陶瓷抛光粉和石灰石粉双掺对混凝土性能的影响研究
Effecting Study of Mixed Ceramic Polishing Powder and Limestone Powder on Performance of Concrete
2013年第8期
陶瓷抛光粉;石灰石粉;混凝土;抗压强度;工作性;耐久性
Ceramic polishing powder; Limestone powder; Concrete; Compressive strength; Workability; Durability
2013年第8期
1000-4637(2013)08-05-04
段明磊,肖 强,程智清,杨金铨,刘 聪,王立军
云南省交通科学研究院,昆明 650011

段明磊,肖 强,程智清,杨金铨,刘 聪,王立军

浏览量:
1000
摘 要:研究了不同掺量的陶瓷抛光粉和石灰石粉对混凝土工作性、力学性能以及抗氯离子扩散和抗冻融性能的影响。结果表明,双掺10%石灰石粉和不超过20%的陶瓷抛光粉可以提高混凝土坍落度,改善粘聚性,同时可细化混凝土孔结构并改善其界面结构,从而提高混凝土强度、抗氯离子扩散和抗冻融性能。双掺时,陶瓷抛光粉最佳掺量为10%;继续增加陶瓷抛光粉掺量对于改善混凝土内部结构无益,反而劣化了混凝土性能。 Abstract: Effects of different contents of ceramic polishing powder and limestone powder on the workability, mechanical properties, resistance chlorine diffusion and freezing-thawing circle of concrete are studied in this paper. The results indicate that the workability, microstructure, compressive strength, resistance chlorine diffusion and freezing-thawing circle performance of concrete mixed with 10% limestone powder and not more than 20% ceramic polishing powder are improved. The optimal replaced content of ceramic polishing powder is 10%, when mixed with limestone and ceramic polishing powder. However, the performance of concrete could not be improved when the dosage of ceramic polishing powder is more than 10%.
英文名 : Effecting Study of Mixed Ceramic Polishing Powder and Limestone Powder on Performance of Concrete
刊期 : 2013年第8期
关键词 : 陶瓷抛光粉;石灰石粉;混凝土;抗压强度;工作性;耐久性
Key words : Ceramic polishing powder; Limestone powder; Concrete; Compressive strength; Workability; Durability
刊期 : 2013年第8期
DOI :
文章编号 : 1000-4637(2013)08-05-04
基金项目 :
作者 : 段明磊,肖 强,程智清,杨金铨,刘 聪,王立军
单位 : 云南省交通科学研究院,昆明 650011

段明磊,肖 强,程智清,杨金铨,刘 聪,王立军

摘要
参数
结论
参考文献
引用本文

摘   要:研究了不同掺量的陶瓷抛光粉和石灰石粉对混凝土工作性、力学性能以及抗氯离子扩散和抗冻融性能的影响。结果表明,双掺10%石灰石粉和不超过20%的陶瓷抛光粉可以提高混凝土坍落度,改善粘聚性,同时可细化混凝土孔结构并改善其界面结构,从而提高混凝土强度、抗氯离子扩散和抗冻融性能。双掺时,陶瓷抛光粉最佳掺量为10%;继续增加陶瓷抛光粉掺量对于改善混凝土内部结构无益,反而劣化了混凝土性能。

Abstract: Effects of different contents of ceramic polishing powder and limestone powder on the workability, mechanical properties, resistance chlorine diffusion and freezing-thawing circle of concrete are studied in this paper. The results indicate that the workability, microstructure, compressive strength, resistance chlorine diffusion and freezing-thawing circle performance of concrete mixed with 10% limestone powder and not more than 20% ceramic polishing powder are improved. The optimal replaced content of ceramic polishing powder is 10%, when mixed with limestone and ceramic polishing powder. However, the performance of concrete could not be improved when the dosage of ceramic polishing powder is more than 10%.

关键词:
陶瓷抛光粉;石灰石粉;混凝土;抗压强度;工作性;耐久性
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加
(1)石灰石粉和陶瓷抛光粉在合适掺量范围内,均具有一定减水效果,可以增大混凝土拌合物的坍落度。双掺10%石灰石粉和10%陶瓷抛光粉的混凝土拌合物坍落度最大;当陶瓷抛光粉掺量超过10%时,反而会降低混凝土的坍落度。
(2)双掺陶瓷抛光粉和石灰石粉的混凝土早期抗压强度随着陶瓷抛光粉掺量的增加而降低,掺入不大于20%陶瓷抛光粉的双掺混凝土后期强度发展良好。双掺10%陶瓷抛光粉和10%石灰石粉的混凝土各龄期强度均高于普通混凝土,表现出陶瓷抛光粉后期活性和石灰石粉早期增强的互补效应。
(3)陶瓷抛光粉和石灰石粉的互补效应使得双掺10%陶瓷抛光粉和10%石灰石粉混凝土的抗氯离子扩散性能优于普通混凝土,其抗冻融性能则与普通混凝土相近。
  由此可见,采用10%陶瓷抛光粉和10%石灰石粉双掺的方法,可以替代传统紧缺矿物掺合料用于公路工程混凝土中,其工作性能、抗压强度及抗氯离子扩散性能均优于普通混凝土,且抗冻融性能与普通混凝土相近,这为缓解公路工程矿物掺合料紧缺提供了新的、有效的方法。
[1] 石正国,王黎.陶瓷砖抛光粉在C30混凝土中的应用[J].混凝土,2012(3):138-140.
[2] 苏达根,王功勋,钟小敏.陶瓷抛光砖粉的组成及火山灰活性研究[J].水泥工程,2008(4):22-24.
[3] 于利刚,吴锦锋,李云国,等.利用陶瓷废料作水泥混合材的试验研究[J].水泥,2004(10):10-11.
[4] 钟明峰,张志杰,王功勋.常温与蒸压条件下陶瓷抛光粉的反应活性及其应用研究[J].混凝土与水泥制品,2010(4):72-74.
[5] 王功勋,苏达根.石灰-抛光砖粉结合料的性能研究[J].公路工程,2008,33(5):65-68.
[6] 王功勋,苏达根,钟小敏.陶瓷抛光砖粉对混凝土性能的影响[J].混凝土,2008(10):64-65.
[7] 杨华山,方坤河,涂胜金,等.石灰石粉在水泥基材料中的作用及机理[J].混凝土,2006(6):32-35.
[8] 肖斐,崔洪涛,陈剑雄,等.超磨细石灰石粉高强混凝土的研究[J].硅酸盐通报,2010,29(6):1303-1307.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州