机制砂物理特性对高强混凝土工作性能和强度的影响[J].混凝土与水泥制品
The Influence on Workability and Strength of Physical Characteristic of High-strength Concrete
2018年第8期
机制砂;高强混凝土; 石粉含量;工作性能;抗压强度
Manufactured sand; High-strength concrete; Stone powder; Workability; Compressive strength
2018年第8期
1000-4637(2018)08-93-04
深圳市科技研发资金基础研究项目(JCYJ2016033 1114415945、JCYJ20150324141711689)
李振怀,甘洋宇,管民生,杜宏彪
深圳大学土木工程学院,518060

李振怀,甘洋宇,管民生,杜宏彪

浏览量:
1000
摘 要:以原料形态为石灰石和卵石的两种机制砂作细骨料,通过配合比设计,研制出了 C60、C80、C100 机制砂高强混凝土,研究了机制砂原料形态以及不同石粉含量(3%、5%、7%、10%)对高强机制砂混凝土工作性能和抗压强度的影响。结果表明,机制砂原料形态对高强机制砂混凝土工作性能和抗压强度影响较为显著;石粉含量对高强机制砂混凝土工作性能影响较大,对强度影响较小;石粉含量小于等于7%时,两种原料形态的高强机制砂混凝土均具有良好的工作性能与力学性能,满足结构设计要求,研究结果可为工程实际应用提供参考。 Abstract: The high-strength manufactured sand concrete with strength grades of C60, C80 and C100 are prepared by using concrete mix design methods. Two forms of raw materials,i.e., pebbles and limestone are adopted. Further, the effect of two key factors associated with raw materials of manufactured sands and contents(3%,5%,7%,10%)of stone powder on workability as well as compressive strength of manufactured sand concrete is investigated. The results show that the raw materials of manufactured sands have significant effects on the workability and compressive strength of high-strength concrete. The contents of stone powder have strong effect on the working performance of high-strength manufactured sand concrete, while small effects on its compressive strength. When the content of stone powder is less than or equal to 7%, the high-strength manufactured sand concrete with two kinds of raw materials has good workability and mechanical properties, and can meet the requirements of structural design. The results can provide reference for practical use.
英文名 : The Influence on Workability and Strength of Physical Characteristic of High-strength Concrete
刊期 : 2018年第8期
关键词 : 机制砂;高强混凝土; 石粉含量;工作性能;抗压强度
Key words : Manufactured sand; High-strength concrete; Stone powder; Workability; Compressive strength
刊期 : 2018年第8期
DOI :
文章编号 : 1000-4637(2018)08-93-04
基金项目 : 深圳市科技研发资金基础研究项目(JCYJ2016033 1114415945、JCYJ20150324141711689)
作者 : 李振怀,甘洋宇,管民生,杜宏彪
单位 : 深圳大学土木工程学院,518060

李振怀,甘洋宇,管民生,杜宏彪

摘要
参数
结论
参考文献
引用本文

摘   要:以原料形态为石灰石和卵石的两种机制砂作细骨料,通过配合比设计,研制出了 C60、C80、C100 机制砂高强混凝土,研究了机制砂原料形态以及不同石粉含量(3%、5%、7%、10%)对高强机制砂混凝土工作性能和抗压强度的影响。结果表明,机制砂原料形态对高强机制砂混凝土工作性能和抗压强度影响较为显著;石粉含量对高强机制砂混凝土工作性能影响较大,对强度影响较小;石粉含量小于等于7%时,两种原料形态的高强机制砂混凝土均具有良好的工作性能与力学性能,满足结构设计要求,研究结果可为工程实际应用提供参考。

Abstract: The high-strength manufactured sand concrete with strength grades of C60, C80 and C100 are prepared by using concrete mix design methods. Two forms of raw materials,i.e., pebbles and limestone are adopted. Further, the effect of two key factors associated with raw materials of manufactured sands and contents(3%,5%,7%,10%)of stone powder on workability as well as compressive strength of manufactured sand concrete is investigated. The results show that the raw materials of manufactured sands have significant effects on the workability and compressive strength of high-strength concrete. The contents of stone powder have strong effect on the working performance of high-strength manufactured sand concrete, while small effects on its compressive strength. When the content of stone powder is less than or equal to 7%, the high-strength manufactured sand concrete with two kinds of raw materials has good workability and mechanical properties, and can meet the requirements of structural design. The results can provide reference for practical use.

