低速搅拌下高水胶比压浆料的制备及其性能研究
Study on Preparation and Properties of High Water-Binder Duct Grouts Under Low-speed Stirring
2020年第11期
压浆料;配合比;制备;性能;施工;低速搅拌
Duct grouts; Mix proportion; Preparation; Performance; Construction; Low-speed stirring
2020年第11期
10.19761/j.1000-4637.2020.11.030.05
国家重点研发计划项目(2016YFC0701904-3);上海市科委社发项目(18DZ1205204)。
沈贵阳1,樊俊江2,於林锋3
1.上海市建筑科学研究院有限公司,上海 200032;2.上海工业固体废弃物资源化利用工程技术研究中心,上海 201108;3.上海市建筑科学研究院(集团)有限公司,上海 200000

沈贵阳1,樊俊江2,於林锋3

沈贵阳,樊俊江,於林锋.低速搅拌下高水胶比压浆料的制备及其性能研究[J].混凝土与水泥制品,2020(11):30-34.

SHEN G Y,FAN J J,YU L F.Study on Preparation and Properties of High Water-Binder Duct Grouts Under Low-speed Stirring[J].CHINA CONCRETE AND CEMENT PRODUCTS,2020(11):30-34.

浏览量:
1000
摘   要:研究了低速搅拌、高水胶比下,减水剂、硅灰、粉煤灰及膨胀剂对压浆料的流动性、泌水率以及抗压强度等性能的影响规律,在此基础上优化了配合比,制备了普通低速搅拌下高水胶比压浆料。试验结果表明,在转速低于300 r/min、0.42高水胶比情况下,可以制备出初始流动度为25.5 s、不泌水、各项性能均满足实际工程应用要求的预应力孔道压浆材料。该制备技术在简化施工工艺的同时降低材料成本约231 元/吨,对促进预应力孔道压浆材料的技术改进具有重要的意义。 Abstract: The effects of high water-binder ratio, water reducing agent, silica fume, fly ash and expansion agent on the flowability, water bleeding rate and compressive strength of duct grouts under low-speed stirring were studied. On this basis, the mix proportion was optimized to prepare a high water-binder ratio duct grouts under ordinary low-speed stirring. The results show that under low-speed stirring at a speed lower than 300 r/min and a high water-binder ratio of 0.42, a prestressed channel grouting material with an initial fluidity of 25.5 s, no bleeding and performance that meets the requirements of practical engineering applications can be prepared. This preparation technology reduces the material cost by about 231 yuan/t while simplifying the construction process, which is of great significance to the technical improvement of the prestressed channel grouting material.
英文名 : Study on Preparation and Properties of High Water-Binder Duct Grouts Under Low-speed Stirring
刊期 : 2020年第11期
关键词 : 压浆料;配合比;制备;性能;施工;低速搅拌
Key words : Duct grouts; Mix proportion; Preparation; Performance; Construction; Low-speed stirring
刊期 : 2020年第11期
DOI : 10.19761/j.1000-4637.2020.11.030.05
文章编号 :
基金项目 : 国家重点研发计划项目(2016YFC0701904-3);上海市科委社发项目(18DZ1205204)。
作者 : 沈贵阳1,樊俊江2,於林锋3
单位 : 1.上海市建筑科学研究院有限公司,上海 200032;2.上海工业固体废弃物资源化利用工程技术研究中心,上海 201108;3.上海市建筑科学研究院(集团)有限公司,上海 200000

沈贵阳1,樊俊江2,於林锋3

沈贵阳,樊俊江,於林锋.低速搅拌下高水胶比压浆料的制备及其性能研究[J].混凝土与水泥制品,2020(11):30-34.

SHEN G Y,FAN J J,YU L F.Study on Preparation and Properties of High Water-Binder Duct Grouts Under Low-speed Stirring[J].CHINA CONCRETE AND CEMENT PRODUCTS,2020(11):30-34.

