硫酸盐腐蚀钢筋混凝土板受弯力学性能的退化规律
Bending Performance Degradation Laws of Reinforced Concrete Slab Attacked by Sulfate
2012年第10期
硫酸盐腐蚀;塑性损伤模型;受弯性能;腐蚀度;承载力;挠度;延性;刚度
Sulfate corrosion; Damaged plastic model; Bending performance; Corrosion degree; Ultimate strength; Deflection; Ductility; Stiff
2012年第10期
1000-4637(2012)10-51-06
住房与城乡建设科学技术计划项目(2009-K2-3
周效国,汪俊华
1. 江苏科技大学船舶与海洋工程学院,镇江 212003; 2. 江苏科技大学土木工程与建筑学院,镇江 212003

周效国,汪俊华

浏览量:
1000
摘  要:通过大型非线性数值分析软件ABAQUS对受硫酸盐腐蚀后的钢筋混凝土板进行模拟分析,揭示了ABAQUS中塑性损伤模型进行非线性模拟的有效性以及钢筋混凝土板受腐蚀后受弯性能的退化规律。通过模拟结果和试验结果的对比,可以看出,ABAQUS非线性模拟是行之有效的。从ABAQUS模拟结果和试验结果均可看出随着腐蚀度D的增加,板的极限承载力、延性和刚度逐渐减小,其中承载力下降约3%~5%,延性下降约19%~28%,刚度下降9.96%~19.43%,而跨中挠度逐渐增大,这主要是因为随着硫酸盐的不断侵蚀,生成膨胀性物质钙矾石,板截面的损伤不断严重,使得截面的有效抗弯高度以及弹性模量降低,最终造成板的承载力、延性、刚度的降低以及跨中挠度的增大Abstract:Thelarge-scalenonlinearfiniteelementsoftwareABAQUSisusedtosimulatethereinforcedconcreteslabattackedbysulfatetorevealtheeffectivenessaboutnonlinearsimulationofdamagedplasticmodelinABAQUSandtheflexuralperformancedegradationlawsofreinforcedconcreteslabattackedbysulfate.Comparedwiththesimulationresultsandexperimentalresults,it’sfoundthattouseABAQUStosimulatenonlinearperformanceiseffective.Theultimatestrength,ductilityandstiffnessoftheseslabsgraduallydecreasewhenthecorrosiondegreeDincreases,andtheultimatestrengthdecreaseabout3%~5%,theductilitydeclinesabout19%~28%,thestiffnessdeclineabout9.96%~19.43%,meanwhilethedeflectionincreasesbecauseoftheconstanterosionofsulfate,whichresultsinmuchexpansivesubstance(Ettringite),andthecross-sectionsoftheslabcontinuetodamageseriously,allthesemaketheeffectiveflexuralheightofthecross-sectionandtheelasticmodulusdecrease,whichmaketheultimatestrength,ductility,stiffnessoftheslabsreduceandthedeflectionincreasesintheend.
英文名 : Bending Performance Degradation Laws of Reinforced Concrete Slab Attacked by Sulfate
刊期 : 2012年第10期
关键词 : 硫酸盐腐蚀;塑性损伤模型;受弯性能;腐蚀度;承载力;挠度;延性;刚度
Key words : Sulfate corrosion; Damaged plastic model; Bending performance; Corrosion degree; Ultimate strength; Deflection; Ductility; Stiff
刊期 : 2012年第10期
DOI :
文章编号 : 1000-4637(2012)10-51-06
基金项目 : 住房与城乡建设科学技术计划项目(2009-K2-3
作者 : 周效国,汪俊华
单位 : 1. 江苏科技大学船舶与海洋工程学院,镇江 212003; 2. 江苏科技大学土木工程与建筑学院,镇江 212003

周效国,汪俊华

摘要
参数
结论
参考文献
引用本文

摘   要:通过大型非线性数值分析软件ABAQUS对受硫酸盐腐蚀后的钢筋混凝土板进行模拟分析,揭示了ABAQUS中塑性损伤模型进行非线性模拟的有效性以及钢筋混凝土板受腐蚀后受弯性能的退化规律。通过模拟结果和试验结果的对比,可以看出,ABAQUS非线性模拟是行之有效的。从ABAQUS模拟结果和试验结果均可看出随着腐蚀度D的增加,板的极限承载力、延性和刚度逐渐减小,其中承载力下降约3%~5%,延性下降约19%~28%,刚度下降9.96%~19.43%,而跨中挠度逐渐增大,这主要是因为随着硫酸盐的不断侵蚀,生成膨胀性物质钙矾石,板截面的损伤不断严重,使得截面的有效抗弯高度以及弹性模量降低,最终造成板的承载力、延性、刚度的降低以及跨中挠度的增大

