玄武岩纤维对超高强混凝土力学性能的影响
Influence of Basalt Fiber on Mechanical Performance of Ultra-high- strength Concrete
2019年第2期
超高强混凝土;玄武岩纤维;力学性能
Ultra-high-strength concrete; Basalt fiber; Mechanical property
2019年第2期
10.19761/j.1000-4637.2019.02.052.04
国家自然科学基金项目(51408449);福建省重点技术基金项目(2014Y0071);福建省自然科学基金项目(2011 J01327);莆田学院校内项目(2018020、2018092)。
杨智硕,陈明霞,叶梅新
1.莆田学院土木工程学院,351100;2.中南大学土木工程学院,长沙 410083

杨智硕,陈明霞,叶梅新

杨智硕,陈明霞,叶梅新.玄武岩纤维对超高强混凝土力学性能的影响[J].混凝土与水泥制品,2019(2):52-55.

YANG Z S,CHEN M X,YE M X.Influence of Basalt Fiber on Mechanical Performance of Ultra-highstrength Concrete[J].China Concrete and Cement Products,2019(2):52-55.

浏览量:
1000
摘  要:选用玄武岩纤维作为超高强混凝土(UHSC)的外掺料,研究其在不同掺量下对UHSC的力学性能的影响。通过试验考察了各配合比下的立方体抗压强度、棱柱体抗压强度、抗折强度、劈裂抗拉强度,分析了玄武岩纤维掺量对各项指标的影响。结果表明:玄武岩纤维对立方体抗压强度、棱柱体抗压强度、抗折强度和劈裂抗拉强度均有提高作用,尤其当玄武岩纤维掺量为2kg/m3时,以上各项指标分别提高了10.9%、14.1%、10.2%、11.0%。Abstract:Usingbasaltfiberasanadmixtureofultra-highstrengthconcrete(UHSC),theinfluenceonthemechanicalpropertiesofUHSCunderdifferentcontentwasstudied.Thecubiccompressivestrength,prismcompressivestrength,flexuralstrengthandsplittingtensilestrengthunderdifferentmixproportionswereconductedbyexperiments,theeffectsofcontentofbasaltfiberonindexeswereanalyzed.Theresultsshowthattheperformancesofcubiccompressivestrength,prismcompressivestrength,flexuralstrengthandsplittingtensilestrengthwereimprovedbybasaltfiber,whenthecontentofbasaltfiberwas2kg/m3,theindexeswereincreasedby10.9%,14.1%,10.2%and11%,respectively.
英文名 : Influence of Basalt Fiber on Mechanical Performance of Ultra-high- strength Concrete
刊期 : 2019年第2期
关键词 : 超高强混凝土;玄武岩纤维;力学性能
Key words : Ultra-high-strength concrete; Basalt fiber; Mechanical property
刊期 : 2019年第2期
DOI : 10.19761/j.1000-4637.2019.02.052.04
文章编号 :
基金项目 : 国家自然科学基金项目(51408449);福建省重点技术基金项目(2014Y0071);福建省自然科学基金项目(2011 J01327);莆田学院校内项目(2018020、2018092)。
作者 : 杨智硕,陈明霞,叶梅新
单位 : 1.莆田学院土木工程学院,351100;2.中南大学土木工程学院,长沙 410083

杨智硕,陈明霞,叶梅新

杨智硕,陈明霞,叶梅新.玄武岩纤维对超高强混凝土力学性能的影响[J].混凝土与水泥制品,2019(2):52-55.

YANG Z S,CHEN M X,YE M X.Influence of Basalt Fiber on Mechanical Performance of Ultra-highstrength Concrete[J].China Concrete and Cement Products,2019(2):52-55.

