养护条件对MgO膨胀剂膨胀性能的影响
The Effect of Different Curing Conditions on the Expansive Properties of MgO Expansive Agent
2021年第1期
MgO膨胀剂；限制膨胀率；膨胀性能；孔隙率
Magnesium oxide expansive agent; Restrained expansion rate; Expansive property; Porosity
2021年第1期
10.19761/j.1000-4637.2021.01.034.05
国家自然科学基金资助项目（51878400、51678344）。
周龙龙，王 舜，苗 苗，冯竟竟，李思琪，孙传珍
山东农业大学 水利土木工程学院，山东 泰安 271018

周龙龙，王 舜，苗 苗，冯竟竟，李思琪，孙传珍

周龙龙,王舜,苗苗,等.养护条件对MgO膨胀剂膨胀性能的影响[J].混凝土与水泥制品,2021(1):34-38

ZHOU L L,WANG S,MIAO M,et al.The Effect of Different Curing Conditions on the Expansive Properties of MgO Expansive Agent[J].CHINA CONCRETE AND CEMENT PRODUCTS,2021(1):34-38.

浏览量:
1000
摘   要：对水养、水养转干养和干湿循环养护条件下不同活性MgO膨胀剂（MEA）膨胀性能及水养条件下不同龄期膨胀净浆微观孔结构进行了研究。结果表明：MEA活性越高，其早期膨胀率增速越大，但后期膨胀率增速越慢；水养转干养条件下，干空膨胀落差与MEA活性成正比；干湿循环养护条件下，高活性MgO的补偿收缩效能高于低活性MgO。掺MEA浆体中大于50 nm孔隙的增加可能是砂浆产生膨胀的原因之一；28~180 d时，MEA主要细化的孔区间为20~200 nm。 Abstract: The expansion properties of different active MgO expansive agent (MEA) under the conditions of water curing, water curing to dry curing and dry and wet cycle curing and micro pore structure of different age expansive paste under water condition were studied. The results show that the higher the activity of MEA, the higher the early expansion rate, but the slower the later expansion rate. Under the condition of water curing to dry curing, dry air expansion drop is directly proportional to MEA activity. Under the condition of dry and wet cycle curing, the compensation contraction efficiency of high active MgO is higher than that of low active MgO. The addition of MEA promotes the increase of pores larger than 50 nm in the paste, which may be one of the reasons for the expansion of the mortar. At the age of 28 to 180 days, the main refining pores of MEA are between 20 nm and 200 nm.
英文名 : The Effect of Different Curing Conditions on the Expansive Properties of MgO Expansive Agent
刊期 : 2021年第1期
关键词 : MgO膨胀剂；限制膨胀率；膨胀性能；孔隙率
Key words : Magnesium oxide expansive agent; Restrained expansion rate; Expansive property; Porosity
刊期 : 2021年第1期
DOI : 10.19761/j.1000-4637.2021.01.034.05
文章编号 :
基金项目 : 国家自然科学基金资助项目（51878400、51678344）。
作者 : 周龙龙，王 舜，苗 苗，冯竟竟，李思琪，孙传珍
单位 : 山东农业大学 水利土木工程学院，山东 泰安 271018

周龙龙，王 舜，苗 苗，冯竟竟，李思琪，孙传珍

周龙龙,王舜,苗苗,等.养护条件对MgO膨胀剂膨胀性能的影响[J].混凝土与水泥制品,2021(1):34-38

ZHOU L L,WANG S,MIAO M,et al.The Effect of Different Curing Conditions on the Expansive Properties of MgO Expansive Agent[J].CHINA CONCRETE AND CEMENT PRODUCTS,2021(1):34-38.

