高钛矿渣膨珠制备轻集料砂浆空心砌块研究

Study on the Preparation of Light-weight Mortar Hollow Blocks with Granulated Blast Titanium Slag

2018年第5期

高钛矿渣膨珠；轻集料砂浆；空心砌块；压制成型

Granulated blast titanium slag; Light-weight mortar; Compressive strength; Dry density

2018年第5期

1000-4637（2018）05-58-05

国家重点研发计划项目（2016YFC0701004）；国家自然科学基金项目（51402246）。

罗凯1,2，李军1，卢忠远1，蒋俊1,2，白媛1,2，赵杰3

1.西南科技大学环境友好能源材料国家重点实验室，绵阳 621010； 2.西南科技大学材料科学与工程学院，绵阳 621010； 3.攀枝花钢城集团凉山瑞海实业有限公司，615000

罗凯1,2，李军1，卢忠远1，蒋俊1,2，白媛1,2，赵杰3

罗凯,李军,卢忠远,等.高钛矿渣膨珠制备轻集料砂浆空心砌块研究[J].混凝土与水泥制品,2018(5):58-62.

LUO K,LI J,LU Z Y,et al.Study on the Preparation of Light-weight Mortar Hollow Blocks with Granulated Blast Titanium Slag[J].China Concrete and Cement Products,2018(5):58-62.

浏览量:

1000

摘要：以水淬高钛矿渣膨珠为轻骨料，普通硅酸盐水泥为胶凝材料，脱硫石膏为激发剂，采用压制成型工艺制备了轻集料砂浆，研究了高钛矿渣膨珠、水泥、脱硫石膏掺量和对轻集料砂浆力学性能和干密度的影响，利用X射线衍射（XRD）、扫描电镜（SEM）手段对轻质砂浆矿物结构和微观形貌进行了表征。此外，以优选的轻质砂浆为基体，工厂试制了轻质砂浆小型空心砌块。结果表明：轻质砂浆力学性能和干密度随水泥用量增加而升高；随脱硫石膏用量增加，轻集料砂浆抗压强度先增加后降低，干密度变化不大。固定胶凝材料用量18%、脱硫石膏替代水泥20%条件下，所制备轻集料砂浆抗压强度16.0MPa，干密度1789kg/m3，以该轻骨料砂浆为基体材料进行轻集料砂浆小型空心砌块试制，可制备出抗压强度9.6MPa，干密度1223kg/m3，MU7.5的空心砌块。Abstract:Thelight-weightmortarismadebyusinggranulatedblasttitaniumslagasaggregate,ordinaryportlandcementascementingmaterial,desulfurizedgypsumasactivator,frompressmouldingandcombinedwithXRDandSEM,theeffectofcementcontentandactivatorcontentonthecopressivestrengthanddrydensityoflight-weightmortarareinvestigated.Onthebasisofthis,theactualproductionofconcretehollowblockiscarriedout.Theresultsshowthatthecompressivestrengthanddrydensitybecomestrongerasthecementcontentincreases.ThechangeofW/Chadalittleeffectonthedrydensityoflight-weightmortar,thecompressivestrengthincreasesatfirstandthendecreaseswhenactivatorincreasedfrom0.5to0.8.Andthematrixmaterial’scompressivestrengthis16.0MPa,drydensityis1789kg/m3,thelight-weightmortarsmallhollowblocks’compressivestrengthis9.6MPa,drydensityis1223kg/m3anditisfeasibletomeettherequirementsofMU7.5.

英文名 : Study on the Preparation of Light-weight Mortar Hollow Blocks with Granulated Blast Titanium Slag

刊期 : 2018年第5期

关键词 : 高钛矿渣膨珠；轻集料砂浆；空心砌块；压制成型

Key words : Granulated blast titanium slag; Light-weight mortar; Compressive strength; Dry density

刊期 : 2018年第5期

DOI :

文章编号 : 1000-4637（2018）05-58-05

基金项目 : 国家重点研发计划项目（2016YFC0701004）；国家自然科学基金项目（51402246）。

作者 : 罗凯1,2，李军1，卢忠远1，蒋俊1,2，白媛1,2，赵杰3

单位 : 1.西南科技大学环境友好能源材料国家重点实验室，绵阳 621010； 2.西南科技大学材料科学与工程学院，绵阳 621010； 3.攀枝花钢城集团凉山瑞海实业有限公司，615000

罗凯1,2，李军1，卢忠远1，蒋俊1,2，白媛1,2，赵杰3

罗凯,李军,卢忠远,等.高钛矿渣膨珠制备轻集料砂浆空心砌块研究[J].混凝土与水泥制品,2018(5):58-62.

