全再生细骨料对砂浆性能影响的实验研究
Experimental Study on Influence of All Recycled Fine Aggregate on Properties of Mortar
2015年第12期
全再生细骨料;传统再生细骨料;砂浆;性能
All recycled fine aggregates; Traditional recycled fine aggregates; Mortar; Performance
2015年第12期
1000-4637(2015)12-94-05
广东省公益研究与能力建设项目(2014B020216001)
杨医博1,2,雷灏轩1,郭文瑛1,郑志勤1,王恒昌1,郑子麟1,林仙杰1,欧阳雄新1, 黄锦炫1,潘洲池1,黄玉清1
1.华南理工大学土木与交通学院,广州 510640;2.华南理工大学亚热带建筑科学 国家重点实验室,广州 510640

杨医博1,2,雷灏轩1,郭文瑛1,郑志勤1,王恒昌1,郑子麟1,林仙杰1,欧阳雄新1, 黄锦炫1,潘洲池1,黄玉清1

浏览量:
1000
摘 要:传统再生细骨料需水量大、强度低,较难利用,将废弃混凝土全部破碎成细骨料的全再生细骨料技术能有效提高再生细骨料性能。在前期研究基础上,进行了全再生细骨料对砂浆性能影响的研究。结果表明,在同样砂浆稠度的情况下,全再生细骨料砂浆的综合性能优于传统再生细骨料砂浆,与机制砂砂浆和河砂砂浆相近,可全取代机制砂或河砂用于制备砂浆;全再生细骨料具有较好的保水性能,用其配制砂浆时可较河砂和机制砂适当降低保水剂用量。 Abstract: The tranditional recycled fine aggregates has large water demand, low strength, and difficult to use, all recycled fine aggregate technology that is brocken waste concrete into fine aggregatecan, improve the performance of recycled fine aggregate. Based on the previous research, the influence of all recycled fine aggregate on mortar performance is studied. The results show that under the condition of the same mortar consistency, the comprehensive performance of the all recycled fine aggregate mortar is superior to the traditional recycled fine aggregate mortar, which is similar with manufactured-sand mortar and river sand mortar, all recycled fine aggregate mortar can fully replace the manufactured-sand mortar or river sand to prepare mortar. The all recycled fine aggregate has good water retention performance, the dosage of aquasorb can be appropriatly decreased for preparing mortar by using all recycled fine aggregate, compared with river sand and manufatured sand.
英文名 : Experimental Study on Influence of All Recycled Fine Aggregate on Properties of Mortar
刊期 : 2015年第12期
关键词 : 全再生细骨料;传统再生细骨料;砂浆;性能
Key words : All recycled fine aggregates; Traditional recycled fine aggregates; Mortar; Performance
刊期 : 2015年第12期
DOI :
文章编号 : 1000-4637(2015)12-94-05
基金项目 : 广东省公益研究与能力建设项目(2014B020216001)
作者 : 杨医博1,2,雷灏轩1,郭文瑛1,郑志勤1,王恒昌1,郑子麟1,林仙杰1,欧阳雄新1, 黄锦炫1,潘洲池1,黄玉清1
单位 : 1.华南理工大学土木与交通学院,广州 510640;2.华南理工大学亚热带建筑科学 国家重点实验室,广州 510640