摘要
参数
结论
参考文献
引用本文
摘   要:选用玄武岩纤维作为超高强混凝土(UHSC)的外掺料,研究其在不同掺量下对UHSC的力学性能的影响。通过试验考察了各配合比下的立方体抗压强度、棱柱体抗压强度、抗折强度、劈裂抗拉强度,分析了玄武岩纤维掺量对各项指标的影响。结果表明:玄武岩纤维对立方体抗压强度、棱柱体抗压强度、抗折强度和劈裂抗拉强度均有提高作用,尤其当玄武岩纤维掺量为2 kg/m3时,以上各项指标分别提高了10.9%、14.1%、10.2%、11.0%。
Abstract: Using basalt fiber as an admixture of ultra-high strength concrete (UHSC), the influence on the mechanical properties of UHSC under different content was studied. The cubic compressive strength, prism compressive strength, flexural strength and splitting tensile strength under different mix proportions were conducted by experiments, the effects of content of basalt fiber on indexes were analyzed. The results show that the performances of cubic compressive strength, prism compressive strength, flexural strength and splitting tensile strength were improved by basalt fiber, when the content of basalt fiber was 2 kg/m3, the indexes were increased by 10.9%, 14.1%, 10.2% and 11%, respectively.
关键词:
超高强混凝土;玄武岩纤维;力学性能
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加
(1) UHSC立方体抗压强度和棱柱体抗压强度分别超过了120 MPa和85 MPa;抗折强度为7.3~11.2 MPa;劈裂抗拉强度为5.5~8.76 MPa;即各项力学性能指标可达到C120的要求。
(2)玄武岩纤维的掺入对UHSC立方体抗压强度、棱柱体抗压强度、抗折强度和劈裂抗拉强度都有较大幅度的提高,其中,掺入2 kg/m3的玄武岩纤维UHSC力学性能提高尤为明显,可将以上各项指标分别提高10.9%、14.1%、10.2%、11.0%。 
(3)经过对两大组,8种配合比,每种配合比3个不同玄武岩纤维掺量试件的各种力学性能综合比较可得,配合比编号为8B,即灰骨比0.366,水胶比0.22,玄武岩纤维为2 kg/m3时,UHSC的各项力学性能指标最优。
[1] 姜睿.超高强混凝土组合柱抗震性能的试验研究[D].大连: 大连理工大学,2007.
[2] 张志豪,余睿,水中和,等.生态型超高强混凝土的制备与性能研究[J].混凝土与水泥制品,2018(1):1-5,16.
[3] 蒲心诚,王冲,王志军,等.C100~C150超高强高性能混凝土的强度及变形性能研究[J].混凝土,2002(10):3-7,33.
[4] 齐建林,朱江.玄武岩纤维在混凝土中的应用与研究进展[J].混凝土,2011(7):46-49.
[5] 薛军鹏.连续玄武岩纤维混凝土技术研究进展及应用[J]. 福建建筑,2009(12):36-38.
[6] 吴钊贤.玄武岩纤维混凝土基本力学性能与应用研究[D]. 武汉:武汉理工大学,2009.
[7] Jongsung sim C P D Y M. Characteristics of basalt fiber as a strength[J].Composites:Part B,2005(36):504-512.
[8] Dylmar penteadodias Cleio-Thaumatuigo. Fracturetoughness  of  geopolymeric  concretes reinforced with basalt fibers[J]. Cement And Conerete Composites,2005(27): 49-54.
[9] 钟耀海.钢管玄武岩纤维混凝土短柱基本力学性能试验研究与经济效果评价[D].天津:天津城建大学,2014.
[10] 王钧,马跃,张野,等.短切玄武岩纤维混凝土力学性能试验与分析[J].工程力学,2014,31(S1):99-102,114.
[11] 成涛华,李玉香.玄武岩纤维增强混凝土力学性能研究[J].混凝土与水泥制品,2017(1):53-56.
[12] 王海良,袁磊,宋浩.短切玄武岩纤维混凝土力学性能试验研究[J].建筑结构,2013,43(S2):562-564.
[13] 张野.短切玄武岩纤维混凝土基本力学性能研究[D].哈尔滨:东北林业大学,2011.
[14] 张兰芳,尹玉龙,刘晶伟,等.玄武岩纤维增强混凝土力学性能的研究[J].硅酸盐通报,2014,33(11):2834-2837.

杨智硕,陈明霞,叶梅新.玄武岩纤维对超高强混凝土力学性能的影响[J].混凝土与水泥制品,2019(2):52-55.

YANG Z S,CHEN M X,YE M X.Influence of Basalt Fiber on Mechanical Performance of Ultra-highstrength Concrete[J].China Concrete and Cement Products,2019(2):52-55.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州