耐碱玻纤和粉煤灰对轻质混凝土强度及冻融 耐久性的影响研究
Experimental Study on Strength and Freeze-thaw Durability of Alkali-Resistant Glass Fiber Fly Ash Lightweight Concrete
2020年第5期
轻质混凝土;耐碱玻纤;粉煤灰;强度;冻融耐久性
Lightweight concrete; Alkali-resistant glass fiber; Fly ash; Strength; Freeze-thaw durability
2020年第5期
10.19761/j.1000-4637.2020.05.051.06
四川省教育厅2018年度科研项目(CKJ175983)。
李茜莎
西昌学院 土木与水利工程学院,615000

李茜莎

李茜莎.耐碱玻纤和粉煤灰对轻质混凝土强度及冻融耐久性的影响研究[J].混凝土与水泥制品,2020(5):51-55,60.

LI Q S.Experimental Study on Strength and Freeze-thaw Durability of Alkali-Resistant Glass Fiber Fly Ash Lightweight Concrete[J].China Concrete and Cement Products,2020(5):51-55,60.

浏览量:
1000
摘 要:以陶粒为粗骨料制备了轻质混凝土试件,研究了耐碱玻纤、粉煤灰增强材料对轻质混凝土的力学性能及冻融耐久性的影响。结果表明,随着耐碱玻纤掺量的增加,同一龄期轻质混凝土试件的抗压强度、抗拉强度先增大后减小;过高的耐碱玻纤掺量不利于强度的增长,且耐碱玻纤对试件抗拉强度的影响大于抗压强度,其最优掺量为0.6kg/m3;掺入适量的粉煤灰(≤15%)能提高轻质混凝土的强度,提升幅度与掺量成正比,但掺量较大时对强度不利;与未掺耐碱玻纤的试件相比,当耐碱玻纤掺量低于0.6kg/m3和1.0kg/m3时,能分别提升试件的相对动弹性模量和降低质量损失率,改善幅度与耐碱玻纤的掺量正相关;粉煤灰掺量低于15%时有利于提高试件的冻融耐久性,但掺量较高(≥20%)则会降低试件的冻融耐久性指标。Abstract:Lightweightconcretespecimenswerefabricatedwithceramsiteascoarseaggregate,andtheeffectsofreinforcedmaterialsasalkali-resistantglassfiberandflyashonthemechanicalpropertiesandfreeze-thawdurabilityoflightweightconcretewerestudied.Theresultsshowthatwiththeincreaseofalkali-resistantglassfibercontent,thecompressiveandtensilestrengthoflightweightconcreteatthesameageincreasefirstandthendecrease.Excessivealkali-resistantglassfibercontentisnotconducivetotheincreaseofstrength,andtheinfluenceofalkali-resistantglassfiberonthetensilestrengthofspecimensisgreaterthanthatofcompressivestrength,andtheoptimalcontentis0.6kg/m3.Thestrengthoflightweightconcretecanbeimprovedbyaddingappropriateamountofflyash(≤15%),andtheincreasingrangeisproportionaltotheamountofflyash,butitisunfavorabletothestrengthwhentheamountofflyashislarge.Comparedwiththespecimenswithoutalkali-resistantglassfiber,whenthecontentofalkali-resistantglassfiberislessthan0.6kg/m3and1.0kg/m3,therelativedynamicelasticmodulusandmasslossrateofspecimenscanbeincreasedrespectively,andtheimprovementrangeispositivelycorrelatedwiththecontentofalkali-resistantglassfiber.Whenflyashcontentislessthan15%,itisbeneficialtoimprovethefreeze-thawdurabilityofthespecimens,butthehighflyashcontent(≥20%)willseriouslyreducethefreeze-thawdurabilityindexofthespecimens.
英文名 : Experimental Study on Strength and Freeze-thaw Durability of Alkali-Resistant Glass Fiber Fly Ash Lightweight Concrete
刊期 : 2020年第5期
关键词 : 轻质混凝土;耐碱玻纤;粉煤灰;强度;冻融耐久性
Key words : Lightweight concrete; Alkali-resistant glass fiber; Fly ash; Strength; Freeze-thaw durability
刊期 : 2020年第5期
DOI : 10.19761/j.1000-4637.2020.05.051.06
文章编号 :
基金项目 : 四川省教育厅2018年度科研项目(CKJ175983)。
作者 : 李茜莎
单位 : 西昌学院 土木与水利工程学院,615000

