基于BOTDA的混凝土管双裂缝监测试验研究
Experimental Study on Double Crack Monitoring of Concrete Pipe Based on BOTDA
2020年第7期
光纤;双裂缝;BOTDA;混凝土管
Optical fiber; Double crack; BOTDA; Concrete pipe
2020年第7期
10.19761/j.1000-4637.2020.07.043.04
国家自然科学基金重点资助项目(51739008)。
何志文1,赵新铭1,叶宇霄2 ,胡少伟2
1.南京航空航天大学,210016;2.南京水利科学研究院,210029

何志文1,赵新铭1,叶宇霄2 ,胡少伟2

何志文,赵新铭,叶宇霄,等.基于BOTDA的混凝土管双裂缝监测试验研究[J].混凝土与水泥制品,2020(7):43-46.

HE Zhi-wen,ZHAO Xin-ming,YE Yu-xiao,et al.Experimental Study on Double Crack Monitoring of Concrete Pipe Based on BOTDA[J].China Concrete and Cement Products,2020(7):43-46.

浏览量:
1000
摘  要:为研究光纤传感器在短距离内混凝土管出现多缝情况下的布里渊频移特征,设计了系列双裂缝间距的板材拉伸试验;通过试验所得布里渊频移结果得出以下结论:当双缝间距小于50mm,难以区分裂缝个数;当双缝间距大于50mm,且小于200mm时,频移图的拟合波峰区间发生了变化;当双缝间距大于200mm,频移图峰值点会发生变化,最后,通过混凝土管压力试验,验证了利用分布式光纤监测混凝土管裂缝的有效性。Abstract:InordertostudytheBrillouinfrequencyshiftcharacteristicsofopticalfibersensorinthecaseofmultiplecracksofconcretepipeinashortdistance,aseriesofplatetensiletestswithdoublecrackspacingaredesigned.TheresultsofBrillouinfrequencyshiftobtainedfromthetestsshowthatwhenthedistancebetweentwocracksislessthan50mm,itisdifficulttodistinguishthenumberofcracks.Whenthedistancebetweentwocracksisgreaterthan50mmandlessthan200mm,therangeoffittingwavepeaksofthefrequencyshiftdiagramchanges.Whenthedistancebetweenthetwojointsismorethan200mm,thepeakpointofthefrequencyshiftdiagramchanges.Theconcretepipepressuretestisdesignedtoverifythetestresultsoftheplate.
英文名 : Experimental Study on Double Crack Monitoring of Concrete Pipe Based on BOTDA
刊期 : 2020年第7期
关键词 : 光纤;双裂缝;BOTDA;混凝土管
Key words : Optical fiber; Double crack; BOTDA; Concrete pipe
刊期 : 2020年第7期
DOI : 10.19761/j.1000-4637.2020.07.043.04
文章编号 :
基金项目 : 国家自然科学基金重点资助项目(51739008)。
作者 : 何志文1,赵新铭1,叶宇霄2 ,胡少伟2
单位 : 1.南京航空航天大学,210016;2.南京水利科学研究院,210029

何志文1,赵新铭1,叶宇霄2 ,胡少伟2

何志文,赵新铭,叶宇霄,等.基于BOTDA的混凝土管双裂缝监测试验研究[J].混凝土与水泥制品,2020(7):43-46.

HE Zhi-wen,ZHAO Xin-ming,YE Yu-xiao,et al.Experimental Study on Double Crack Monitoring of Concrete Pipe Based on BOTDA[J].China Concrete and Cement Products,2020(7):43-46.

摘要
参数
结论
参考文献
引用本文

摘   要:为研究光纤传感器在短距离内混凝土管出现多缝情况下的布里渊频移特征,设计了系列双裂缝间距的板材拉伸试验;通过试验所得布里渊频移结果得出以下结论:当双缝间距小于50 mm,难以区分裂缝个数;当双缝间距大于50 mm,且小于200 mm时,频移图的拟合波峰区间发生了变化;当双缝间距大于200 mm,频移图峰值点会发生变化,最后,通过混凝土管压力试验,验证了利用分布式光纤监测混凝土管裂缝的有效性。

Abstract: In order to study the Brillouin frequency shift characteristics of optical fiber sensor in the case of multiple cracks of concrete pipe in a short distance, a series of plate tensile tests with double crack spacing are designed. The results of Brillouin frequency shift obtained from the tests show that when the distance between two cracks is less than 50 mm, it is difficult to distinguish the number of cracks. When the distance between two cracks is greater than 50 mm and less than 200 mm, the range of fitting wave peaks of the frequency shift diagram changes. When the distance between the two joints is more than 200 mm, the peak point of the frequency shift diagram changes. The concrete pipe pressure test is designed to verify the test results of the plate.

关键词:
光纤;双裂缝;BOTDA;混凝土管
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加
(1)光纤信号在较短距离内出现双裂缝情况下会受到干扰,较单一裂缝的情况呈现更离散规律。
(2)通过板材裂缝拉伸试验可以得到如下结论:光纤传感器在50 mm范围内出现两条裂缝时,频移峰值不会发生漂移;在50~200 mm内出现两条裂缝时,频移峰值会出现区间漂移;在200~250 mm内出现两条裂缝时,频移峰值会出现峰值点漂移。
(3)通过分析钢筋混凝土管道裂缝监测试验的布里渊频移数据可知:板材裂缝拉伸试验所得到的频移规律在实际管道裂缝试验中有较好体现,可以由板材试验的结论结合裂缝处频移图像特征粗略判断裂缝发展情况。
[1] 钱振东,韩光义,黄卫.BOTDA监测的钢桥面环氧沥青铺装层裂缝监测中的应用[J].东南大学学报:自然科学版,2008,38(5):79-82.
[2] 钱振东,韩光义,黄卫.基于BOTDA的钢桥面铺装裂缝疲劳扩展研究[J].土木工程学报:自然科学版,2009,42(10):132-136.
[3] 何勇,邢峰,毛江鸿,等.基于BOTDA的钢筋应力实时监测方法[J].深圳大学学报:理工版,2010,27(3):291-294.
[4] 张桂生,毛江鸿,何勇,等.基于BOTDA的隧道变形监测技术研究[J].公路,2010(2):204-208.
[5] 毛江鸿,何勇,金伟良.基于分布式传感光纤的隧道二次衬砌全寿命应力监测方法[J].中国公路学报,2011,24(2):77-82.
[6] 毛江鸿,何勇,金伟良.新型埋入式长距离应变光纤传感器研制及性能研究[J].传感技术学报,2011,24(2):190-195.
[7] 何勇,姜帅,毛江鸿,等.结构裂缝的分布式光纤监测方法及试验研究[J].土木建筑与环境工程,2012,34(1):1-6.
[8] 毛江鸿,崔磊,金伟良,等.基于分布式光纤传感的混凝土裂缝识别与监测试验研究[J].传感技术学报,2014,27(9):1298-1303.
[9] 卢毅,施斌,席均,等.基于BOTDR的地裂缝分布式光纤监测技术研究[J].工程地质学报,2014,22(1):8-13.
[10] 张宝祥.多种受力状态下结构分布式光纤传感应变传递及裂纹监测[D].哈尔滨:哈尔滨工业大学,2015.

何志文,赵新铭,叶宇霄,等.基于BOTDA的混凝土管双裂缝监测试验研究[J].混凝土与水泥制品,2020(7):43-46.

HE Zhi-wen,ZHAO Xin-ming,YE Yu-xiao,et al.Experimental Study on Double Crack Monitoring of Concrete Pipe Based on BOTDA[J].China Concrete and Cement Products,2020(7):43-46.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州