摘要
参数
结论
参考文献
引用本文

摘   要:研究了低速搅拌、高水胶比下,减水剂、硅灰、粉煤灰及膨胀剂对压浆料的流动性、泌水率以及抗压强度等性能的影响规律,在此基础上优化了配合比,制备了普通低速搅拌下高水胶比压浆料。试验结果表明,在转速低于300 r/min、0.42高水胶比情况下,可以制备出初始流动度为25.5 s、不泌水、各项性能均满足实际工程应用要求的预应力孔道压浆材料。该制备技术在简化施工工艺的同时降低材料成本约231 元/吨,对促进预应力孔道压浆材料的技术改进具有重要的意义。

Abstract: The effects of high water-binder ratio, water reducing agent, silica fume, fly ash and expansion agent on the flowability, water bleeding rate and compressive strength of duct grouts under low-speed stirring were studied. On this basis, the mix proportion was optimized to prepare a high water-binder ratio duct grouts under ordinary low-speed stirring. The results show that under low-speed stirring at a speed lower than 300 r/min and a high water-binder ratio of 0.42, a prestressed channel grouting material with an initial fluidity of 25.5 s, no bleeding and performance that meets the requirements of practical engineering applications can be prepared. This preparation technology reduces the material cost by about 231 yuan/t while simplifying the construction process, which is of great significance to the technical improvement of the prestressed channel grouting material.

关键词:
及其
the
of
and
材料
水胶
water-binder
low-speed
under
ratio
扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加

(1)在转速低于300 r/min低速搅拌、高水胶比0.42下,通过调整减水剂、硅灰、粉煤灰、膨胀剂等原材料的掺量,优选配合比,可以制备出凝结时间、流动度、泌水率、抗折强度、抗压强度、膨胀率、充盈度等性能均良好的预应力孔道压浆材料。

(2)从工程试点的结果来看,本文制备的预应力孔道压浆材料无论从新拌浆体的状态、硬化浆体强度,还是在桥梁预应力孔道实际填充的密实度均达到预期要求,可以在实际工程中推广和应用。
(3)与市售压浆材料相比,本文制备的预应力孔道压浆材料生产成本约降低231 元/吨,是一种经济、实用的压浆材料。
(4)本文开发的普通低速搅拌下高水胶比压浆料的制备技术,制备出了性能指标满足实际工程应用需求的压浆料,简化了传统压浆料的施工工艺且降低材料成本,对促进预应力孔道压浆材料的技术改进具有重要的意义。

[1] 于超,马海峰,张亚梅.高性能预应力孔道灌浆料的试验研究[J].混凝土与水泥制品,2014(5):1-7. 
[2] 冯小伟,王勇.转速对预应力孔道压浆料性能的影响[J].中外公路,2012,32(5):173-176. 
[3] 邵正明,王强,邹新,等.国标《水泥基灌浆材料施工技术规范》编制背景介绍[J].混凝土,2009(9):1-4. 
[4] RAFAT  S.Utilization  of  silica  fume  in  concrete:  Review  of  hardened properties.[J]Resources, Conservation and Recycling,2011,55:923-32.
[5] 牛全林,冯乃谦,杨静.矿物质超细粉在水泥粉体中填充效果的分析[J].硅酸盐学报,2004,32(1):102-106.
[6] 马悦.常用矿物掺合料对水泥基材料的性能影响研究[D].合肥:安徽建筑大学,2015.
[7] SCHOKKER A,BREEN J E,KREGER M.Simulated field testing of high performance grouts for post-tensioning[J].Journal of bridge engineering,2002(2):127-133.
[8] SCHOKKER A,BREEN J E,KREGER M.Simulated field testing of highperformance grouts for post-tensioning [J].Journal of Bridge Engineering,2002(2):127-133.
[9] 韩建国,阎培渝,侯伟红.C4A3S-CaSO4-CaO体系在硅酸盐水泥浆体中的膨胀机理[J].硅酸盐学报,2016,44(11):1543-1551.
[10] 胡亮,徐智勇,段双,等.孔道压浆料专用塑性膨胀剂的试验研究[J].新型建筑材料,2011(10):18-20.

沈贵阳,樊俊江,於林锋.低速搅拌下高水胶比压浆料的制备及其性能研究[J].混凝土与水泥制品,2020(11):30-34.

SHEN G Y,FAN J J,YU L F.Study on Preparation and Properties of High Water-Binder Duct Grouts Under Low-speed Stirring[J].CHINA CONCRETE AND CEMENT PRODUCTS,2020(11):30-34.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州