LUO K,LI J,LU Z Y,et al.Study on the Preparation of Light-weight Mortar Hollow Blocks with Granulated Blast Titanium Slag[J].China Concrete and Cement Products,2018(5):58-62.





摘要

参数

结论

参考文献

引用本文

Abstract: The light-weight mortar is made by using granulated blast titanium slag as aggregate, ordinary portland cement as cementing material, desulfurized gypsum as activator, from press moulding and combined with XRD and SEM, the effect of cement content and activator content on the copressive strength and dry density of light-weight mortar are investigated. On the basis of this, the actual production of concrete hollow block is carried out. The results show that the compressive strength and dry density become stronger as the cement content increases. The change of W/C had a little effect on the dry density of light-weight mortar, the compressive strength increases at first and then decreases when activator increased from 0.5 to 0.8. And the matrix material’s compressive strength is 16.0MPa, dry density is 1789kg/m³, the light-weight mortar small hollow blocks’ compressive strength is 9.6MPa, dry density is 1223kg/m³ and it is feasible to meet the requirements of MU7.5.

关键词:

高钛矿渣膨珠；轻集料砂浆；空心砌块；压制成型

扫二维码用手机看

[1] 赵凯,齐渊洪,郭培民,等.含钛矿渣的生产及综合利用新进展[J].环境工程,2011(s1):223-226.

[2] 张则岗,王强,陈洁.钢铁厂工业废弃物的综合利用[J].新疆钢铁,2002(4):19-21.

[3] 江海民.高钛重矿渣集料制备高性能混凝土的研究与应用[D].武汉:武汉理工大学,2011.

[4] Malhotra S K,Tehri S P.Development of bricks from granu lated blast furnace slag[J].Construction & Building Materials, 1996,10(3):191-193.

[5] 潘宝风,谭克锋.新型钛矿渣砖的生产工艺研究[J].硫磷设计与粉体工程,2003(6):6-9.

[6] 潘宝风,戴亚堂.钛矿渣实心砖的制备[J].四川建筑,2003, 23(5):87-88.

[7] 谭克锋,周芝林.钛矿渣活性激发及用其生产墙体材料可行性研究[J].武汉理工大学学报,2004,26(7):31-33.

[8] 谭克锋,潘宝风,李玉香,等.利用钛矿渣生产砂浆空心砌块的可行性研究[J] 新型建筑材料 2004(8):44-45.

[9] 周芝林,谭克锋,潘宝风,等.钛矿渣混凝土空心砌块的研制[J].混凝土与水泥制品,2003(5):43-45.

[10] Liu Y, Meng F, Fang F, et al. Preparation of rutile titanium dioxide pigment from low-grade titanium slag pretreated by the NaOH molten salt method[J].Dyes & Pigments,2016,125(FEB):384-391.

[11] L. Wang, W. Liu, J. Hu, et al. Indirect mineral carbonation of titanium-bearing blast furnace slag coupled with recovery of TiO2 and Al2O3[J].Chinese. J. Chem. Eng,2017.

[12] Institute I S. The Journal of the Iron and Steel Institute[M]. The Institute,1956.

[13] 张振明,翁庆强,高艳霞,等.高钛渣用于水泥混合材的性能研究[J].硅酸盐通报,2014,33(8):1874-1879.

[14] 张建鹏,李刚,马玉薇,等.炉渣混凝土的制备及其性能研究[J]. 混凝土,2016(2):137-139.

[15] 张明聚,郭雪源,李战国,等.高性能填充轻集料混凝土试验研究[J].北京工业大学学报,2017,43(6):919-928.

[16] Vinokurov I Y, Panfilov M I, Golov G V, et al. Production of foamed titanium slag[J].Metallurgist,1976,20(3):180-182.

[17] Zhu F,Zhou Q,Wang F,et al.Spatial variability and sensiti vity analysis on the compressive strength of hollow concrete block masonry wallettes[J].Construction & Building Materials, 2017,140:129-138.

[18] Sodupe-Ortega E, Fraile-Garcia E, Ferreiro-Cabello J, et al. Evaluation of crumb rubber as aggregate for automated manufacturing of rubberized long hollow blocks and bricks[J]. Construction & Building Materials,2016,106:305-316.

[19] Poon C S, Kou S C, Lam L. Use of recycled aggregates in molded concrete bricks and blocks[J].Construction & Building Materials,2002,16(5):281-289.

[20] 冉少念,贾兴文,吴洲,等.硫酸盐对石膏复合胶凝材料水化进程的激发作用研究[J].非金属矿,2014(6):1-3.

上一个

隔震技术在框架结构轻钢加层工程中的应用

下一个

基于磁探针电感检测法检测UHPFRC中纤维的空间分布

头部文案

高钛矿渣膨珠制备轻集料砂浆空心砌块研究

相关文件