EVA对煤矸石泡沫混凝土性能的影响研究
Effecting Research of EVA on Properties of Coal Gangue Foamed Concrete
2013年第7期
泡沫混凝土;煤矸石;EVA;性能
Foamed concrete; Coal gangue; EVA; Properties
2013年第7期
1000-4637(2013)07-83-04
陕西省“13115”重大科技专项项目(2010ZDKG-58)、国家级大学生创新创业训练计划项目
揣 丹,刘开平,温久然,刘 宁,鲍俊敏,沈 凯
长安大学材料科学与工程学院,西安 710061

揣 丹,刘开平,温久然,刘 宁,鲍俊敏,沈 凯

浏览量:
1000
摘  要:以煤矸石为主要原料,用普通硅酸盐水泥作粘结剂,制备了煤矸石-水泥基泡沫混凝土,研究了EVA乳液对煤矸石泡沫混凝土力学性能、吸水率及导热性能的影响。结果表明,EVA乳液的掺入可有效降低煤矸石泡沫混凝土的密度和导热系数。随EVA的掺入量增加,煤矸石泡沫混凝土的抗压强度、抗折强度呈现先降低后增加的趋势,而吸水率则呈先上升后下降趋势。当EVA乳液掺量为7%时,煤矸石泡沫混凝土的抗压强度达到6.62MPa,抗折强度达到2.01MPa,且其干密度、吸水率和导热系数均优于普通泡沫混凝土。Abstract:Thecoalgangue-cementfoamedconcreteispreparedbytheuseofcoalgangueandordinaryPortlandcement.TheeffectsofEVAemulsiononthemechanicalproperties,waterabsorptionandthermal-insulatingpropertiesofthecoalgangue-cementfoamedconcretearestudied.TheresultsshowthattheadditionofEVAemulsioncaneffectivelyreducethedensityandthecoefficientofthermalconductivityofthecoalgangue-cementfoamedconcrete.WiththedosageincreaseofEVA,thecompressivestrengthsandtheflexuralstrengthsofthecoalgangue-cementfoamedconcretegetdownfirst,thengoup,whilethewaterabsorptionrateshowstheoppositetendency.WhentheEVAemulsioncontentis7%,thecompressivestrengthofthecoalgangue-cementfoamedconcretereachesto6.62MPa,theflexuralstrengthreachesto2.01MPa,thedensity,andthewaterabsorptionrateandthecoefficientofthermalconductivityareallbetterthantheordinaryfoamconcrete.
英文名 : Effecting Research of EVA on Properties of Coal Gangue Foamed Concrete
刊期 : 2013年第7期
关键词 : 泡沫混凝土;煤矸石;EVA;性能
Key words : Foamed concrete; Coal gangue; EVA; Properties
刊期 : 2013年第7期
DOI :
文章编号 : 1000-4637(2013)07-83-04
基金项目 : 陕西省“13115”重大科技专项项目(2010ZDKG-58)、国家级大学生创新创业训练计划项目
作者 : 揣 丹,刘开平,温久然,刘 宁,鲍俊敏,沈 凯
单位 : 长安大学材料科学与工程学院,西安 710061

揣 丹,刘开平,温久然,刘 宁,鲍俊敏,沈 凯

摘要
参数
结论
参考文献
引用本文

摘   要:以煤矸石为主要原料,用普通硅酸盐水泥作粘结剂,制备了煤矸石-水泥基泡沫混凝土,研究了EVA乳液对煤矸石泡沫混凝土力学性能、吸水率及导热性能的影响。结果表明,EVA乳液的掺入可有效降低煤矸石泡沫混凝土的密度和导热系数。随EVA的掺入量增加,煤矸石泡沫混凝土的抗压强度、抗折强度呈现先降低后增加的趋势,而吸水率则呈先上升后下降趋势。当EVA乳液掺量为7%时,煤矸石泡沫混凝土的抗压强度达到6.62MPa,抗折强度达到2.01MPa,且其干密度、吸水率和导热系数均优于普通泡沫混凝土。

Abstract: The coal gangue-cement foamed concrete is prepared by the use of coal gangue and ordinary Portland cement. The effects of EVA emulsion on the mechanical properties, water absorption and thermal-insulating properties of the coal gangue-cement foamed concrete are studied. The results show that the addition of EVA emulsion can effectively reduce the density and the coefficient of thermal conductivity of the coal gangue-cement foamed concrete. With the dosage increase of EVA, the compressive strengths and the flexural strengths of the coal gangue-cement foamed concrete get down first, then go up, while the water absorption rate shows the opposite tendency. When the EVA emulsion content is 7%, the compressive strength of the coal gangue-cement foamed concrete reaches to 6.62MPa, the flexural strength reaches to 2.01MPa, the density, and the water absorption rate and the coefficient of thermal conductivity are all better than the ordinary foam concrete.

关键词:
泡沫混凝土;煤矸石;EVA;性能
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加
(1)EVA乳液的掺入可有效降低煤矸石泡沫混凝土的密度和导热系数。当EVA掺量为6%时,较不加EVA试样的干密度降低5.5%,导热系数降低14%;当EVA掺量为7%时,较不加EVA试样干密度降低3.5%,导热系数降低13%。
(2)随EVA掺量的增加,煤矸石泡沫混凝土的抗压、抗折强度呈先降低后增加的趋势。当EVA掺量为7%时,煤矸石泡沫混凝土的28d抗折强度比不掺EVA时提高4%,抗压强度则提高35.7%。
(3)随EVA掺量的增加,煤矸石泡沫混凝土的吸水率呈先上升后下降趋势。当EVA掺量为7%时,试件的吸水率比不掺EVA时降低8.6%。
(4)掺7%EVA为最佳配比,此掺量时,煤矸石泡沫混凝土的抗压强度达到6.62MPa,抗折强度达到2.01MPa,且干密度、吸水率和导热系数均优于普通泡沫混凝土,可达到应用标准。
[1] 闫振甲,何艳君.泡沫混凝土实用生产技术[M].北京:化学工业出版社,2006.
[2] 向超,刘自力,牛飞.高分子聚合物泡沫混凝土制备防火保温材料的研究[J].scientific research,2011:946-949.
[3] 赵春新,张志强,段东方.聚合物改性水泥基泡沫混凝土的试验研究[J]. 新型墙材,2011(10):31-34.
[4] 管文.减水剂对泡沫混凝土性能的影响[J].新型建筑材料,2011(5):46-49.
[5]张磊蕾,王武祥.聚合物对泡沫混凝土孔结构和性能的影响研究[J].混凝土与水泥制品,2011(9):9-12.
[6] 俞心刚,李德军,田学春.煤矸石泡沫混凝土的研究[J].新型建筑材料,2008(1):16-19.
[7] 张海鸿,刘开平,和立新.活化煤矸石在水泥砂浆中的应用研究[J].非金属矿,2009(1):45-50.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州