利用钢渣制备矿物掺合料对混凝土性能的影响
Preparation of Mineral Admixtures from Steel Slag and Its Effect on Concrete Performance
2020年第7期
钢渣;矿物掺合料;性能指标;混凝土;力学性能;体积稳定性;耐久性能
Steel slag; Mineral admixture; Performance index; Concrete; Mechanical property; Volume stability; Durability
2020年第7期
10.19761/j.1000-4637.2020.07.087.05
国家重点研发计划项目(2018YFC1903602-1)。
郑永超1,2,周钰沦1,2,房桂明1,2,陈旭峰1,2,吝晓然3,王 卉1,2,黄天勇1,2
1.北京建筑材料科学研究总院有限公司,100041;2.固废资源化利用与节能建材国家重点实验室,北京 100041;3.河北工程大学 土木工程学院,邯郸 075000

郑永超1,2,周钰沦1,2,房桂明1,2,陈旭峰1,2,吝晓然3,王 卉1,2,黄天勇1,2

郑永超,周钰沦,房桂明,等.利用钢渣制备矿物掺合料对混凝土性能的影响[J].混凝土与水泥制品,2020(7):87-91.

ZHENG Yong-chao,ZHOU Yu-lun,FANG Gui-ming,et al.Preparation of Mineral Admixtures from Steel Slag and Its Effect on Concrete Performance[J].China Concrete and Cement Products,2020(7):87-91.

浏览量:
1000
摘  要:为了提高钢渣的资源化利用率,利用钢渣制备了矿物掺合料,测试了钢渣粉自身的性能指标,并用钢渣粉取代矿粉配制了C30混凝土,研究了钢渣粉对混凝土力学性能、体积稳定性和耐久性能的影响。结果表明,钢渣粉的掺入可降低胶凝材料体系的总水化热,但对外加剂饱和掺量点和经时损失率影响较大。利用钢渣粉取代矿粉对混凝土的出机工作性影响不大;随着钢渣粉掺量的增多,混凝土的早期强度低,后期强度增进量较大;掺钢渣粉混凝土的收缩率、氯离子渗透系数及碳化深度均高于基准组;将钢渣粉作为矿物掺合料配制混凝土时需控制其掺量。Abstract:Inordertoimprovetheresourceutilizationofsteelslag,thesteelslagwasusedtopreparemineraladmixture,andtheperformanceindexofsteelslagpowderwastested,andC30concretewaspreparedbyusingsteelslagpowderinsteadofmineralpowder,anditseffectonmechanicalproperties,volumestabilityanddurabilityofconcretewasstudied.Theresultsshowthattheincorporationofsteelslagpowdercanreducethetotalhydrationheatofcementitiousmaterialsystem,butithasagreatinfluenceonthesaturationdosagepointandthelossrateoffluidityovertime.Usingsteelslagpowderinsteadofmineralpowderhaslittleeffectontheperformanceoffreshconcrete.Withtheincreaseoftheamountofsteelslagpowder,theearlystrengthofconcreteislow,andthelaterstrengthincreasesgreatly.Theshrinkage,chlorideionpermeabilitycoefficientandcarbonizationdepthofthesteelslagpowderconcretearehigherthanthoseofthecomparativesample.Whenthesteelslagpowderisusedasamineraladmixturetoprepareconcrete,itisnecessarytocontrolitscontent.
英文名 : Preparation of Mineral Admixtures from Steel Slag and Its Effect on Concrete Performance
刊期 : 2020年第7期
关键词 : 钢渣;矿物掺合料;性能指标;混凝土;力学性能;体积稳定性;耐久性能
Key words : Steel slag; Mineral admixture; Performance index; Concrete; Mechanical property; Volume stability; Durability
刊期 : 2020年第7期
DOI : 10.19761/j.1000-4637.2020.07.087.05
文章编号 :
基金项目 : 国家重点研发计划项目(2018YFC1903602-1)。
作者 : 郑永超1,2,周钰沦1,2,房桂明1,2,陈旭峰1,2,吝晓然3,王 卉1,2,黄天勇1,2
单位 : 1.北京建筑材料科学研究总院有限公司,100041;2.固废资源化利用与节能建材国家重点实验室,北京 100041;3.河北工程大学 土木工程学院,邯郸 075000

郑永超1,2,周钰沦1,2,房桂明1,2,陈旭峰1,2,吝晓然3,王 卉1,2,黄天勇1,2

郑永超,周钰沦,房桂明,等.利用钢渣制备矿物掺合料对混凝土性能的影响[J].混凝土与水泥制品,2020(7):87-91.

ZHENG Yong-chao,ZHOU Yu-lun,FANG Gui-ming,et al.Preparation of Mineral Admixtures from Steel Slag and Its Effect on Concrete Performance[J].China Concrete and Cement Products,2020(7):87-91.