Abstract: The large-scale nonlinear finite element software ABAQUS is used to simulate the reinforced concrete slab attacked by sulfate to reveal the effectiveness about nonlinear simulation of damaged plastic model in ABAQUS and the flexural performance degradation laws of reinforced concrete slab attacked by sulfate. Compared with the simulation results and experimental results, it’s found that to use ABAQUS to simulate nonlinear performance is effective. The ultimate strength, ductility and stiffness of these slabs gradually decrease when the corrosion degree D increases, and the ultimate strength decrease about 3%~5%, the ductility declines about 19%~28%, the stiffness decline about 9.96%~19.43%, meanwhile the deflection increases because of the constant erosion of sulfate, which results in much expansive substance (Ettringite), and the cross-sections of the slab continue to damage seriously, all these make the effective flexural height of the cross-section and the elastic modulus decrease, which make the ultimate strength, ductility, stiffness of the slabs reduce and the deflection increases in the end.

关键词:
硫酸盐腐蚀;塑性损伤模型;受弯性能;腐蚀度;承载力;挠度;延性;刚度
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加
(1)混凝土塑性损伤模型是以混凝土受压破碎和受拉开裂为准则的,通过本文的模拟结果证明利用ABAQUS的塑性损伤模型进行混凝土的非线性模拟分析是行之有效的。
(2)混凝土的非线性分析不可避免要遇到收敛问题,一般采用位移加载方式要比力加载方式要容易得到收敛结果,通过选取合理的参数以及对诸如初始增量步大小、加载值大小的选取和模型的简化处理等手段,可得到较合理的结果。
(3)通过ABAQUS模拟结果可以看出,随着腐蚀程度D的增大,板的承载力下降约3%~5%,延性下降约19%~28%,以及刚度降低9.96%~19.43%,而跨中挠度逐渐增大,这与试验结果一致。这是因为随着侵蚀物质硫酸盐的不断渗入,产生的膨胀物质(钙矾石)造成了混凝土内部损伤的不断加深,使得构件的抗弯截面的有效承载面积减小,相当于截面的有效高度减小,以及截面刚度的减小,最终造成构件承载力的下降和跨中挠度的增加。
 
[1] 冯乃谦,邢锋.混凝土与混凝土结构的耐久性[M]. 北京:机械工业出版社,2009.
[2] 罗福午.建筑结构缺陷事故的分析与防止[M]. 北京:清华大学出版社,1996.
[3] Mehta P.K. and Burrows R.W. Building Durable Structures in the 21th century[J].Concrete   International,2001(3):45.
[4] 金伟良,赵羽习.混凝土结构耐久性研究的回顾与展望[J].浙江大学学报,2002,36(4):371-380.
[5] 王铠,庞锦娟. 论水、土中硫酸盐对混凝土结晶腐蚀的气候与评价[J]. 勘探科学技术,2007(1):34-28.
[6] 刘连新. 察尔汗盐湖及超盐渍土地区混凝土腐蚀及预防初探[J]. 建筑材料学报,2001,4(4): 395-400.
[7] 樊恒辉,陈涛,李永红,等. 定边二号隧洞混凝土腐蚀原因的初探[J]. 水利与建筑工程学报,2003,1(2):14-16.
[8] 王丽,邓思华.基于ABAQUS的混凝土梁受弯破坏实验非线性分析[J]. 土木建筑工程信息技术,2010,2(1):64-67.
[9] 刘劲松,刘红军.ABAQUS钢筋混凝土数值分析[J]. 装备制造技术,2009(6):69-70.
[10] 梁咏宁.受硫酸盐腐蚀的混凝土结构基本性能退化规律与机理研究[D]. 徐州:中国矿业大学,2005.
[11] 秦国顺.受硫酸盐侵蚀的地下结构抗力性能退化的基础研究[D].徐州:徐州工程学院,2010.
[12] 中华人民共和国建设部,国家质量监督检验检疫总局. GB 50010—2002 混凝土结构设计规范[C].北京:中国建筑工业出版社,2002.
[13] 吕西林,金国芳,吴晓涵,钢筋混凝土结构非线性理论与应用[M] .上海:同济大学出版, 1997.
[14] 王金昌,陈页开. ABAQUS在土木工程中的应用[M].杭州:浙江大学出版社,2006.
[15] 曹金凤,石亦平. ABAQUS数值分析常见问题解答[M].北京:机械工业出版社,2009.
[16] 石亦平,周玉蓉. ABAQUS数值分析实例详解[M].北京:机械工业出版社,2009.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州