聚丙烯纤维直径对高温后高强混凝土的影响
Effects of Polypropylene Fiber Diameter on High Strength Concrete after High Temperature
2013年第9期
聚丙烯纤维直径;高强混凝土;高温;相对残余抗压强度;相对渗透能力
Polypropylene fiber diameter; High strength concrete; High temperature; Relative residual compressive strength; Relative permeab
2013年第9期
1000-4637(2013)09-48-03
国家自然科学基金项目(51278325);山西省自然科学基金项目(2011011024-2)
葛韦华,杜红秀,阎蕊珍
太原理工大学建筑与土木工程学院,030024

葛韦华,杜红秀,阎蕊珍

浏览量:
1000
摘  要:为研究高温前后聚丙烯纤维直径对高强混凝土的相对残余抗压强度及相对渗透能力的影响,在C60混凝土中分别掺入直径为25μm和35μm的聚丙烯纤维,进行了抗压性能及抗渗性能试验。试验结果表明,600℃以下,掺聚丙烯纤维的高强混凝土相对残余抗压强度略高于素混凝土;600℃以上,结果相反。同条件下,直径为25μm的聚丙烯纤维的贡献略优于直径为35μm的聚丙烯纤维。快速氯离子迁移系数法说明,与素混凝土相比,掺入聚丙烯纤维使得高强混凝土高温(100~700℃)作用后的抗渗性提高,其中,掺入直径为25μm的聚丙烯纤维高强混凝土的相对渗透能力低于掺入直径为35μm的聚丙烯纤维高强混凝土。Abstract:C60concretewasaddedwith?覫25μmand?覫35μmpolypropylenefibersandthecompressivebehaviorandpermeabilityresistanceoftheconcretewastestedtostudytheeffectofpolypropylenefiberdiameterontherelativeresidualcompressivestrengthandpermeabilityofhighstrengthconcrete(HSC)beforeandafterhightemperature.TheresultsshowthattherelativeresidualcompressivestrengthofHSCwithpolypropylenefibersisslightlyhigherthanthatoftheplainconcretebelow600℃,whiletheresultisoppositeover600℃.Underthesameconditions,thecontributionof25μmpolypropylenefiberisalittlebiggerthanthatof35μmpolypropylenefibertotherelativeresidualcompressivestrengthofHSC.Comparedwithplainconcrete,polypropylenefiberscanincreasethepermeabilityresistanceofHSCwhenexposedtoahightemperature(100~700℃),inwhichtherelativepermeabilityofHSCwith25μmpolypropylenefibersislowerthanthatofHSCwith35μmaccordingtotheresultsofrapidchlorideionmigrationcoefficientmethod.
英文名 : Effects of Polypropylene Fiber Diameter on High Strength Concrete after High Temperature
刊期 : 2013年第9期
关键词 : 聚丙烯纤维直径;高强混凝土;高温;相对残余抗压强度;相对渗透能力
Key words : Polypropylene fiber diameter; High strength concrete; High temperature; Relative residual compressive strength; Relative permeab
刊期 : 2013年第9期
DOI :
文章编号 : 1000-4637(2013)09-48-03
基金项目 : 国家自然科学基金项目(51278325);山西省自然科学基金项目(2011011024-2)
作者 : 葛韦华,杜红秀,阎蕊珍
单位 : 太原理工大学建筑与土木工程学院,030024

葛韦华,杜红秀,阎蕊珍

摘要
参数
结论
参考文献
引用本文

摘   要:为研究高温前后聚丙烯纤维直径对高强混凝土的相对残余抗压强度及相对渗透能力的影响,在C60混凝土中分别掺入直径为25μm和35μm的聚丙烯纤维,进行了抗压性能及抗渗性能试验。试验结果表明,600℃以下,掺聚丙烯纤维的高强混凝土相对残余抗压强度略高于素混凝土;600℃以上,结果相反。同条件下,直径为25μm的聚丙烯纤维的贡献略优于直径为35μm的聚丙烯纤维。快速氯离子迁移系数法说明,与素混凝土相比,掺入聚丙烯纤维使得高强混凝土高温(100~700℃)作用后的抗渗性提高,其中,掺入直径为25μm的聚丙烯纤维高强混凝土的相对渗透能力低于掺入直径为35μm的聚丙烯纤维高强混凝土。

Abstract: C60 concrete was added with ?覫25μm and ?覫35μm polypropylene fibers and the compressive behavior and permeability resistance of the concrete was tested to study the effect of polypropylene fiber diameter on the relative residual compressive strength and permeability of high strength concrete (HSC) before and after high temperature. The results show that the relative residual compressive strength of HSC with polypropylene fibers is slightly higher than that of the plain concrete below 600℃, while the result is opposite over 600℃. Under the same conditions, the contribution of 25μm polypropylene fiber is a little bigger than that of 35μm polypropylene fiber to the relative residual compressive strength of HSC. Compared with plain concrete, polypropylene fibers can increase the permeability resistance of HSC when exposed to a high temperature (100~700℃), in which the relative permeability of HSC with 25μm polypropylene fibers is lower than that of HSC with 35μm according to the results of rapid chloride ion migration coefficient method.

关键词:
聚丙烯纤维直径;高强混凝土;高温;相对残余抗压强度;相对渗透能力
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加
(1)随着温度的升高,HSC相对残余抗压强度降低,600℃之前,D系列的相对残余抗压强度优于M,600~800℃出现逆差。
(2)高温后,掺入直径为25μm聚丙烯纤维的HSC抗压强度与抗渗性能优于掺入直径为35μm的HSC。
(3)500~600℃之间为HSC性能变化的关键温度区间。
(4)常温~700℃之间,HSC的抗渗性不断提高,D系列的相对渗透能力小于M,D25小于D35。
(5)掺入1.8kg/m3、长8mm、直径25μm的聚丙烯纤维能有效抑制HSC的爆裂。
[1] Cheon-Goo Han,Min-Cheol Han,Young-Sun Heo.Improvement of residual compressive strength and spalling resistance of  hish-strength RC columns subjected to fire[J].Construction and Building Materials,2009,23(1):107-116.
[2] Pierre Kalifa,Gregoire Chene,Christophe Galle.High-temperature behaviour of HPC with polypropylene fibres From spalling to microstructure[J].Cement and Concrete Research,2001,31:1487-1499.
[3] 赵军,高丹盈.高温后聚丙烯纤维高强混凝土力学性能试验研究[J] .四川建筑科学研究,2008,34(1):133-135.
[4] 肖建庄,王平.掺聚丙烯纤维高性能混凝土高温后的抗压性能[J] .建筑材料学报,2004,7(3):281-285.
[5] 罗百福,郑文忠,李海艳.高温下掺PPF的RPC立方体抗压性能[J] .哈尔滨工业大学学报,2012,44(12):1-7. 
[6] 鞠丽艳,张雄.聚丙烯纤维对高温下混凝土性能的影响[J] .同济大学学报,2003,31(9):1064-1067.
[7] 杜红秀,张宁,王慧芳,阎蕊珍.聚丙烯纤维对高强混凝土高温后残余抗压强度的影响[J] .太原理工大学学报,2012,43(2):207-211.
[8] 库马·梅塔,保罗 J·M·蒙特罗.混凝土:微观结构、性能和材料[M].北京:中国电力出版社,2008:83.
[9] 柳献,袁勇,叶光,等.高性能混凝土高温爆裂的机理探讨[J].土木工程学报,2008,41(6):61-68.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州