铸造废砂对混凝土强度的影响
Effects of Waste Foundry Sand on Strength of Concrete
2013年第12期
铸造废砂;废砂处理;抗压强度;流动性
Waste foundry sand; Treatment of waste sand; Compressive strength; Fluidity
2013年第12期
1000-4637(2013)12-73-03
谢一飞1,楼浙湘2,田 寅1
1. 苏州混凝土水泥制品研究院有限公司、江苏省高耐久混凝土工程技术研究中心,215004; 2. 湖南路桥建设集团公司,长沙410004

谢一飞1,楼浙湘2,田 寅1

浏览量:
1000
摘 要:使用未处理和处理后的铸造废砂取代天然砂制备混凝土,并对混凝土的性能作了对比分析。结果表明,与基准混凝土相比,用未处理的废砂取代天然砂时,随着取代率的提高,混凝土的流动性变差,抗压强度也随之降低;处理后的废砂与未处理废砂对混凝土性能的影响趋势一致,抗压强度有所提高,当仅取代天然砂中的细砂时,对混凝土的抗压强度几乎没影响。 Abstract: The green concretes are prepared by using untreated and treated waste foundry sand to partially substitute the natural sands, and the performances of the two kinds of concretes were compared and analyzed. The test results show that comparing with the reference concrete, the liquidity and compressive strength of the concrete with untreated waste foundry sand decrease with the creasing the content of the waste foundry sand; the effect tendency of treated waste foundry sand on the performances of concrete are consistent with those of untreated waste foundry sand, and the performances have a certain improvement. When using all the treated waste foundry sand to replace the fine sand in natural sand, it’s found that treated waste foundry sand has hardly effect on the compressive strength of the concrete.
英文名 : Effects of Waste Foundry Sand on Strength of Concrete
刊期 : 2013年第12期
关键词 : 铸造废砂;废砂处理;抗压强度;流动性
Key words : Waste foundry sand; Treatment of waste sand; Compressive strength; Fluidity
刊期 : 2013年第12期
DOI :
文章编号 : 1000-4637(2013)12-73-03
基金项目 :
作者 : 谢一飞1,楼浙湘2,田 寅1
单位 : 1. 苏州混凝土水泥制品研究院有限公司、江苏省高耐久混凝土工程技术研究中心,215004; 2. 湖南路桥建设集团公司,长沙410004

谢一飞1,楼浙湘2,田 寅1

摘要
参数
结论
参考文献
引用本文

摘   要:使用未处理和处理后的铸造废砂取代天然砂制备混凝土,并对混凝土的性能作了对比分析。结果表明,与基准混凝土相比,用未处理的废砂取代天然砂时,随着取代率的提高,混凝土的流动性变差,抗压强度也随之降低;处理后的废砂与未处理废砂对混凝土性能的影响趋势一致,抗压强度有所提高,当仅取代天然砂中的细砂时,对混凝土的抗压强度几乎没影响。

Abstract: The green concretes are prepared by using untreated and treated waste foundry sand to partially substitute the natural sands, and the performances of the two kinds of concretes were compared and analyzed. The test results show that comparing with the reference concrete, the liquidity and compressive strength of the concrete with untreated waste foundry sand decrease with the creasing the content of the waste foundry sand; the effect tendency of treated waste foundry sand on the performances of concrete are consistent with those of untreated waste foundry sand, and the performances have a certain improvement. When using all the treated waste foundry sand to replace the fine sand in natural sand, it’s found that treated waste foundry sand has hardly effect on the compressive strength of the concrete.

关键词:
铸造废砂;废砂处理;抗压强度;流动性
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加
(1)随着未处理废砂取代率的增大,新拌混凝土的流动性降低,立方体抗压强度有明显降低。当用废砂取代天然砂中小于0.6mm细砂时,混凝土的流动性和抗压强度变化较小。
(2)经过处理后的废砂部分取代天然砂虽然也会导致混凝土抗压强度降低,但较之未处理废砂混凝土有所改善。当只取代小于0.6mm的细砂时,对混凝土强度几乎没有影响。
(3)与未处理的废砂相比较,处理后的废砂使混凝土的抗压强度略有提升,但在处理过程中也增加了成本。因此,建议在实际生产应用中,需综合考虑原材料、产品性能、经济成本等因素,确定最佳方案。
 
[1] 牟艳秋,巴吾东,刘世森,等. 铸造废砂的再利用[J]. 铸造技术,2010,31(10):1358-1360.
[2] 刘日鑫. 铸造废砂的综合利用进展[J]. 中国资源综合利用,2008(10):26-28.
[3] 刘日鑫. 胶粉、废砂、水泥混凝土材料的研究[D]. 昆明:昆明理工大学,2007.
[4] 刘日鑫,孙可伟,林志伟,等. 铸造水玻璃废砂在混凝土中的应用[J]. 铸造,2006,55(11):1203-1205.
[5] 袁礼东.水玻璃旧砂干法再生研究[D]. 昆明:昆明理工大学,2007.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州