普通硅酸盐水泥与快硬硫铝酸盐水泥复配砂浆性能研究
Performance Research on Mortar with Ordinary Portland Cement Mixed with Rapid Hardening Sulphoaluminate Cement
2014年第3期
收缩;膨胀剂;复配;强度
Shrinkage; Expensive agent; Compounding; Strength
2014年第3期
1000-4637(2014)03-10-04
聂光临,孙诗兵,姚晓丹,田英良
北京工业大学材料科学与工程学院,100124

聂光临,孙诗兵,姚晓丹,田英良

浏览量:
1000
摘 要:针对外墙保温材料用粘结砂浆收缩较大的缺点,本文采用普通硅酸盐水泥与快硬硫铝酸盐水泥复配以降低砂浆的收缩率。试验结果显示,不论有无UEA膨胀剂的加入,PO-SAC复配可以显著降低砂浆的收缩率,但同时砂浆试样的抗压、抗折强度也会降低,且快硬硫铝酸盐水泥占比在30%时,砂浆试样的强度最低。此外,PO-SAC复配砂浆的凝结时间也较短,该种砂浆要应用于实际工程,仍需要后期试验研究。 Abstract: Because of the large shrinkage of the mortar used for external thermal insulating materials, in order to reduce the shrinkage, the ordinary Portland cement and rapid hardening sulphoaluminate cement is used to make mortar in this paper. The experimental results show that whether added the UEA expensive agent, or without the expensive agent, compounding of ordinary Portland cement and rapid hardening sulphoaluminate cement could significantly reduce the shrinkage of mortar, but the compressive strength and flexural strength of the mortar specimen reduce at the same time, and when the rapid hardening sulphoaluminate cement accounted for 30%, the strength of the specimen is the lowest. Moreover, the setting time of the PO-SAC system is very short, so the research is needed to continue whether this kind of mortar is suitable to engineering application.
英文名 : Performance Research on Mortar with Ordinary Portland Cement Mixed with Rapid Hardening Sulphoaluminate Cement
刊期 : 2014年第3期
关键词 : 收缩;膨胀剂;复配;强度
Key words : Shrinkage; Expensive agent; Compounding; Strength
刊期 : 2014年第3期
DOI :
文章编号 : 1000-4637(2014)03-10-04
基金项目 :
作者 : 聂光临,孙诗兵,姚晓丹,田英良
单位 : 北京工业大学材料科学与工程学院,100124

聂光临,孙诗兵,姚晓丹,田英良

摘要
参数
结论
参考文献
引用本文

摘   要:针对外墙保温材料用粘结砂浆收缩较大的缺点,本文采用普通硅酸盐水泥与快硬硫铝酸盐水泥复配以降低砂浆的收缩率。试验结果显示,不论有无UEA膨胀剂的加入,PO-SAC复配可以显著降低砂浆的收缩率,但同时砂浆试样的抗压、抗折强度也会降低,且快硬硫铝酸盐水泥占比在30%时,砂浆试样的强度最低。此外,PO-SAC复配砂浆的凝结时间也较短,该种砂浆要应用于实际工程,仍需要后期试验研究。

Abstract: Because of the large shrinkage of the mortar used for external thermal insulating materials, in order to reduce the shrinkage, the ordinary Portland cement and rapid hardening sulphoaluminate cement is used to make mortar in this paper. The experimental results show that whether added the UEA expensive agent, or without the expensive agent, compounding of ordinary Portland cement and rapid hardening sulphoaluminate cement could significantly reduce the shrinkage of mortar, but the compressive strength and flexural strength of the mortar specimen reduce at the same time, and when the rapid hardening sulphoaluminate cement accounted for 30%, the strength of the specimen is the lowest. Moreover, the setting time of the PO-SAC system is very short, so the research is needed to continue whether this kind of mortar is suitable to engineering application.

关键词:
收缩;膨胀剂;复配;强度
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加
(1)不论有无膨胀剂的加入,普通硅酸盐水泥与快硬硫铝酸盐水泥复配都可以大幅降低砂浆试样的收缩率,且快硬硫铝酸盐水泥占比在30%~100%的砂浆试样的收缩率相近。但PO-SAC复配砂浆的强度低于任一单组份砂浆,快硬硫铝酸盐水泥占比在30%时,试样的强度最低。
(2)UEA膨胀剂的掺加可以降低砂浆试样的收缩率,但降低幅度不大,且砂浆试样的抗压、抗拉强度也会降低。从砂浆的成本考虑,可以采用快硬硫铝酸盐水泥替代UEA膨胀剂,以获得一种低收缩砂浆。
(3)PO-SAC复配砂浆的凝结时间较短,工程应用时需要加入合适的缓凝剂;此外,PO-SAC复配砂浆的强度较低,工程应用时必须采取一定的增强手段,如增加胶粉的掺加量,纤维增强等。因此,要使该砂浆应用于实际工程,仍需要后期继续研究。
[1] 涂逢祥, 王庆一. 我国建筑节能现状及发展[J]. 保温材料与建筑节能, 2004(43): 9-11.
[2] 李华忠, 匡立涛. 外墙外保温技术的应用现状及发展[J]. 建筑与结构设计, 2008(10): 42-45.
[3] 张新庆, 吴小翔, 王古营, 等.  A级防火等级外墙外保温系统推荐[J]. 建筑节能, 2011(9): 57-59.
[4] 杨林, 严云. 硫铝酸盐水泥与硅酸盐水泥复配性能研究[J]. 水泥, 2012(7): 7-10.
[5] 王复生, 杨海艳. 硫铝酸盐水泥与硅酸盐水泥混合对复合水泥性能的影响[J]. 北京建材, 1996(2): 17-21.
[6] 李德栋. 影响硫铝酸盐水泥凝结时间的因素[J]. 新世纪水泥导报, 2002(4): 36-37.
[7] 牟善彬, 苏小萍. 硫铝酸盐水泥熟料快凝探因[J]. 新世纪水泥导报, 2000(1): 17-18 .
[8] 张丕兴. 硫铝酸盐同硅酸盐复合水泥的研究[J]. 水泥, 1989(12): 2-6.
[9] 陈娟, 李北星. 硅酸盐-硫铝酸盐水泥混合体系的试验研究[J]. 重庆建筑大学学报, 2007(4): 121-124.
[10] 王红. 硅酸盐水泥熟料对硫铝酸盐水泥某些性能影响的研究[J]. 武汉建材学院学报, 1984(1): 47-65.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州