聚丙烯酸高效减水剂的制备及其研究
Preparation and Research of Polyacrylic Superplasticizer
2013年第9期
聚丙烯酸减水剂;工艺优化;坍落度
Polyacrylic superplasticizer; Process optimization; Slump
2013年第9期
1000-4637(2013)09-17-05
熊 珂,左 跃
江西省建筑材料工业科学研究设计院,南昌 330001

熊 珂,左 跃

浏览量:
1000
摘 要:根据分子设计的原则,采用“滴加法”合成出一种带长侧链聚醚基团、羧酸基团的聚丙烯酸高效减水剂。通过正交试验和单因素优化,得到最佳工艺条件n(OXAC):n(AA) =0.046:0.175,H2O2的用量为单体总质量的1.2%,VC的用量为H2O2用量的26.9%,在60℃下反应5.0h。当聚丙烯酸高效减水剂的掺量为0.92%时,C40混凝土的初始坍落度为217mm,1h后塌落度为195 mm,含气量为3.5%,28d的强度高达65.4MPa。 Abstract: Based on the principle of molecular design, a polyacrylic superplasticizer is synthesized with long side-chain polyether group and carboxylic group by the method of “titration”. The best reactant ratio are n(OXAC):n(AA) =0.046:0.175 and m(H2O2)= 1.2% [m(OXAC) +m(AA)], m(VC)= 26.9%[m(H2O2)], and the optimal reaction conditions are 60℃ for 5.0h, which is obtained via orthogonal test and single factor optimized. The initial slump of C40 concrete containing the 0.92% superplasticizer is 217mm and remains 195mm after 1h. The air content of the concrete is 3.5%, and its strength reaches up to 65.4MPa at 28d.
英文名 : Preparation and Research of Polyacrylic Superplasticizer
刊期 : 2013年第9期
关键词 : 聚丙烯酸减水剂;工艺优化;坍落度
Key words : Polyacrylic superplasticizer; Process optimization; Slump
刊期 : 2013年第9期
DOI :
文章编号 : 1000-4637(2013)09-17-05
基金项目 :
作者 : 熊 珂,左 跃
单位 : 江西省建筑材料工业科学研究设计院,南昌 330001

熊 珂,左 跃

摘要
参数
结论
参考文献
引用本文

摘   要:根据分子设计的原则,采用“滴加法”合成出一种带长侧链聚醚基团、羧酸基团的聚丙烯酸高效减水剂。通过正交试验和单因素优化,得到最佳工艺条件n(OXAC):n(AA) =0.046:0.175,H2O2的用量为单体总质量的1.2%,VC的用量为H2O2用量的26.9%,在60℃下反应5.0h。当聚丙烯酸高效减水剂的掺量为0.92%时,C40混凝土的初始坍落度为217mm,1h后塌落度为195 mm,含气量为3.5%,28d的强度高达65.4MPa。

Abstract: Based on the principle of molecular design, a polyacrylic superplasticizer is synthesized with long side-chain polyether group and carboxylic group by the method of “titration”. The best reactant ratio are n(OXAC):n(AA) =0.046:0.175 and m(H2O2)= 1.2% [m(OXAC) +m(AA)], m(VC)= 26.9%[m(H2O2)], and the optimal reaction conditions are 60℃ for 5.0h, which is obtained via orthogonal test and single factor optimized. The initial slump of C40 concrete containing the 0.92% superplasticizer is 217mm and remains 195mm after 1h. The air content of the concrete is 3.5%, and its strength reaches up to 65.4MPa at 28d.

关键词:
聚丙烯酸减水剂;工艺优化;坍落度
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加
(1)以国内易得且价格便宜的异丁烯醇代替主要靠国外进口且价格昂贵的异丙烯醇为合成亲水长侧链的单体原料。
(2)通过正交试验和单因素优化试验得到聚丙烯酸高效减水剂的最佳工艺为n(OXAC):n(AA)=0.046:0.175,H2O2的用量为单体总质量的1.2%,VC的用量为H2O2用量的26.9%,在60℃下反应5.0h。各单体对混凝土坍落度的影响大小次序依次为H2O2>AA>OXAC。
(3)当聚丙烯酸高效减水剂的掺量为0.92%时,C40混凝土的初始坍落度为217mm,1h后坍落度为195mm,含气量为3.5%,28d的强度高达65.4MPa,性能略优于奥克公司生产的OXAB和格雷公司生产的ADVA两种减水剂。
[1] F. Puertas, H. Santos, M. Palacios, et al. Polycarboxylate superplasticiser admixtures:effect on hydration, microstructure and rheological behaviour in cement pastes[J]. Adv. Cem. Res, 2005, 17(2):77-89.
[2] J. Plank, B. Sachsenhauser. Experimental determination of the effective anionic charge density of polycarboxylate superplasticizers in cement pore solution[J]. Cem. Concr. Res, 2009(39): 1-5.
[3] G. Ferrari, T. Cerulli, P. Clemente, et al. Influence of Carboxylic Acid Carboxylic Ester Ratio of Carboxylic Acid Ester Superplasticizer on Characteristics of Cement Mixtures[C] 6thCANMET/ACI International Conference Superplasticizers and Other ChemicalAdmixtures in Concrete. New Orleans: Am. Concr. Int, 2000: 505-52.
[4] Wang Ziming. Synthesis Performance and ApplicaTion of Polycarboxylate Type High Performance Superplasticizers[M]. Beijing: China Architecture & Building Press, 2009(6):15-60.
[5] Arzu Büyükyac, Gzde Tuzcu, Leyla Aras. Synthesis of copolymers of methoxy polyethylene glycol acrylate and 2-acrylamido-2-methyl-1-propanesulfonic acid: Its characterization and application as superplasticizer in concrete[J]. Cem. Concr. Res.2009(39): 629-635.
[6] R. Qianping, P. Somasundaran, M. Changwen, et al. Effect of the length of the side chains of comb-like copolymer dispersants on dispersion and rheological properties of concentrated cement suspensions[J]. J. Colloid Interface. Sci. 2009(336): 624-633.
[7] Winnefeld F, Becker S, Pakusch J,et al. Effects of the Molecular Architecture of Comb-Shaped Superplasticizers on Their Performance in Cementitious Systems[J].Cem.Concr .Compos.2007(29): 251-262.
[8] J.Plank, B.Sachsenhauser, J.de Reese. Experimental determination of the thermodynamic parameters affecting the adsorption behaviour and dispersion effectiveness of PCE superplasticizers[J]. Cem. Concr. Res, 2010(40): 699-709.
[9] 赵振河. 高分子化学和物理[M]. 北京: 中国纺织出版社, 2003.
[10] 杨万泰. 聚合物材料表征与测试[M]. 北京: 中国轻工业出版社, 2008.
[11] Jolicoeur C. Chemical admixture-interactions: phenomenology and physic-chemical concepts [J]. Cement and Concrete Research, 1998, 20(2/3): 87-101.
[12] Uchikawa H. The role of steric repulsive force in the dispersion of cement particles in fresh paste prepared with organic admixture[J]. Cement and Concrete Research, 1997, 27(1): 37-50.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州