3D打印水泥基材料的建造性研究
Research on Buildability of 3D Printing Cementitious Materials
2020年第5期
水泥基材料;3D打印;建造性;流变性能
Cementitious materials; 3D printing; Buildability; Rheological property
2020年第5期
10.19761/j.1000-4637.2020.05.006.04
国家自然科学基金重点项目(51738003)。
章苏阳,蒋亚清,王 玉,潘亭宏
河海大学 力学与材料学院,南京 211100

章苏阳,蒋亚清,王 玉,潘亭宏

章苏阳,蒋亚清,王玉,等.3D打印水泥基材料的建造性研究[J].混凝土与水泥制品,2020(5):6-9.

ZHANG S Y,JIANG Y Q,WANG Y,et al.Research on Buildability of 3D Printing Cementitious Materials[J].China Concrete and Cement Products,2020(5):6-9.

浏览量:
1000
摘 要:通过塑性强度、静态屈服应力和跳桌流动度的经时变化试验,研究了纳米黏土与减水剂协同作用对3D打印水泥基材料(3DPC)建造性的影响,并以流变性能为参考依据,建立了3DPC建造性的评价指标。结果表明,复掺纳米黏土和增黏型聚羧酸减水剂的3DPC经时塑性强度和经时静态屈服应力均随纳米黏土掺量增加而提高,纳米黏土的适宜掺量为0.8%;当静态屈服应力时变速率为2.0~4.2Pa/s时,可实现3DPC的挤出性与建造性的协同;在可打印、可建造窗口时间内,3DPC的跳桌流动度为170~190mm。掺用纳米黏土和增黏型聚羧酸减水剂对3DPC的流变参数进行调控是提高3DPC建造性的有效途径。Abstract:Buildabilityisanimportantperformanceparameterof3Dprintingcementitiousmaterials(3DPC).Effectofnano-clayandviscositymodifyingpolycarboxylatesuperplasticizer(VPCE)onbuildabilityof3DPCwasinvestigatedbytestingtimedependentgreenstrength,staticyieldstressandflowtable.Indexesforevaluationthebuildabilityof3DPCwereestablishedbasedonthereferenceofrheologicalparameter.ExperimentalresultsshowthatbothgreenstrengthandstaticyieldstressofVPCEdispersed3DPCincreasewithincreaseofnano-claydosage,andthesuitabledosageofnano-clayis0.8%.Synergybetweenextruderabilityandbuildabilitycanberealizedwhenthestaticyieldstressretentionrateequals2.0~4.2Pa/s.Duringprintwindowtime,flowtablevalueof3DPCis170~190mm.Itisaneffectivewaytoimprovethebuildabilityof3DPCbyrheologymodifyingtechniquebasedonnano-clayandVPCE.
英文名 : Research on Buildability of 3D Printing Cementitious Materials
刊期 : 2020年第5期
关键词 : 水泥基材料;3D打印;建造性;流变性能
Key words : Cementitious materials; 3D printing; Buildability; Rheological property
刊期 : 2020年第5期
DOI : 10.19761/j.1000-4637.2020.05.006.04
文章编号 :
基金项目 : 国家自然科学基金重点项目(51738003)。
作者 : 章苏阳,蒋亚清,王 玉,潘亭宏
单位 : 河海大学 力学与材料学院,南京 211100

章苏阳,蒋亚清,王 玉,潘亭宏

章苏阳,蒋亚清,王玉,等.3D打印水泥基材料的建造性研究[J].混凝土与水泥制品,2020(5):6-9.

ZHANG S Y,JIANG Y Q,WANG Y,et al.Research on Buildability of 3D Printing Cementitious Materials[J].China Concrete and Cement Products,2020(5):6-9.

摘要
参数
结论
参考文献
引用本文

摘  要:通过塑性强度、静态屈服应力和跳桌流动度的经时变化试验,研究了纳米黏土与减水剂协同作用对 3D打印水泥基材料(3DPC)建造性的影响,并以流变性能为参考依据,建立了3DPC建造性的评价指标。结果表明,复掺纳米黏土和增黏型聚羧酸减水剂的3DPC经时塑性强度和经时静态屈服应力均随纳米黏土掺量增加而提高,纳米黏土的适宜掺量为0.8%;当静态屈服应力时变速率为2.0~4.2 Pa/s时,可实现3DPC的挤出性与建造性的协同;在可打印、可建造窗口时间内,3DPC的跳桌流动度为170~190 mm。掺用纳米黏土和增黏型聚羧酸减水剂对3DPC的流变参数进行调控是提高3DPC建造性的有效途径。Abstract: Buildability is an important performance parameter of 3D printing cementitious materials (3DPC). Effect of nano-clay and viscosity modifying polycarboxylate superplasticizer (VPCE) on buildability of 3DPC was investigated by testing time dependent green strength, static yield stress and flow table. Indexes for evaluation the buildability of 3DPC were established based on the reference of rheological parameter. Experimental results show that both green strength and static yield stress of VPCE dispersed 3DPC increase with increase of nano-clay dosage, and the suitable dosage of nano-clay is 0.8%. Synergy between extruderability and buildability can be realized when the static yield stress retention rate equals 2.0~4.2 Pa/s. During print window time, flow table value of 3DPC is 170~190 mm. It is an effective way to improve the buildability of 3DPC by rheology modifying technique based on nano-clay and VPCE.

关键词:
3d
3dpc
of
and
buildability
黏土
纳米
建造
the
is
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加
(1)利用纳米黏土和增黏型聚羧酸减水剂对砂浆中水泥浆体絮凝及结构化过程的协同调控,可获得具有优良挤出性和建造性的3D打印水泥基材料,纳米黏土的适宜掺量为水泥质量的0.8%。
(2)当3D打印水泥基材料的静态屈服应力时变率大于最小时变率Athix,min时,将会获得预期的3D打印建造性。
(3)以静态屈服应力时变率2~4.2 Pa/s为建造性参数,相应的砂浆跳桌流动度170~190 mm,可作为3D打印砂浆打印窗口时间内的性能控制指标。
 
[1] 耿会岭,杨政,袁雅贤.3D打印在建筑领域的应用[J].混凝土与水泥制品,2019(7):34-38.
[2] 侯泽宇,张宇,张超.3D打印混凝土力学性能试验方法[J].混凝土与水泥制品,2019(11):1-5.
[3] YUAN Q,Li Z M,ZHOU D J,et al.A feasible method for measuring the buildability of fresh 3D printing mortar[J]. Construction and Building Materials,2019,227:116600.
[4] CASAGRANDE L,ESPOSITO L,MENNA C,et al.Effect of testing procedures on buildability properties of 3D-printable concrete[J].Construction and Building Materials,2020,245:118286.
[5] MENDOZA R O A,DUDA P,SILVA E C C M,et al. Nanosilica particles as structural buildup agents for 3D printing with Portland cement pastes[J].Construction and Building Materials,2019,219:91-100.
[6] MANIKANDAN K,WI K,ZHANG X,et al.Characterizing cement mixtures for concrete 3D printing[J].Manufacturing Letters,2020(24):33-37.
[7] PAPACHRISTOFOROU M,MITSOPOULOSLOS V,STEFANIDOU M.Evaluation of workability parameters in 3D printing concrete[J].Procedia Structural Integrity,2018(10):155-162.

章苏阳,蒋亚清,王玉,.3D打印水泥基材料的建造性研究[J].混凝土与水泥制品,2020(5):6-9.

ZHANG S Y,JIANG Y Q,WANG Y,et al.Research on Buildability of 3D Printing Cementitious Materials[J].China Concrete and Cement Products,2020(5):6-9.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州