C30~C60自密实混凝土的配制及性能研究
Preparation and Performance Research on C30~C60 Self-compacting Concrete(SCC)
2014年第2期
自密实混凝土;大掺量矿物掺合料;抗压强度;氯离子渗透性能
Self-compacting concrete; High volume of mineral admixtures; Compressive strength; Permeability of chloride ion
2014年第2期
1000-4637(2014)02-09-04
徐仁崇1,陈 茜1,苏艺凡1,刘光锐1,徐少杰2
1. 厦门市建筑科学研究院集团股份有限公司,361004;2. 厦门天润锦龙建材有限公司,361009

徐仁崇1,陈 茜1,苏艺凡1,刘光锐1,徐少杰2

浏览量:
1000
摘 要:采用大掺量矿物掺合料配制C30~C60自密实混凝土,并对自密实混凝土的工作性能、强度及抗氯离子渗透性能进行研究。结果表明,增加胶凝材料用量可以改善混凝土的自密实性能,采用大掺量矿物掺合料替代水泥保证混凝土粉体总量,是配制中低强度自密实混凝土的方法之一;大掺量矿物掺合料自密实混凝土的抗压强度和抗氯离子渗透性能随龄期的增长不断提高,大矿物掺合料自密实混凝土的抗压强度和抗氯离子渗透性能评价应以56d龄期为准。 Abstract: C30~C60 self-compacting concrete (SCC) is made by a high volume of mineral admixtures. The workability, strength and the penetration resistance of chloride ions performance of SCC are investigated. The results show that increasing the proportion of binding material can improve the self compacting performance of concrete, and using large amount of mineral admixture as substitution of cement is a way of making mid-low strength SCC. The compressive strength and penetration resistance of chloride ions performance of SCC with a large proportion of mineral admixtures are improved continually with the increase of curing period, and should be evaluated by the age of 56d.
英文名 : Preparation and Performance Research on C30~C60 Self-compacting Concrete(SCC)
刊期 : 2014年第2期
关键词 : 自密实混凝土;大掺量矿物掺合料;抗压强度;氯离子渗透性能
Key words : Self-compacting concrete; High volume of mineral admixtures; Compressive strength; Permeability of chloride ion
刊期 : 2014年第2期
DOI :
文章编号 : 1000-4637(2014)02-09-04
基金项目 :
作者 : 徐仁崇1,陈 茜1,苏艺凡1,刘光锐1,徐少杰2
单位 : 1. 厦门市建筑科学研究院集团股份有限公司,361004;2. 厦门天润锦龙建材有限公司,361009

徐仁崇1,陈 茜1,苏艺凡1,刘光锐1,徐少杰2

摘要
参数
结论
参考文献
引用本文

摘   要:采用大掺量矿物掺合料配制C30~C60自密实混凝土,并对自密实混凝土的工作性能、强度及抗氯离子渗透性能进行研究。结果表明,增加胶凝材料用量可以改善混凝土的自密实性能,采用大掺量矿物掺合料替代水泥保证混凝土粉体总量,是配制中低强度自密实混凝土的方法之一;大掺量矿物掺合料自密实混凝土的抗压强度和抗氯离子渗透性能随龄期的增长不断提高,大矿物掺合料自密实混凝土的抗压强度和抗氯离子渗透性能评价应以56d龄期为准。

Abstract: C30~C60 self-compacting concrete (SCC) is made by a high volume of mineral admixtures. The workability, strength and the penetration resistance of chloride ions performance of SCC are investigated. The results show that increasing the proportion of binding material can improve the self compacting performance of concrete, and using large amount of mineral admixture as substitution of cement is a way of making mid-low strength SCC. The compressive strength and penetration resistance of chloride ions performance of SCC with a large proportion of mineral admixtures are improved continually with the increase of curing period, and should be evaluated by the age of 56d.

关键词:
自密实混凝土;大掺量矿物掺合料;抗压强度;氯离子渗透性能
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加
(1)足够的胶凝材料用量是配制自密实混凝土的前提,增加胶凝材料用量能够改善自密实混凝土拌合物的自密实性能,采用大掺量矿物掺合料替代水泥保证混凝土粉体总量,是配制中低强度自密实混凝土的方法之一。
(2)试验配制的自密实混凝土的抗压强度随龄期的增长不断提高,56d抗压强度可达最终强度的95%;试验结果表明,实际操作中应以56d抗压强度作为大掺量矿物掺合料自密实混凝土的抗压强度判定值。
(3)试验配制的自密实混凝土具有良好的抗氯离子渗透性能,且其抗氯离子渗透性能随龄期的增长不断提高,28d到56d混凝土的抗氯离子渗透性能提高约50%,56d后混凝土的抗氯离子渗透性能提高较小;对于大掺量矿物掺合料自密实混凝土,混凝土抗氯离子渗透性能的评价应以56d龄期为准。
[1] 刘运华, 谢友均, 龙广成. 自密实混凝土研究进展[J]. 硅酸盐学报, 2007(5): 671-674.
[2] 顾国荣. 广州西塔工程C100及C100自密实混凝土配制、生产及其超高层泵送技术[J]. 混凝土世界, 2009,(7): 31-41.
[3] 徐仁崇, 桂苗苗, 曾冲盛, 等. 厦门财富中心钢管自密实混凝土的研究与应用[J]. 施工技术, 2011, 40(8): 65-67.
[4] 刘建忠, 孙伟, 缪昌文, 等. 矿物掺合料对低水胶比混凝土干缩和自收缩的影响[J]. 东南大学学报: 自然科学版, 2009(5): 580-585.
[5] 谢友均, 马昆林, 龙广成, 等. 矿物掺合料对混凝土中氯离子渗透性能的影响[J]. 硅酸盐学报, 2006, 34(11): 1345-1350.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州