李茜莎

李茜莎.耐碱玻纤和粉煤灰对轻质混凝土强度及冻融耐久性的影响研究[J].混凝土与水泥制品,2020(5):51-55,60.

LI Q S.Experimental Study on Strength and Freeze-thaw Durability of Alkali-Resistant Glass Fiber Fly Ash Lightweight Concrete[J].China Concrete and Cement Products,2020(5):51-55,60.

摘要
参数
结论
参考文献
引用本文

摘  要:以陶粒为粗骨料制备了轻质混凝土试件,研究了耐碱玻纤、粉煤灰增强材料对轻质混凝土的力学性能及冻融耐久性的影响。结果表明,随着耐碱玻纤掺量的增加,同一龄期轻质混凝土试件的抗压强度、抗拉强度先增大后减小;过高的耐碱玻纤掺量不利于强度的增长,且耐碱玻纤对试件抗拉强度的影响大于抗压强度,其最优掺量为0.6 kg/m3;掺入适量的粉煤灰(≤15%)能提高轻质混凝土的强度,提升幅度与掺量成正比,但掺量较大时对强度不利;与未掺耐碱玻纤的试件相比,当耐碱玻纤掺量低于0.6 kg/m3和1.0 kg/m3时,能分别提升试件的相对动弹性模量和降低质量损失率,改善幅度与耐碱玻纤的掺量正相关;粉煤灰掺量低于15%时有利于提高试件的冻融耐久性,但掺量较高(≥20%)则会降低试件的冻融耐久性指标。

Abstract: Lightweight concrete specimens were fabricated with ceramsite as coarse aggregate, and the effects of reinforced materials as alkali-resistant glass fiber and fly ash on the mechanical properties and freeze-thaw durability of lightweight concrete were studied. The results show that with the increase of alkali-resistant glass fiber content, the compressive and tensile strength of lightweight concrete at the same age increase first and then decrease. Excessive alkali-resistant glass fiber content is not conducive to the increase of strength, and the influence of alkali-resistant glass fiber on the tensile strength of specimens is greater than that of compressive strength, and the optimal content is 0.6 kg/m3. The strength of lightweight concrete can be improved by adding appropriate amount of fly ash(≤15%), and the increasing range is proportional to the amount of fly ash, but it is unfavorable to the strength when the amount of fly ash is large. Compared with the specimens without alkali-resistant glass fiber, when the content of alkali-resistant glass fiber is less than 0.6 kg/m3 and 1.0 kg/m3, the relative dynamic elastic modulus and mass loss rate of specimens can be increased respectively, and the improvement range is positively correlated with the content of alkali-resistant glass fiber. When fly ash content is less than 15%, it is beneficial to improve the freeze-thaw durability of the specimens, but the high fly ash content (≥ 20%) will seriously reduce the freeze-thaw durability index of the specimens.

