预拌砂浆用外加剂的技术经济特性分析
Technical and Economic Characteristic Analysis on Admixture Used for Ready-mixed Mortar
2014年第12期
:砂浆外加剂;预拌砂浆;保水性;收缩率;拉伸粘结强度;抗压强度
Mortar admixture; Ready mixed mortar; Water-retaining property; Shrinkage; Tensile bond strength; Compressive strength
2014年第12期
1000-4637(2014)12-75-05
范红兵1,胡建安2,王 涛3
1.江苏三阳建设工程检测有限公司,常州213023;2.无锡市市政工程质量检测中心,214011; 3.江苏省建工建材质量检测中心,南京210009

范红兵1,胡建安2,王 涛3

浏览量:
1000
摘 要:随着预拌砂浆的推广和普及,作为改善砂浆性能的外加剂得到了广泛的应用,不同的外加剂对砂浆的技术性能有着不同的作用。研究了四种不同砂浆外加剂对预拌砂浆技术性能的影响,结果表明,砂浆外加剂不同的掺量对砂浆的性能影响较大,当外加剂的掺量为0.025%~0.075%时,能有效提高砂浆的抗压强度和拉伸粘结强度。外加剂的掺入可以改善砂浆的收缩率和抗冻性,多组分的砂浆外加剂体现出较为优异的技术经济特性。 Abstract:With the promotion and popularization of ready mixed mortar,admixture which can improve the performance of mortar has been widely used. Admixtures would affect the performance of building mortar. Here, the effect of four kinds of mortar admixture on the performance of mortars is investigated, and the results show that the admixture content has a great effect on the performance of the mortar. When the admixture content is 0.025%~0.075%, the compressive strength and tensile strength of mortars increase effectively, and the shrinkage and freezing resistance are improved as well. The mortar admixture with multi-component shows more prominent technical and economic characteristics.
英文名 : Technical and Economic Characteristic Analysis on Admixture Used for Ready-mixed Mortar
刊期 : 2014年第12期
关键词 : :砂浆外加剂;预拌砂浆;保水性;收缩率;拉伸粘结强度;抗压强度
Key words : Mortar admixture; Ready mixed mortar; Water-retaining property; Shrinkage; Tensile bond strength; Compressive strength
刊期 : 2014年第12期
DOI :
文章编号 : 1000-4637(2014)12-75-05
基金项目 :
作者 : 范红兵1,胡建安2,王 涛3
单位 : 1.江苏三阳建设工程检测有限公司,常州213023;2.无锡市市政工程质量检测中心,214011; 3.江苏省建工建材质量检测中心,南京210009

范红兵1,胡建安2,王 涛3

摘要
参数
结论
参考文献
引用本文

摘   要:随着预拌砂浆的推广和普及,作为改善砂浆性能的外加剂得到了广泛的应用,不同的外加剂对砂浆的技术性能有着不同的作用。研究了四种不同砂浆外加剂对预拌砂浆技术性能的影响,结果表明,砂浆外加剂不同的掺量对砂浆的性能影响较大,当外加剂的掺量为0.025%~0.075%时,能有效提高砂浆的抗压强度和拉伸粘结强度。外加剂的掺入可以改善砂浆的收缩率和抗冻性,多组分的砂浆外加剂体现出较为优异的技术经济特性。

Abstract:With the promotion and popularization of ready mixed mortar,admixture which can improve the performance of mortar has been widely used. Admixtures would affect the performance of building mortar. Here, the effect of four kinds of mortar admixture on the performance of mortars is investigated, and the results show that the admixture content has a great effect on the performance of the mortar. When the admixture content is 0.025%~0.075%, the compressive strength and tensile strength of mortars increase effectively, and the shrinkage and freezing resistance are improved as well. The mortar admixture with multi-component shows more prominent technical and economic characteristics.

关键词:
砂浆外加剂;预拌砂浆;保水性;收缩率;拉伸粘结强度;抗压强度
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加
(1)砂浆外加剂具有明显的保水增稠效果,当掺量为0.025%~0.075%时,能满足多种类型砂浆对稠度、保水率和凝结时间的要求。掺量过大,会导致砂浆的凝结时间过长。在工程施工中,如果砂浆的凝结时间太长,将减缓施工速度,甚至会影响到砌体工程或抹灰工程的质量。
(2)砂浆外加剂的掺量在0.050%~0.100%范围内,能有效地降低砂浆收缩率,在此掺量范围内收缩率的降低并不随掺量的增大而增大。而低掺量则对收缩率的改善无明显效果。
(3)砂浆的拉伸粘结强度并不随砂浆外加剂掺量的增加而提高,相反,过量的掺加砂浆外加剂可能导致其拉伸粘结强度的降低,当砂浆外加剂的掺量为0.025%~0.075%时,对砂浆的拉伸粘结强度有所提高,高掺量(≥0.100%)有可能导致拉伸粘结强度不合格。
(4)四种外加剂的掺量在0.025%~0.050%范围内,均有效地提高了抗压强度,T-3和T-4的提高幅度明显高于T-1、T-2。掺量加大,抗压强度的提高幅度反而降低,甚至无增强作用。
(5)外加剂中,多组分T-3和T-4的各项技术经济指标明显优于单组分的T-1和T-2。
[1] 黄利频.预拌砂浆技术的研究[J].新型建筑材料,2007(3):8-11.
[2] 李春荣,管小军,鞠丽艳.AF砂浆保水剂的研制[J].房材与应用,2001(6):25-27.
[3] 李燚.无机增稠剂在干混砂浆中的应用[J].建设科技,2012(22):90-91.
[4] 赵立群,樊钧.稠化粉在砂浆中的应用研究[A].2004年中国国际建筑干混砂浆生产应用技术研讨会论文集[C].北京,2004:77-81,121.
[5] 雷艳春,贺军贤,鲍迎水,等.高效砂浆增塑剂配制水泥砂浆试验研究[J].科技信息,2009(1):57.
[6] 徐志芳,卢迪芬.用于干粉砂浆中的添加剂[J].广东建材,2007(12):32-35.
[7] 叶慧丽,潘钢华.干混砌筑砂浆外加剂的研究[J].材料工程,2006(S1):259-263.
[8] 中华人民共和国质量监督检验检疫总局,中国国家标准化管理委员会. GB/T25181-2010 预拌砂浆[S].北京:中国标准出版社,2011.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州