基于粉料粒径变化的超硫酸盐水泥力学性能研究
Mechanical Properties Study on Super Sulphate Cement (SSC) Based on Powder Particle Diameter Change
2014年第3期
超硫酸盐水泥;粉料粒径;力学性能;激光粒度分析;比表面积
Super sulphated cement; Powder particle diameter; Mechanical property; Laser particle size analysis; Surface area
2014年第3期
1000-4637(2014)03-14-05
高育欣,王 军,向佳瑜,余保英
中建商品混凝土有限公司,武汉 430070

高育欣,王 军,向佳瑜,余保英

浏览量:
1000
摘  要:研究了超硫酸盐水泥(简称SSC)胶凝材料体系中矿粉、石膏和水泥熟料的粒径变化对其力学性能的影响,借助激光粒度分析仪和扫描电子显微镜分别分析粉料粒度分布和SSC试件的微观形貌,得出从粉料粒径角度提高SSC力学强度的相关方法。研究表明,矿粉粒径对力学强度影响最为明显,随着矿粉粒径变小,力学强度呈现增大的变化趋势。矿粉比表面积为545m2/kg的试件相对于比表面积为227m2/kg的试件28d抗压强度增加31.8%;石膏粉磨至比表面积为350~450m2/kg比较适宜,不磨或粉磨时间过长对力学强度均有不利影响;水泥熟料粒径对力学强度影响相对较小,粉磨至比表面积高于350m2/kg就可以满足SSC的配制强度要求。Abstract:Effectofslag,gypsumandcementclinkerparticlediametersonthemechanicalpropertyofsupersulphatedcement(SSC)arestudied.InordertoobtainedsomerelevantmethodsofimprovingSSCmechanicalstrength,thepowderparticlesizedistributionandmicrostructureofSSCspecimensareanalyzedbylaserparticlesizeanalyzerandscanningelectronmicroscope(SEM).TheresultsshowthatthemostremarkablefactorofpowdertoinfluenceSSCmechanicalstrengthisslagparticlediameter,thereexistsoppositechangetrendbetweenthem.Thespecimens28dayscompressivestrengthwithslagsurfacearea545m2/kgincreased31.8%tothesurfacearea227m2/kg.Thegypsumsurfacearearangefrom350m2/kgto450m2/kgisfavorable,nogrindortoomuchbothhaveadverseeffectonmechanicalstrength.Cementclinkerparticlediameterhasarelativelyslighteffectonthemechanicalstrength,grindingsurfaceareato350m2/kgcanmeettherequirementsofSSCmechanicalstrength.
英文名 : Mechanical Properties Study on Super Sulphate Cement (SSC) Based on Powder Particle Diameter Change
刊期 : 2014年第3期
关键词 : 超硫酸盐水泥;粉料粒径;力学性能;激光粒度分析;比表面积
Key words : Super sulphated cement; Powder particle diameter; Mechanical property; Laser particle size analysis; Surface area
刊期 : 2014年第3期
DOI :
文章编号 : 1000-4637(2014)03-14-05
基金项目 :
作者 : 高育欣,王 军,向佳瑜,余保英
单位 : 中建商品混凝土有限公司,武汉 430070

高育欣,王 军,向佳瑜,余保英

摘要
参数
结论
参考文献
引用本文

摘   要:研究了超硫酸盐水泥(简称SSC)胶凝材料体系中矿粉、石膏和水泥熟料的粒径变化对其力学性能的影响,借助激光粒度分析仪和扫描电子显微镜分别分析粉料粒度分布和SSC试件的微观形貌,得出从粉料粒径角度提高SSC力学强度的相关方法。研究表明,矿粉粒径对力学强度影响最为明显,随着矿粉粒径变小,力学强度呈现增大的变化趋势。矿粉比表面积为545m2/kg的试件相对于比表面积为227m2/kg的试件28d抗压强度增加31.8%;石膏粉磨至比表面积为350~450m2/kg比较适宜,不磨或粉磨时间过长对力学强度均有不利影响;水泥熟料粒径对力学强度影响相对较小,粉磨至比表面积高于350m2/kg就可以满足SSC的配制强度要求。

Abstract:Effect of slag, gypsum and cement clinker particle diameters on the mechanical property of super sulphated cement (SSC) are studied. In order to obtained some relevant methods of improving SSC mechanical strength, the powder particle size distribution and microstructure of SSC specimens are analyzed by laser particle size analyzer and scanning electron microscope (SEM). The results show that the most remarkable factor of powder to influence SSC mechanical strength is slag particle diameter, there exists opposite change trend between them. The specimens 28 days compressive strength with slag surface area 545m2/kg increased 31.8% to the surface area 227m2/kg. The gypsum surface area range from 350m2/kg to 450m2/kg is favorable, no grind or too much both have adverse effect on mechanical strength. Cement clinker particle diameter has a relatively slight effect on the mechanical strength, grinding surface area to 350m2/kg can meet the requirements of SSC mechanical strength.

关键词:
超硫酸盐水泥;粉料粒径;力学性能;激光粒度分析;比表面积
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加
(1)SSC胶凝材料体系中,矿粉粒径对力学强度影响最大。随着矿粉粉磨时间的增加,对应的试件力学强度依次增大。增加矿粉的粉磨时间,矿粉比表面积为545m2/kg时相对于比表面积为227m2/kg的试件,抗压强度增加31.8%,抗折强度增加36.0%,SEM微观形貌分析也证实矿粉比表面积大的体系结构更加密实。
(2)随着石膏粉磨时间的增加,对应的试件力学强度呈现出先增加后略微降低的趋势,粉磨时间不长的石膏G1或G2比表面积较大,分别为358m2/kg和416m2/kg,试样力学强度也较高。粉磨时间长的石膏在振动磨上存在“粘球”的现象,导致分散效果反而不好,因此控制粉磨时间对石膏作用的发挥很重要。
(3)水泥熟料粒径对SSC体系力学强度影响相对较小,粉磨至比表面积高于350m2/kg时已经可以满足SSC配制要求,过小和过大的颗粒对SSC体系力学强度都不利。
[1] Yu -Xin Gao, Bao-Ying Yu, Fen-Lian Xu. Effect of Modified Phosphogypsum on the Mechanical Properties of Super Sulphate Cement [J]. Applied Mechanics and Materials, 2012, 161: 264-268
[2] 李兰,石玉成. 激光粒度分析仪测量黄土粉体粒度的应用研究[J]. 甘肃科学学报, 2009, 21(4):46-50.
[3] 董军. 天然硬石膏活性激发及其水化硬化特性研究[D]. 重庆大学, 2008.
[4] Manjit Singh. Treating waste phosphogypsum for cement and plaster manufacture[J]. Cement and Concrete Research, 2002,(32): 1033-1038.
[5] 张亚梅, 秦鸿根, 孙伟. 再生混凝土配合比设计初探[J]. 混凝土与水泥制品, 2002(1): 7-9.
[6] 刘朝宗, 杨印生, 张魁元, 等. 水泥熟料粒径与强度关系的灰色分析[J]. 数理统计与管理, 1996, 15(5): 16-19.
[7] Yu-Xin Gao, Bao-Ying Yu, Fen-Lian Xu, Xi-hua Lin. Preparation of Calcined Phosphogypsum-based High-strength Supersulphated Cement [J]. Applied Mechanics and Materials, 2012(188): 199-204.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州