关键词:
轻质混凝土;耐碱玻纤;粉煤灰;强度;冻融耐久性
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加
(1)适量耐碱玻纤对提高轻质混凝土的抗拉、抗压强度有利,尤其对抗拉强度改善幅度较大。耐碱玻纤的适宜掺量为0.6 kg/m3,低于该掺量,试件的抗压及抗拉强度与耐碱玻纤掺量成正比,高于该掺量,试件的强度反而会逐步下降。
(2)与耐碱玻纤对轻质混凝土强度的影响规律类似,粉煤灰的适宜掺量为15%,掺量低于该值时对强度有利,超过15%则会削弱强度,尤其是耐碱玻纤掺量较高时。
(3)耐碱玻纤掺量低于1.0 kg/m3、粉煤灰掺量低于15%时对降低冻融试件的质量损失率有利。耐碱玻纤掺量0.6 kg/m3及以下时有利于提高轻质混凝土的相对动弹性模量,高于该掺量则会降低试件的相对动弹性模量。
(4)大掺量粉煤灰(≥20%)对掺有耐碱玻纤的轻质混凝土的强度及冻融耐久性均不利,尤其是耐碱玻纤掺量较大时。
[1] 范雪,张亮.聚合物对火山渣轻集料混凝土性能的影响[J].吉林建筑大学学报,2018,35(4) :5-8.
[2] SARI D,PASAMEHMETOGLU A G.The effects of gradation and admixture on the pumice lightweight aggregate concrete[J].Cement and Concrete Research,2005,35(5):936-942.
[3] 董祥,何培玲,高建明.聚合物对高性能轻骨料混凝土力学性能及微观结构的影响研究[J].四川建筑科学研究,2006,32(3):131-134.
[4] 陈培鑫,李建新,陈耿,等.原料掺量对泡沫混凝土性能的影响研究[J].广东土木与建筑,2018,25(9):55-58.
[5] HUANG Z,ZHANG T,WEN Z.Proportioning and characterization of Portland cement-based ultra-lightweight foam concretes[J].Construction and Building Materials,2015,79:390-396.
[6] MALESEV M,RADONJANIN V,LUKIC I,et al.The effect of aggregate, type and quantity of cement on modulus of elasticity of lightweight aggregate concrete[J].Arabian Journal for Science and Engineering,2014,39(2):705-711.
[7] 杨智硕,陈明霞,叶梅新.玄武岩纤维对超高强混凝土力学性能的影响[J].混凝土与水泥制品,2019(2):56-59.
[8] 赵文辉,苏谦,李婷,等.玻璃纤维增强泡沫轻质混凝土力学性能的试验研究[J].工业建筑,2017,47(9):110-115.
[9] 张荣辉,李健.仿钢纤维增强轻骨料混凝土性能研究[J].新型建筑材料,2012,39(5):69-72.
[10] 丁庆军,王涛,张锋,等.混掺纤维增强轻集料混凝土研究[J].武汉理工大学学报,2004,26(1):42-45.
[11] EVA K,PACH L,PALOU M.Effect of activated foaming agent on the foam concrete properties[J].Construction and Building Materials,2016,125:998-1004.
[12] 郑秀华,张宝生,袁杰,等.引气剂与粉煤灰对大流动性轻集料混凝土性能的影响[J].混凝土,2005(4):88-92.
[13]  中华人民共和国住房和城乡建设部.JGJ/T 221—2010纤维混凝土应用技术规程[S].北京:中国建筑工业出版社,2010.
[14] 中华人民共和国建设部.JGJ 51—2002轻骨料混凝土技术规程[S].北京:中国建筑工业出版社,2002.
[15] 中华人民共和国建设部,国家质量监督检验检疫总局.GB/T 50081—2002普通混凝土力学性能试验方法标准[S].北京:中国建筑工业出版社,2003.
[16] 中华人民共和国住房和城乡建设部.GB/T 50082—2009普通混凝土长期性能和耐久性能试验方法标准[S].北京:中国建筑工业出版社,2010.

李茜莎.耐碱玻纤和粉煤灰对轻质混凝土强度及冻融耐久性的影响研究[J].混凝土与水泥制品,2020(5):51-55,60.

LI Q S.Experimental Study on Strength and Freeze-thaw Durability of Alkali-Resistant Glass Fiber Fly Ash Lightweight Concrete[J].China Concrete and Cement Products,2020(5):51-55,60.

 

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州