杨医博1,2,雷灏轩1,郭文瑛1,郑志勤1,王恒昌1,郑子麟1,林仙杰1,欧阳雄新1, 黄锦炫1,潘洲池1,黄玉清1

摘要
参数
结论
参考文献
引用本文

摘   要:传统再生细骨料需水量大、强度低,较难利用,将废弃混凝土全部破碎成细骨料的全再生细骨料技术能有效提高再生细骨料性能。在前期研究基础上,进行了全再生细骨料对砂浆性能影响的研究。结果表明,在同样砂浆稠度的情况下,全再生细骨料砂浆的综合性能优于传统再生细骨料砂浆,与机制砂砂浆和河砂砂浆相近,可全取代机制砂或河砂用于制备砂浆;全再生细骨料具有较好的保水性能,用其配制砂浆时可较河砂和机制砂适当降低保水剂用量。Abstract: The tranditional recycled fine aggregates has large water demand, low strength, and difficult to use, all recycled fine aggregate technology that is brocken waste concrete into fine aggregatecan, improve the performance of recycled fine aggregate. Based on the previous research, the influence of all recycled fine aggregate on mortar performance is studied. The results show that under the condition of the same mortar consistency, the comprehensive performance of the all recycled fine aggregate mortar is superior to the traditional recycled fine aggregate mortar, which is similar with manufactured-sand mortar and river sand mortar, all recycled fine aggregate mortar can fully replace the manufactured-sand mortar or river sand to prepare mortar. The all recycled fine aggregate has good water retention performance, the dosage of aquasorb can be appropriatly decreased for preparing mortar by using all recycled fine aggregate, compared with river sand and manufatured sand.

关键词:
全再生细骨料;传统再生细骨料;砂浆;性能
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加
(1)全再生细骨料在砂浆中应用时,采用常规搅拌机制即可满足使用要求。
(2)与传统再生细骨料砂浆相比,全再生细骨料砂浆的保水率高、黏结强度高、干燥收缩小,其综合性能优于传统再生细骨料。
(3)与机制砂砂浆相比,全再生细骨料砂浆的胶凝材料用量少、抗压强度高、黏结强度高、干燥收缩较大,其综合性能与机制砂相近,可全取代机制砂用于制备砂浆。
(4)与河砂砂浆相比,全再生细骨料砂浆的保水率高、抗压强度高、干燥收缩小或相近、黏结强度较低,其综合性能与河砂相近,可全取代河砂用于制备砂浆。
(5)全再生细骨料具有一定保水性能,用其配制砂浆时可较河砂和机制砂适当降低保水剂用量。
[1] 肖建庄.再生混凝土[M].北京:建筑工业出版社,2008.
[2] 陈家珑.我国建筑垃圾资源化利用现状与建议[J].建设科技,2014(1):9-12.
[3] 胡坤.广州推出建筑废弃物循环利用新方案[EB/OL]. [2013-06-24]. 
[4] 李秋义,全洪株,秦原.再生混凝土性能与应用技术[M].北京:中国建材工业出版社,2010.
[5] Monalisa Behera,S.K.Bhattacharyya, A.K.Minocha,et al. Recycled aggregate from C&D waste & its use in concrete-A breakthrough towards sustainability in construction sector:A review[J].Construction and Building Materials,2014,68:501-516.
[6] 孙家瑛,耿健.再生细骨料粒径及掺量对混凝土抗冻性能的影响 [J].建筑材料学报,2012,15(3):382-385.
[7] 李秋义,李云霞,朱崇绩.颗粒整形对再生细骨料性能的影响[J].新型建筑材料,2006(1):17-19.
[8] 杨医博,梁松,莫海鸿,等.建筑废弃物的处理及再生利用方法:中国,200710028107.7[P].2007-05-02.
[9] 郑子麟.全再生细骨料的制备及其在砂浆和混凝土中的应用研究[D].广州:华南理工大学土木与交通学院,2014.
[10] 中华人民共和国国家质量监督检验检疫总局,中国国家标准化管理委员会. GB/T 25176—2010 混凝土和砂浆用再生细骨料[S].北京:中国标准出版社,2011.
[11] 中华人民共和国住房和城乡建设部. JGJ/T 70—2009 建筑砂浆基本性能试验方法标准[S].北京:中国建筑工业出版社,2009.
[12] 巩晓健,杨医博,朱磊,等.预拌砂浆拉伸粘结强度检测新方法的试验研究[J].混凝土,2012(1):100-103.
[13] 陈宗平,王妮,郑述芳,等.再生细骨料水泥砂浆的力学性能研究[J].混凝土,2011(8):115-120.
[14] 袁帅.砖、混凝土再生细骨料砂浆力学性能及应用研究[D].长沙:长沙理工大学,2013.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州