钢筋锈蚀对混凝土梁抗剪性能的影响
Influence of Steel Corrosion on the Shearing Performance of RC Beams
２００5年第4期
钢筋混凝土梁；钢筋锈蚀；箍筋；抗剪承载力；安全性；耐久性
Reiuforced concrete beam; Corrosion of steel bar; Stirrup; Shear-bearing capacity; Safety; Durability
２００5年第4期
1000-4637（2005）04-04-03
倪国荣1，戎冠纶2
1. 浙江大学结构工程研究所， 杭州 310027；2. 中港三航浦东分公司，上海 200137

倪国荣1，戎冠纶2

浏览量:
1000
摘 要：钢筋锈蚀是混凝土构件主要病害之一。与梁底纵筋相比，箍筋易首先腐蚀，且腐蚀程度更为严重。本文在研究锈蚀RC构件抗剪承载力衰减模型的基础上，借助Monte Carlo模拟，分析了钢筋锈蚀对RC梁抗剪承载力的影响。结果表明，箍筋的锈蚀率明显大于纵筋，构件抗剪失效的可能性大大增加，对梁的安全性和耐久性具有潜在危害。 Abstract: The corrosion of steel bar is a grave faults for RC menbers. Compared with longitudinal bars at the bottom of beams, the stirrups are usually corroded at the first and the corrosion degree is more serious. Based on investigation of the model of declinning of shear-bearing capacity of corroded RC beams, and by means of Monte Carlo simulation, the influence of corrosion on shearing capacity of RC beams is analysed. The rezults show that the corrosion rate of stirraps is obviously larger than that of longitudinal bars, and the possibility of failure by shearing is greatly increased. That will potentially endanger to safety and durability of RC beams.
英文名 : Influence of Steel Corrosion on the Shearing Performance of RC Beams
刊期 : ２００5年第4期
关键词 : 钢筋混凝土梁；钢筋锈蚀；箍筋；抗剪承载力；安全性；耐久性
Key words : Reiuforced concrete beam; Corrosion of steel bar; Stirrup; Shear-bearing capacity; Safety; Durability
刊期 : ２００5年第4期
DOI :
文章编号 : 1000-4637（2005）04-04-03
基金项目 :
作者 : 倪国荣1，戎冠纶2
单位 : 1. 浙江大学结构工程研究所， 杭州 310027；2. 中港三航浦东分公司，上海 200137

倪国荣1，戎冠纶2

摘要
参数
结论
参考文献
引用本文

摘   要：钢筋锈蚀是混凝土构件主要病害之一。与梁底纵筋相比，箍筋易首先腐蚀，且腐蚀程度更为严重。本文在研究锈蚀RC构件抗剪承载力衰减模型的基础上，借助Monte Carlo模拟，分析了钢筋锈蚀对RC梁抗剪承载力的影响。结果表明，箍筋的锈蚀率明显大于纵筋，构件抗剪失效的可能性大大增加，对梁的安全性和耐久性具有潜在危害。

Abstract: The corrosion of steel bar is a grave faults for RC menbers. Compared with longitudinal bars at the bottom of beams, the stirrups are usually corroded at the first and the corrosion degree is more serious. Based on investigation of the model of declinning of shear-bearing capacity of corroded RC beams, and by means of Monte Carlo simulation, the influence of corrosion on shearing capacity of RC beams is analysed. The rezults show that the corrosion rate of stirraps is obviously larger than that of longitudinal bars, and the possibility of failure by shearing is greatly increased. That will potentially endanger to safety and durability of RC beams.

关键词:
钢筋混凝土梁；钢筋锈蚀；箍筋；抗剪承载力；安全性；耐久性
扫二维码用手机看
未找到相应参数组，请于后台属性模板中添加
（1）箍筋的锈蚀率明显高于梁底纵筋。从而较大地削弱了由混凝土和抗剪钢筋提供的剪切抗力，导致抗剪承载力随时间降低较快。
（2）剪切破坏失效概率比弯曲破坏失效率随时间而增加得更快。剪切破坏属于脆性破坏，对于抗剪性能富余量不足的构件，随着时间的增长，失效模式可能会发生转变，从弯曲破坏转变为剪切破坏，这对构件的安全性具有很大影响。因此，对于在侵蚀环境下使用的RC构件，其抗剪性能的衰减是必须考虑的。
[1] 金伟良，赵羽习，混凝土结构耐久性，科学出版社，2002.9
[2] J Rodriguez ,L M Ortega ,J Casal ,Load carrying capacity of concrete structures with corroded reinforcement , Construction and Building Materials ,Vol.11 ,No.4：239-248 ,1997
[3] 田瑞华，颜桂云，孙炳楠. 锈蚀钢筋混凝土构件抗剪承载力的试验研究与理论分析. 四川建筑科学研究，2003，29(3)
[4] 张平生，卢梅. 锈蚀钢筋的力学性能. 工业建筑，1995，25(9)
[5] Dimitri V. Val ,Mark G. Stewart ,Robert E. Melchers ,Effect of reinforcement corrosion on reliability of highway bridges ,Engineering Structures ,Vol.20,No.11：1010-1019,1998
[6] 牛荻涛，卢梅，王庆霖. 锈蚀钢筋混凝土梁正截面受弯承载力计算方法研究. 建筑结构，2002，33(10)
[7] T.Liu ,R.W.Weyers ,Modeling the dynamic corrosion process in chloride contaminated concrete structures ,Cement and Concrete Research ,Vol.28 ,No.3：365-379 ,1998
上一个
用Fick第二定律描述混凝土中氯离子浓度分布的适用性
下一个
混合材对碱-硅反应的作用 I.混合材对碱-硅反应膨胀的作用

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设：中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设：中企动力 苏州