摘要
参数
结论
参考文献
引用本文

摘   要:为了提高钢渣的资源化利用率,利用钢渣制备了矿物掺合料,测试了钢渣粉自身的性能指标,并用钢渣粉取代矿粉配制了C30混凝土,研究了钢渣粉对混凝土力学性能、体积稳定性和耐久性能的影响。结果表明,钢渣粉的掺入可降低胶凝材料体系的总水化热,但对外加剂饱和掺量点和经时损失率影响较大。利用钢渣粉取代矿粉对混凝土的出机工作性影响不大;随着钢渣粉掺量的增多,混凝土的早期强度低,后期强度增进量较大;掺钢渣粉混凝土的收缩率、氯离子渗透系数及碳化深度均高于基准组;将钢渣粉作为矿物掺合料配制混凝土时需控制其掺量。

Abstract: In order to improve the resource utilization of steel slag, the steel slag was used to prepare mineral admixture, and the performance index of steel slag powder was tested, and C30 concrete was prepared by using steel slag powder instead of mineral powder, and its effect on mechanical properties, volume stability and durability of concrete was studied. The results show that the incorporation of steel slag powder can reduce the total hydration heat of cementitious material system, but it has a great influence on the saturation dosage point and the loss rate of fluidity over time. Using steel slag powder instead of mineral powder has little effect on the performance of fresh concrete. With the increase of the amount of steel slag powder, the early strength of concrete is low, and the later strength increases greatly. The shrinkage, chloride ion permeability coefficient and carbonization depth of the steel slag powder concrete are higher than those of the comparative sample. When the steel slag powder is used as a mineral admixture to prepare concrete, it is necessary to control its content.

关键词:
钢渣;矿物掺合料;性能指标;混凝土;力学性能;体积稳定性;耐久性能
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加
(1)钢渣粉的比表面积为420 m2/kg,28 d活性指数达到75%,流动度比达到95%,沸煮法安定性合格,6 h压蒸膨胀率为0.04%,符合二级钢渣粉的指标要求。
(2)矿粉、粉煤灰和钢渣粉的掺入均能降低胶凝材料体系的总水化热,不同胶凝体系7 d的总放热量大小依次为100%水泥>70%水泥+30%矿粉>70%水泥+30%粉煤灰>70%水泥+30%钢渣粉。
(3)复掺水泥、粉煤灰和矿粉胶凝体系的外加剂饱和掺量点与纯水泥胶凝体系基本一致,随着钢渣粉替代矿粉的比例增大,外加剂饱和掺量随之升高,且对经时损失影响较大。
(4)随着钢渣粉掺量的增多,混凝土早期强度发展较慢,28 d抗压强度均达到C30强度等级要求,掺钢渣粉混凝土的后期强度增进量较大。
(5)掺钢渣粉混凝土的收缩率较基准组大,抗氯离子渗透性能和抗碳化性能较基准组差。在使用钢渣粉配制混凝土时,应综合考虑以上因素影响,控制钢渣粉掺量。
[1] 刘长波,彭犇,夏春,等.钢渣利用及稳定化技术研究进展[J].矿产保护与利用,2018(6):145-150.
[2] 张亮亮,田广银,蒲克元,等.钢渣改性研究进展[C].中国节能环保科技成果集,2015:151-154.
[3] 赵海晋,余其俊,韦江雄,等.组成和温度对重构钢渣结构及早期水化活性的影响[J].建筑材料学报,2012(3):399-405.
[4] LI L L,ZHAO F Q,LIU S J.The Activation of Steel Slag and its Application in Construction and Building Materials[J].Advanced Materials Research,2014,884-885:702-705.
[5] QIN S W,SHEN J J,WANG H F,et al.Utilization of Blast Furnace Slag, Steel Slag in the Production of Clinker[J].Materials Science Forum,2013,743-744:334-338.
[6] 赵计辉,阎培渝.钢渣的体积安定性问题及稳定化处理的国内研究进展[J].硅酸盐通报,2017(2):477-484.
[7] 王毓.钢渣活性激发及其在水泥基材料中的应用研究[D].淮南:安徽理工大学,2018.
[8] 李泽理,李葆生,吕进锋.钢渣处理工艺与装备的现状与创新[J].矿山机械,2016,44(2):1-6.
[9] 孟振亚,刘加平,刘建忠,等.矿物掺和料的掺入对混凝土抗氯离子渗透性能影响的评价与研究[J].混凝土,2010(7):28-30+33.
[10] 刘静,王元纲.含钢渣复合掺和料对高性能混凝土抗氯离子渗透性能的影响[J].混凝土与水泥制品,2013(8):9-12.
[11] 王爱国,何懋灿,莫立武,等.碳化养护钢渣制备建筑材料的研究进展[J].材料导报,2019,33(17):2939-2948.

郑永超,周钰沦,房桂明,等.利用钢渣制备矿物掺合料对混凝土性能的影响[J].混凝土与水泥制品,2020(7):87-91.

ZHENG Yong-chao,ZHOU Yu-lun,FANG Gui-ming,et al.Preparation of Mineral Admixtures from Steel Slag and Its Effect on Concrete Performance[J].China Concrete and Cement Products,2020(7):87-91.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州