钢纤维取向角对超高性能混凝土抗拉强度的影响

The Effects of Steel Fiber Orientation on Tensile Strength of Ultra-high Performance Concrete

２０19年第1期

超高性能混凝土；抗拉强度；浇筑方向；增韧；钢纤维取向角

Ultra-high performance concrete; Tensile strength; Pouring direction; Toughening; Steel fiber orientation

２０19年第1期

10.19761/j.1000-4637.2019.01.051.04

王强

上海市市政规划设计研究院有限公司，200031

王强

王强.钢纤维取向角对超高性能混凝土抗拉强度的影响[J].混凝土与水泥制品,2019(1):51-54.

WANG Q.The Effects of Steel Fiber Orientation on Tensile Strength of Ultra-high Performance Concrete[J].China Concrete and Cement Products,2019(1):51-54.

浏览量:

1000

摘要：为了明确钢纤维在超高性能混凝土（UHPC）中的增韧效果，人为改变钢纤维在UHPC拌合物中的排列取向。采用随机浇筑、顺拉伸方向浇筑、垂直拉伸方向浇筑三种成型模式成型了UHPC拉伸试件，通过轴拉试验得到UHPC的应力-应变曲线，并从断面观测钢纤维的分布取向。试验结果表明，钢纤维的取向对拉伸强度有决定性影响，其中，顺拉伸方向浇筑的UHPC抗拉强度达到12.4MPa，极限应变达到了0.0038；从拉伸断面上分析得出UHPC的抗拉强度与钢纤维沿轴向取向角有线性相关性。Abstract:Inordertoclarifythetougheningeffectofsteelfiberinultra-highperformanceconcrete(UHPC),theorientationofsteelfiberinUHPCmixturewaschangedartificiallybychangingthepouringdirectionofUHPC.Thetensiletestonshapespecimenswasformedbythreekindsofmoldingmodels:randompouring,indirectionofstretchingandverticaldirection.Thestress-straincurveofUHPCwasobtainedbyaxialtensiletest,andthedistributionorientationofsteelfiberwasobservedfromthecrosssection.Thetestresultsshowthattheorientationofsteelfiberhasadecisiveinfluenceonthetensilestrength.Especially，thetensilestrengthofUHPCisupto12.4MPaalongthedirectionofpouring,andtheultimatestrainreaches0.0038.Fromtheanalysisofthetensilesection,itisconcludedthatthetensilestrengthofUHPCislinearlyrelatedtotheorientationangleofthesteelfiber.

英文名 : The Effects of Steel Fiber Orientation on Tensile Strength of Ultra-high Performance Concrete

刊期 : ２０19年第1期

关键词 : 超高性能混凝土；抗拉强度；浇筑方向；增韧；钢纤维取向角

Key words : Ultra-high performance concrete; Tensile strength; Pouring direction; Toughening; Steel fiber orientation

刊期 : ２０19年第1期

DOI : 10.19761/j.1000-4637.2019.01.051.04

文章编号 :

基金项目 :

作者 : 王强

单位 : 上海市市政规划设计研究院有限公司，200031

王强

王强.钢纤维取向角对超高性能混凝土抗拉强度的影响[J].混凝土与水泥制品,2019(1):51-54.

WANG Q.The Effects of Steel Fiber Orientation on Tensile Strength of Ultra-high Performance Concrete[J].China Concrete and Cement Products,2019(1):51-54.





摘要

参数

结论

参考文献

引用本文

摘要：为了明确钢纤维在超高性能混凝土（UHPC）中的增韧效果，人为改变钢纤维在UHPC拌合物中的排列取向。采用随机浇筑、顺拉伸方向浇筑、垂直拉伸方向浇筑三种成型模式成型了UHPC拉伸试件，通过轴拉试验得到UHPC的应力-应变曲线，并从断面观测钢纤维的分布取向。试验结果表明，钢纤维的取向对拉伸强度有决定性影响，其中，顺拉伸方向浇筑的UHPC抗拉强度达到12.4 MPa，极限应变达到了0.003 8；从拉伸断面上分析得出UHPC的抗拉强度与钢纤维沿轴向取向角有线性相关性。

Abstract: In order to clarify the toughening effect of steel fiber in ultra-high performance concrete (UHPC), the orientation of steel fiber in UHPC mixture was changed artificially by changing the pouring direction of UHPC. The tensile test on shape specimens was formed by three kinds of molding models: random pouring, in direction of stretching and vertical direction. The stress-strain curve of UHPC was obtained by axial tensile test, and the distribution orientation of steel fiber was observed from the cross section. The test results show that the orientation of steel fiber has a decisive influence on the tensile strength. Especially，the tensile strength of UHPC is up to 12.4 MPa along the direction of pouring, and the ultimate strain reaches 0.003 8. From the analysis of the tensile section, it is concluded that the tensile strength of UHPC is linearly related to the orientation angle of the steel fiber.

关键词:

超高性能混凝土；抗拉强度；浇筑方向；增韧；钢纤维取向角

扫二维码用手机看

[1] 夏骏,Chee Chin,徐晓明,等.超高性能纤维混凝土空心配筋板抗弯承载力研究[J].混凝土与水泥制品,2017(9):44-47.

[2] 赵士豪,林喜华,车玉君,等.基于DE响应面分析的C100超高性能混凝土配合比优化设计[J].混凝土与水泥制品,2018(8):24-28.

[3] 阎培渝.超高性能混凝土（UHPC）的发展与现状[J].混凝土世界,2010(9):36-41.

[4] 赵筠,廉慧珍,金建昌.钢-混凝土复合的新模式——超高性能混凝土（UHPC/UHPFRC）之二：配制、生产与浇筑及水化硬化与微观结构和力学性能[J].混凝土世界,2013(11):60-71.

[5] 王俊颜 ,耿莉萍,郭君渊,等. UHPC的轴拉性能与裂缝宽度控制能力研究[J].哈尔滨工业大学学报,2017(12):165-169.

[6] 张哲,邵旭东,李文光,等.超高性能混凝土轴拉性能试验[J].中国公路学报,2015(8):50-58.

[7] 朋改非,牛旭婧,赵怡琳.异形钢纤维对超高性能混凝土增强增韧的影响[J].建筑材料学报,2016(6):1013-1018.

[8] Liberato Ferrara. High mechanical performance of fibre reinforced cementitious composites: the role of“casting-flow induced”fibre orientation[J]. Materials and Structures,2011(44):109-128.

[9] KANG S T，KIM J.The relation between fiber orientation and tensile behavior in an ultra-high performance fiber reinforced cementitious composites（UHPFRCC）[J].Cement and Concrete Reseach，2011,41(10):1001-1014.

[10] Kang S T，Kim J K. Investigation on the flexural behavior of UHPCC considering the effect of fiber orientation distribution[J]. Constr Build Mater,2012,28(1):57.

[11] 张倩倩，刘建忠等.超高性能混凝土流变特性及其对纤维分散性的影响[J].材料导报,2017,12(A):73-77.

[12] 慕儒,邱欣,赵全明,等.单向分布钢纤维增强水泥基复合材料(Ⅰ)钢纤维方向控制[J].建筑材料学报,2015,18(2):208-213.

[13] 慕儒,马艳奉,李辉,等.定向钢纤维混凝土中的钢纤维分布X-ray CT分析[J].电子显微学报,2015,34(6):487-491.

上一个

钢纤维搭配对超高性能混凝土拌合物性能的影响

下一个

孔隙结构对玄武岩纤维混凝土力学性能的影响研究

头部文案

钢纤维取向角对超高性能混凝土抗拉强度的影响

相关文件