用于钢板剪力墙的C60混合砂混凝土试验研究
Experimental Research on C60 Mixed Sand Concrete for Steel Plate Shearing Wall
2014年第6期
钢板剪力墙;混合砂;自收缩
Steel plate shearing wall; Mixed sand; Autogenous shrinkage
2014年第6期
1000-4637(2014)06-17-04
陈 景1,林喜华2,王 斌2,刘其彬1
1.中建商品混凝土成都有限公司,610052;2.中建商品混凝土重庆有限公司,401336

陈 景1,林喜华2,王 斌2,刘其彬1

浏览量:
1000
摘 要:结合重庆瑞安超高层项目对C60钢板剪力墙混凝土性能的要求,通过采用重庆当地机制砂与天然河砂混合的方式,并对胶凝材料进行优选,制备出满足工程设计要求的C60钢板剪力墙混凝土。结果表明,机制砂与河砂比例为5∶5时,混凝土的各项性能良好且经济合理;胶凝材料体系采用水泥、粉煤灰与硅灰组合较合理;掺入6%HCSA膨胀剂可以有效抑制混凝土的自收缩。 Abstract: Based on the requirements of C60 concrete with steel plate shearing wall by Chongqing Rui An ultra high-rise project, the C60 concrete with steel plate shearing wall is successfully prepared by optimizing cementitious system and mixed sand. The mixed sand is composed of natural river sand and manufactured sand in Chongqing area. The results show that when the proportion of manufactured sand to river sand is 5∶5, the properties of concrete are better and economical. The optimized cementitious system is composed of cement, fly-ash and silica fume. The autogenous shrinkage of concrete could be restrained by adding 6% HCSA expansion agent.
英文名 : Experimental Research on C60 Mixed Sand Concrete for Steel Plate Shearing Wall
刊期 : 2014年第6期
关键词 : 钢板剪力墙;混合砂;自收缩
Key words : Steel plate shearing wall; Mixed sand; Autogenous shrinkage
刊期 : 2014年第6期
DOI :
文章编号 : 1000-4637(2014)06-17-04
基金项目 :
作者 : 陈 景1,林喜华2,王 斌2,刘其彬1
单位 : 1.中建商品混凝土成都有限公司,610052;2.中建商品混凝土重庆有限公司,401336

陈 景1,林喜华2,王 斌2,刘其彬1

摘要
参数
结论
参考文献
引用本文

摘   要:结合重庆瑞安超高层项目对C60钢板剪力墙混凝土性能的要求,通过采用重庆当地机制砂与天然河砂混合的方式,并对胶凝材料进行优选,制备出满足工程设计要求的C60钢板剪力墙混凝土。结果表明,机制砂与河砂比例为5∶5时,混凝土的各项性能良好且经济合理;胶凝材料体系采用水泥、粉煤灰与硅灰组合较合理;掺入6%HCSA膨胀剂可以有效抑制混凝土的自收缩。

Abstract: Based on the requirements of C60 concrete with steel plate shearing wall by Chongqing Rui An ultra high-rise project, the C60 concrete with steel plate shearing wall is successfully prepared by optimizing cementitious system and mixed sand. The mixed sand is composed of natural river sand and manufactured sand in Chongqing area. The results show that when the proportion of manufactured sand to river sand is 5∶5, the properties of concrete are better and economical. The optimized cementitious system is composed of cement, fly-ash and silica fume. The autogenous shrinkage of concrete could be restrained by adding 6% HCSA expansion agent.

关键词:
钢板剪力墙;混合砂;自收缩
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加
(1)当机制砂和河砂按照5∶5混合时,砂粗细颗粒分布均匀,级配效果较好;采用该比例的混合砂制备的C60钢板剪力墙混凝土综合性能良好。
(2)胶凝材料体系采用水泥、Ⅰ级粉煤灰与硅灰组合,制备的混凝土工作性能与抗压强度均满足工程设计要求,且胶凝材料种类较少,有利于混凝土的生产组织。
(3)在混凝土中掺入HCSA膨胀剂有利于抑制混凝土的自收缩,当HCSA掺量为6%时,60h内混凝土膨胀率较大,28d龄期的混凝土还略微有膨胀;掺入一定量的矿粉可以降低混凝土的早期自收缩,但28d龄期自收缩率较基准混凝土的大。
[1] 刘晓. 组合钢板剪力墙抗震性能研究[D]. 西安: 西安建筑科技大学, 2010.
[2] 李凤兰, 罗俊礼. 不同骨料高强混凝土自收缩试验研究[J]. 港工技术, 2009, 46(1): 35-37.
[3] 王稷良, 周明凯. 机制砂对高强混凝土体积稳定性的影响[J]. 武汉理工大学学报, 2007, 29(10): 20-24.
[4] 韦庆东. 人工砂石制备高性能混凝土研究[D]. 北京: 北京工业大学, 2007.
[5] 王稷良. 机制砂特性对混凝土性能的影响及机理研究[D]. 武汉: 武汉理工大学, 2008.
[6] 阎培渝, 陈志城. 含不同矿物掺合料的高强混凝土的自收缩特性[J]. 工业建筑, 2011, 41(6): 124-127.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州