碱渣混凝土耐磨性能试验研究
Experimental Research on Abrasion Resistance of Alkaline Residue Concrete
2013年第9期
碱渣;混凝土;耐磨性
Alkaline residue; Concrete; Abrasion resistance
2013年第9期
1000-4637(2013)09-81-04
淮安市科技支撑计划项目(HAG2012018),淮安市“533英才工程”技术拔尖人才工程项目
张 渊1 ,刘 勋1,曹 军2,陈宝海1,董 云1,张 颖1,宗 荣1
1.淮阴工学院,223001;2.江苏井神盐业,淮阴 223200

张 渊1 ,刘 勋1,曹 军2,陈宝海1,董 云1,张 颖1,宗 荣1

浏览量:
1000
摘 要:对碱渣掺合料混凝土在不同条件下的耐磨性能进行了试验研究,结果表明,随着碱渣掺量的增加,碱渣混凝土的耐磨性呈现先增强后减弱的规律,当碱渣占胶凝材料10%时,混凝土耐磨性能最优。结合SEM图像分析,碱渣占胶凝材料10%时,混凝土的微观结构变得更为密实;继续增加碱渣的掺量,碱渣的耐磨性呈现大幅减弱。试验还对不同养护龄期的碱渣掺合料混凝土进行了研究,发现混凝土的耐磨性随养护龄期增长呈现增强趋势。 Abstract: The abrasion resistance of the alkaline residue concrete under different conditions are tested and studied. The results show that the abrasion resistance of the alkaline residue concrete increase firstly and then decrease with the increasing of alkaline content. The abrasion resistance of the concrete is the best when the content of alkaline residue is 10% of cementation content. Combined with SEM, it’s found that the microstructure of the concrete is more dense when the cement replacement ratio of alkaline residue is 10%, and then, the abrasion resistance of the concrete sharply decrease with the increasing the content of alkaline residue. In addition, the abrasion resistance of the alkaline residue concrete under the different curing periods is tested, and the test results indicate that the abrasion resistance of the concrete increases with the increasing of curing ages.
英文名 : Experimental Research on Abrasion Resistance of Alkaline Residue Concrete
刊期 : 2013年第9期
关键词 : 碱渣;混凝土;耐磨性
Key words : Alkaline residue; Concrete; Abrasion resistance
刊期 : 2013年第9期
DOI :
文章编号 : 1000-4637(2013)09-81-04
基金项目 : 淮安市科技支撑计划项目(HAG2012018),淮安市“533英才工程”技术拔尖人才工程项目
作者 : 张 渊1 ,刘 勋1,曹 军2,陈宝海1,董 云1,张 颖1,宗 荣1
单位 : 1.淮阴工学院,223001;2.江苏井神盐业,淮阴 223200

张 渊1 ,刘 勋1,曹 军2,陈宝海1,董 云1,张 颖1,宗 荣1

摘要
参数
结论
参考文献
引用本文

摘   要:对碱渣掺合料混凝土在不同条件下的耐磨性能进行了试验研究,结果表明,随着碱渣掺量的增加,碱渣混凝土的耐磨性呈现先增强后减弱的规律,当碱渣占胶凝材料10%时,混凝土耐磨性能最优。结合SEM图像分析,碱渣占胶凝材料10%时,混凝土的微观结构变得更为密实;继续增加碱渣的掺量,碱渣的耐磨性呈现大幅减弱。试验还对不同养护龄期的碱渣掺合料混凝土进行了研究,发现混凝土的耐磨性随养护龄期增长呈现增强趋势。

Abstract: The abrasion resistance of the alkaline residue concrete under different conditions are tested and studied. The results show that the abrasion resistance of the alkaline residue concrete increase firstly and then decrease with the increasing of alkaline content. The abrasion resistance of the concrete is the best when the content of alkaline residue is 10% of cementation content. Combined with SEM, it’s found that the microstructure of the concrete is more dense when the cement replacement ratio of alkaline residue is 10%, and then, the abrasion resistance of the concrete sharply decrease with the increasing the content of alkaline residue. In addition, the abrasion resistance of the alkaline residue concrete under the different curing periods is tested, and the test results indicate that the abrasion resistance of the concrete increases with the increasing of curing ages. 

关键词:
碱渣;混凝土;耐磨性
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加
(1)随着碱渣占混凝土胶凝材料比例的增加,混凝土的耐磨性能先增加后逐步减小,当碱渣掺量占胶凝材料总量的10%时,混凝土的耐磨性最好,随着碱渣掺量的继续增加,混凝土的耐磨性明显降低。
(2)随着养护龄期的增加,碱渣混凝土的耐磨性呈现逐渐增强趋势,但变化幅度越来越小并逐步趋向一个稳定值。
(3)对碱渣混凝土进行烘干处理和自然条件,不同碱渣掺合料比例混凝土耐磨性的提高有一定影响,但对不同养护龄期的碱渣混凝土的耐磨性能影响不大。
[1] 彭松枭,尹健,王德辉. 矿物掺合料对再生混凝土耐磨性能的影响研究[J]. 混凝土,2009(3):56-59.
[2] 曾阳春,郑克仁,李益进.矿物掺合料对道路混凝土耐磨性的影响及机理[J].铁道科学与工程学报,2007,4(2):59-62.
[3] Ukiata K. Shigematsu S. Improvements in the properties of concrete utilizing classified fly ash[C]. Proceedings of the CANMET/ACI Third International Conference on the Use of fly ash. Silica Fume. Slag and Natural Pozzolans in Concrete, Trondheim, N ORWAY, 1989:219-240.
[4] Ghafoori N. Diawara H. Abrasion resistance of fine aggregate replaced silica fume concrete[J]. ACI Materials Journal, 1999. 96(5):559-567.
[5] 杨久俊,谢武,张磊,等.粉煤灰-碱渣-水泥混合料砂浆的配制实验研究[J].硅酸盐通报,2010,29(5):167-170.
[6] 李宝佳,娄德利,张磊,等.碱渣-粉煤灰复合胶凝材料力学性能的研究[J].砖瓦综合利用,2009(10):35-37.
[7] 杨良佐,李永丹,张立红. 碱渣的综合治理与利用[J].环境保护科学,2008,34(2):70-73.
[8] 王珺,孔德晶. 在混凝土中掺入纯碱废渣生产建材制品的研究[J].化学工业与工程技术,2004,25(4):43-44.
[9] 中华人民共和国国家质量监督检验检疫总局,中国国家标准化管理委员会. GBT 12988—2009 无机地面材料耐磨性能试验方法[S].北京:中国标准出版社,2009.
 

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州