配合比为:水胶比0.65、泡沫掺量3500mL、聚苯颗粒掺量2800mL;以导热系数为考核指标时,最佳配合比为:水胶比0.55、泡沫掺量2500mL、聚苯颗粒掺量2400mL。孔结构分析表明,掺加聚苯颗粒泡沫混凝土的孔隙率增大和孔隙尺寸降低,都会明显提高其力学性能。

Abstract: The effects of various factors on properties of foam concrete are studied when polystyrene particles dosage is 2400mL, 2600mL and 2800mL, the best mix ratio of raw materials is determined. The results show that with the specific strength as assessment indicators, the best mixing ratio include that  water/cement ratio is 0.65, foam dosage is 3500mL, polystyrene particles dosage is 2800mL; with the thermal conductivity as assessment indicators, the best mixing ratio include 0.55 water/cement ratio, 2500mL foam dosage, 2400mL polystyrene particles dosage. Pore structure analysis indicate that by adding polystyrene particles, porosity of foam concrete is increased and pore size of foam concrete is decreased, which can obviously improve its mechanical properties. 

关键词:
泡沫混凝土;聚苯颗粒;比强度;导热系数;孔结构
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加
(1)在水胶比和泡沫掺量一定的条件下,泡沫混凝土试块的干密度和抗压强度均随聚苯颗粒掺量的增加而明显减小。
(2)聚苯颗粒掺量对泡沫混凝土比强度影响的显著优劣顺序为:聚苯颗粒掺量>泡沫掺量>水胶比,最佳配合比为:水胶比为0.65、泡沫掺量为3500mL、聚苯颗粒掺量为2600mL;聚苯颗粒掺量对泡沫混凝土导热系数影响的显著优劣顺序为:聚苯颗粒掺量>泡沫掺量>水胶比,最佳配合比为:水胶比为0.60、泡沫掺量为3500mL、聚苯颗粒掺量为2600mL。
(3)掺加聚苯颗粒的泡沫混凝土的孔隙率增大和孔隙尺寸降低,均可明显提高其力学性能。但是掺有聚苯颗粒的泡沫混凝土真圆度较空白组的真圆度稍有增大,导致其抗压强度低于未掺加聚苯颗粒的泡沫混凝土。
[1] 吴成,谭家升.聚苯泡沫混凝土在屋面保温系统的应用与施工[J].辽宁建材,2011(11):50-51.
[2] 张磊,杨鼎宜.轻质泡沫混凝土的研究及应用现状[J].混凝土,2005(8):44-48.
[3] 蔡娜,张智强.超轻泡沫混凝土保温材料的实验研究[D].重庆:重庆大学,2009.
[4] 张磊蕾,王武祥.水料比对泡沫混凝土孔结构和性能的影响研宄[J].建材技术与应用,2011(5):1-3.
[5] Just A, Middendorf B. Microstructure of high-strength foam concrete[J]. Materialsn Characterization,2009,60(7):741-748.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州