矿渣-稻壳灰基碱激发胶凝材料的制备
Preparation for Slag-rice Husk Ash Cementing Materials Activated by Alkali Activator
2014年第10期
碱激发;矿渣;稻壳灰;强度;水化产物;微观结构
Alkali activated; Slag; Rice husk ash; Strength; Hydration production; Microstructure
2014年第10期
1000-4637(2014)10-12-04
詹 兰1,郭丽萍2,3,4
1.东南大学土木工程学院,南京211189;2.东南大学材料科学与工程学院,南京211189; 3.先进土木工程材料协同创新中心(东南大学),南京211189;4. 江苏省土木工程材料 重点实验室,南京211189

詹 兰1,郭丽萍2,3,4

浏览量:
1000
摘 要:以工农业废料矿渣、稻壳灰为主要原料,制成一种新型胶凝材料,并对此胶凝材料的强度进行探讨,就不同种类的碱激发剂等因素进行探究。同时,用X射线衍射分析不同龄期此体系碱激发胶凝材料的矿物组成,并用扫描电镜观察不同龄期材料的微观形貌。结果表明,稻壳灰的活化可采用“两段煅烧法”,碱组分含量为10%、激发剂为水玻璃时激发效果最好,胶凝材料水化产物为低钙硅比的 C-S-H 凝胶。 Abstract: A slag-rice husk ash cementing material is prepared by using slag and rice husk ash as raw materials and alkali as activator. The strength of the material, the different effects of different kinds of alkali activators, and the hydration products of the cementing material are studied. The mineral composition of the material at different ages is analyzed by X-ray diffraction. The microstructure of hydration products of this material at different ages are characterized by scanning electron microscope with X-ray energy dispersive technique. The results show that the activation of rice husk ash could be made from “calcination by steps”. The highest strength is made from the specimen which is used 10% (the Na2O mass ratio) sodium silicate. The hydration product is low calcium-silicate ratio C-S-H gel.
英文名 : Preparation for Slag-rice Husk Ash Cementing Materials Activated by Alkali Activator
刊期 : 2014年第10期
关键词 : 碱激发;矿渣;稻壳灰;强度;水化产物;微观结构
Key words : Alkali activated; Slag; Rice husk ash; Strength; Hydration production; Microstructure
刊期 : 2014年第10期
DOI :
文章编号 : 1000-4637(2014)10-12-04
基金项目 :
作者 : 詹 兰1,郭丽萍2,3,4
单位 : 1.东南大学土木工程学院,南京211189;2.东南大学材料科学与工程学院,南京211189; 3.先进土木工程材料协同创新中心(东南大学),南京211189;4. 江苏省土木工程材料 重点实验室,南京211189

詹 兰1,郭丽萍2,3,4

摘要
参数
结论
参考文献
引用本文

摘   要:以工农业废料矿渣、稻壳灰为主要原料,制成一种新型胶凝材料,并对此胶凝材料的强度进行探讨,就不同种类的碱激发剂等因素进行探究。同时,用X射线衍射分析不同龄期此体系碱激发胶凝材料的矿物组成,并用扫描电镜观察不同龄期材料的微观形貌。结果表明,稻壳灰的活化可采用“两段煅烧法”,碱组分含量为10%、激发剂为水玻璃时激发效果最好,胶凝材料水化产物为低钙硅比的 C-S-H 凝胶。

Abstract: A slag-rice husk ash cementing material is prepared by using slag and rice husk ash as raw materials and alkali as activator. The strength of the material, the different effects of different kinds of alkali activators, and the hydration products of the cementing material are studied. The mineral composition of the material at different ages is analyzed by X-ray diffraction. The microstructure of hydration products of this material at different ages are characterized by scanning electron microscope with X-ray energy dispersive technique. The results show that the activation of rice husk ash could be made from “calcination by steps”. The highest strength is made from the specimen which is used 10% (the Na2O mass ratio) sodium silicate. The hydration product is low calcium-silicate ratio C-S-H gel.

关键词:
碱激发;矿渣;稻壳灰;强度;水化产物;微观结构
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加
(1)碱激发剂的选择对于矿渣-稻壳灰基胶凝材料的强度有很大影响。在三种激发剂中,水玻璃的激发效果最好,用其激发的胶凝材料体系强度随着碱组分含量的增大而增大。使用其余两种激发剂的体系,随着碱组分含量的增加,强度有所波动。
(2)碱组分含量为5%、碱激发剂为水玻璃的胶凝材料脆性最小。
(3)稻壳灰中的方解石、石英等晶相不参加碱激发胶凝材料的水化反应,参加反应的主要是玻璃相。胶凝材料体系随着水化反应的进行,大部分颗粒被连接成整体,空隙数量和宽度逐渐减小。
  
[1] 杨南如. 碱胶凝材料形成的物理化学基础(Ⅰ)[J]. 硅酸盐学报, 1996,24(2): 209-215.
[2] 梁世庆,孙波成. 稻壳灰混凝土性能研究[J]. 混凝土,2009(2): 73-75.
[3] 郭夫超,潘钢华,刘丽娟.碱激发胶凝材料基稻壳粉复合材料制备技术研究[J]. 散装水泥,2006(6):66-67.
[4] 余其俊,赵三银, 冯庆革,等.高活性稻壳灰的制备及其对水泥性能的影响[J].武汉理工大学学报, 2003,25(1):15-33.
[5] Sugita S. Fundamental Study on the Effective Utilization of Rice Husk Ash as Concrete Materials[D]. Hokkaido:Hokkaido University, 1996.
 

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州