摘要
参数
结论
参考文献
引用本文

摘   要：对水养、水养转干养和干湿循环养护条件下不同活性MgO膨胀剂（MEA）膨胀性能及水养条件下不同龄期膨胀净浆微观孔结构进行了研究。结果表明：MEA活性越高，其早期膨胀率增速越大，但后期膨胀率增速越慢；水养转干养条件下，干空膨胀落差与MEA活性成正比；干湿循环养护条件下，高活性MgO的补偿收缩效能高于低活性MgO。掺MEA浆体中大于50 nm孔隙的增加可能是砂浆产生膨胀的原因之一；28~180 d时，MEA主要细化的孔区间为20~200 nm。

Abstract: The expansion properties of different active MgO expansive agent (MEA) under the conditions of water curing, water curing to dry curing and dry and wet cycle curing and micro pore structure of different age expansive paste under water condition were studied. The results show that the higher the activity of MEA, the higher the early expansion rate, but the slower the later expansion rate. Under the condition of water curing to dry curing, dry air expansion drop is directly proportional to MEA activity. Under the condition of dry and wet cycle curing, the compensation contraction efficiency of high active MgO is higher than that of low active MgO. The addition of MEA promotes the increase of pores larger than 50 nm in the paste, which may be one of the reasons for the expansion of the mortar. At the age of 28 to 180 days, the main refining pores of MEA are between 20 nm and 200 nm.

扫二维码用手机看
未找到相应参数组，请于后台属性模板中添加

（1）水养条件下，MgO活性越高其早期膨胀率增长速度越快，但后期其膨胀率增速越慢。
（2）水养转干养条件下，干空膨胀落差与MEA活性有关，MEA活性越高，干空膨胀落差越大。
（3）干湿循环养护条件下，高活性MgO的补偿收缩效能高于低活性MgO。
（4）MEA的掺加导致浆体中大于50 nm孔隙的增加，掺高活性MEA浆体中大于50 nm的孔明显多于掺低活性MEA浆体，这可能是掺有MEA浆体产生膨胀的原因之一。
（5）28~180 d时，MEA主要细化孔的区间为20~200 nm；长龄期时，MEA水化产物的生成有效细化了孔隙。

[1] 王铁梦.工程结构裂缝控制[M].北京:中国建筑工业出版社,1997.
[2] MO L W,DENG M,TANG M S,et al.MgO expansive cement and concrete in China: Past, Present and Future [J].Cement and Concrete Research,2014,57(3):1-12.
[3] 游宝坤,赵顺增.我国混凝土膨胀剂发展的回顾和展望[J]. 膨胀剂与膨胀混凝土,2012(2):1-5.
[4] 莫立武,邓敏.氧化镁膨胀剂的研究现状[J].膨胀剂与膨胀混凝土,2010(1):2-9.
[5] MO L W,DENG M,TANG M S.Effects of calcination condition on expansion property of MgO-type expansive agent used in cement-based materials[J].Cement and Concrete Research,2010,40(3):437-446.
[6] 冯竟竟,苗苗,阎培渝．第五届全国混凝土膨胀剂学术交流会议论文集[C].上海:中国建材工业出版社,2010．
[7] 张红波,高培伟,耿飞,等.掺新型膨胀材料水泥砂浆变形性能研究[J].工业建筑,2012,42(7):119-123.
[8] 吴中伟,张鸿直.膨胀混凝土[M].北京:中国铁路出版社, 1990.
[9] 李延波,邓敏,莫立武,等.不同约束条件下掺轻烧MgO混凝土的力学性能[J].中南大学学报(自然科学版),2012,43(7):2534-2541.
[10] CAO F Z,MIAO M,YAN P Y.Hydration characteristics and expansive mechanism of MgO expansive agents[J].Construction and Building Materials,2018(183):234-242.

周龙龙,王舜,苗苗,等.养护条件对MgO膨胀剂膨胀性能的影响[J].混凝土与水泥制品,2021(1):34-38

ZHOU L L,WANG S,MIAO M,et al.The Effect of Different Curing Conditions on the Expansive Properties of MgO Expansive Agent[J].CHINA CONCRETE AND CEMENT PRODUCTS,2021(1):34-38.

上一个
利用碱性电解水激发砂浆中矿粉活性的研究
下一个
无

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设：中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设：中企动力 苏州