关键词:
机制砂;高强混凝土
石粉含量;工作性能;抗压强度
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加
(1)机制砂原料形态对高强机制砂混凝土工作性能和抗压强度影响较显著。卵石原料形态高强机制砂混凝土工作性能较好,而在石粉含量小于10%时,石灰石原料形态的机制砂混凝土强度略大于卵石原料形态机制砂混凝土,当石粉含量大于等于10%时,两者强度接近。
(2)石粉对机制砂混凝土拌合物的工作性能有较大的影响。随着石粉含量的增加,高强机制砂混凝土的坍落度和坍落扩展度均呈下降趋势,当石粉含量增加到10%时,C60机制砂混凝土不离析、不泌水,工作性能最佳;而C80、C100机制砂混凝土则在石粉含量分别为7%和3%时,具有较好的工作性。
(3)石粉对高强机制砂混凝土抗压强度作用较小。随着石粉含量的增加,C60机制砂混凝土强度略有提高,C80和C100机制砂混凝土强度则略微下降。当石粉含量分别为10%、3%、3%时,C60、C80、C100机制砂混凝土的抗压强度达到最大值。
(4)两种不同原料形态的机制砂高强混凝土都有优良的工作性能和抗压强度,具有适量石粉的机制砂可完全代替天然砂作为细骨料用于实际工程。
[1] 潘菲.机制砂应用技术研究进展[J].粉煤灰综合利用,2016(3):61-64.
[2] 江京平.《建筑用砂》(GB/T 14684—2001)内容概要与人工砂应用前景展望[J].建筑技术,2003,34(1):54-56.
[3] 蒋正武,任启欣,吴建林,等.机制砂特性及其在混凝土中应用的相关问题研究[J].新型建筑材料,2010(11):1-4.
[4] 杨家伟,李固华,于春辉,等.石粉对低强度机制砂混凝土和易性的影响[J].四川建筑科学研究,2015,41(1):230-233.
[5] 王玲,田培,白杰,等.我国混凝土减水剂的现状及未来[J]. 混凝土与水泥制品,2008(5):1-7.
[6] 闵婕,韩静云,宋旭艳.机制砂对新拌混凝土工作性影响及减水剂对其适应性研究[J].混凝土与水泥制品,2014(10):16-20.
[7] 张礼华,刘来宝,周永生,等.石粉含量对机制砂混凝土力学性能与微观结构的影响[J].混凝土与水泥制品,2011(12):22-26.
[8] 蒋正武,石连富,孙振平.用机制砂配制自密实混凝土的研究[J].建筑材料学报,2007,10(2):154-160.
[9] 中华人民共和国建设部.GB/T 50081—2002 普通混凝土力学性能试验方法标准[S].北京:中国建筑工业出版社,2003.
[10] 李北星,周明凯,蔡基伟,等.机制砂中石粉对不同强度等级混凝土性能的影响研究[J].混凝土,2008(7):51-54,57.
[11] 陈飚,王稷良,杨玉辉,等.石粉含量对C80机制砂混凝土性能的影响[J].武汉理工大学学报,2007,29(8):41-43.
[12] 范德科,马强,周宗辉,等.石粉对机制砂混凝土性能的影响[J].硅酸盐通报,2016,35(3):913-917.
[13] Choi S.J.,Jun S.S.,Oh J.E.,et al.Properties of alkali-activ ated systems with stone powder sludge[J]. Journal of Material Cycles & Waste Management,2010,12(4):275-282.
[14] 赵社民,郁军.机制砂品质对混凝土质量的影响[J].施工技术,2016(s1):577-579.
[15] 张如林,陈玉前,刘书童,等.机制砂石粉含量对混凝土的性能影响研究[J].混凝土,2016(3):84-85.
[16] Donza H,Cabrera O,Irassar E.F.High-strength concrete with different fine aggregate[J]. Cem. & Con. Research,2002,32(11):1755-1761.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州