不同机制砂微观形貌和胶砂性能研究
Study on Microstructure and Mortar Properties of Different Machine-made Sands
2021年第1期
机制砂;微观结构;胶砂;级配;强度
Machine-made sand; Microstructure; Mortar; Gradation; Strength
2021年第1期
10.19761/j.1000-4637.2021.01.085.05
北京市自然科学基金项目(2192047);中国矿业大学(北京)越崎青年学者基金项目(2019QN10)。
孙星海1,刘 泽1,王军伟2,姜启衎1
1.中国矿业大学(北京) 化学与环境工程学院 混凝土与环境材料研究所,北京 100083;2.中国铁道科学研究院集团有限公司标准计量研究所 中铁检验认证中心有限公司,北京 100081

孙星海1,刘 泽1,王军伟2,姜启衎1

孙星海,刘泽,王军伟,等.不同机制砂微观形貌和胶砂性能研究[J].混凝土与水泥制品,2021(1):85-89.

SUN X H,LIU Z,WANG J W,et al.Study on Microstructure and Mortar Properties of Different Machine-made Sands[J].CHINA CONCRETE AND CEMENT PRODUCTS,2021(1):85-89.

浏览量:
1000
摘   要:为更好研究机制砂的合理应用,选取了3种不同岩性的机制砂,通过分级筛分后调配成Ⅱ区中砂,设计了三种不同级配的机制砂。研究了不同机制砂的化学组成、矿物组成和微观形貌,以及不同机制砂对胶砂性能的影响。研究表明:不同机制砂颗粒的长径比和圆形度有一定的差异,个别粒级的参数差异较大;级配对钙基机制砂胶砂强度影响没有硅基机制砂显著;细度模数较大时,钙基机制砂胶砂强度大于硅基机制砂。 Abstract: In order to study the reasonable application of machine-made sands, 3 kinds of machine-made sands with different lithology were selected and mixed into the middle sands of Area Ⅱ through classification and screening, and three different gradations of machine-made sands were prepared. The influence on the properties of mortar of the chemical composition, mineral composition, and micro-morphology of machine-made sands, different machine-made sands were analyzed. The results indicate that the slenderness ratio and roundness of different machine-made sands are different, and the parameters of individual grades are also different. The effect of gradation on the strength of silicon-based sands is more significant than that of calcium-based sands. When the fineness modulus is larger, the strength of calcium-based machine-made sand is higher than that of silicon-based machine-made sand.
英文名 : Study on Microstructure and Mortar Properties of Different Machine-made Sands
刊期 : 2021年第1期
关键词 : 机制砂;微观结构;胶砂;级配;强度
Key words : Machine-made sand; Microstructure; Mortar; Gradation; Strength
刊期 : 2021年第1期
DOI : 10.19761/j.1000-4637.2021.01.085.05
文章编号 :
基金项目 : 北京市自然科学基金项目(2192047);中国矿业大学(北京)越崎青年学者基金项目(2019QN10)。
作者 : 孙星海1,刘 泽1,王军伟2,姜启衎1
单位 : 1.中国矿业大学(北京) 化学与环境工程学院 混凝土与环境材料研究所,北京 100083;2.中国铁道科学研究院集团有限公司标准计量研究所 中铁检验认证中心有限公司,北京 100081

孙星海1,刘 泽1,王军伟2,姜启衎1

孙星海,刘泽,王军伟,等.不同机制砂微观形貌和胶砂性能研究[J].混凝土与水泥制品,2021(1):85-89.

SUN X H,LIU Z,WANG J W,et al.Study on Microstructure and Mortar Properties of Different Machine-made Sands[J].CHINA CONCRETE AND CEMENT PRODUCTS,2021(1):85-89.

摘要
参数
结论
参考文献
引用本文

摘   要:为更好研究机制砂的合理应用,选取了3种不同岩性的机制砂,通过分级筛分后调配成Ⅱ区中砂,设计了三种不同级配的机制砂。研究了不同机制砂的化学组成、矿物组成和微观形貌,以及不同机制砂对胶砂性能的影响。研究表明:不同机制砂颗粒的长径比和圆形度有一定的差异,个别粒级的参数差异较大;级配对钙基机制砂胶砂强度影响没有硅基机制砂显著;细度模数较大时,钙基机制砂胶砂强度大于硅基机制砂。

Abstract: In order to study the reasonable application of machine-made sands, 3 kinds of machine-made sands with different lithology were selected and mixed into the middle sands of Area Ⅱ through classification and screening, and three different gradations of machine-made sands were prepared. The influence on the properties of mortar of the chemical composition, mineral composition, and micro-morphology of machine-made sands, different machine-made sands were analyzed. The results indicate that the slenderness ratio and roundness of different machine-made sands are different, and the parameters of individual grades are also different. The effect of gradation on the strength of silicon-based sands is more significant than that of calcium-based sands. When the fineness modulus is larger, the strength of calcium-based machine-made sand is higher than that of silicon-based machine-made sand.

扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加

(1)圆形度和长径比是机制砂级配中较重要的参数,不同机制砂由于其岩性、风化程度和杂质含量的不同,宏观形貌、圆形度和长径比会有比较大区别,钙基机制砂和硅基机制砂表现出一定的差异。机制砂各粒级之间的圆形度和长径比会有一定变化趋势和差别,从而导致了各个粒级在胶砂级配中的影响程度不同。其中,0.60 mm粒级的含量较为重要。
(2)级配对机制砂强度的影响需要考虑到机制砂的岩性不同。对于钙基机制砂,由于矿物本身的性质,细颗粒的填充效应比较明显,级配的影响相较于硅质机制砂较小。硅质机制砂由于对于减水剂吸附性较高,对减水剂和水泥用量要求较高,在一定的级配下对胶砂强度会有明显的影响。
(3)特定级配下岩性对机制砂的强度有一定的影响,这可能与表面性质有关,钙质机制砂相较于硅质机制砂表面活性低,同时表面较为粗糙,界面结合面积较大,界面结合较好,强度高于同级配的硅基质机制砂。

[1] 赵有明,韩自力,李化建,等.我国铁路工程机制砂混凝土应用现状及存在问题[J].中国铁路,2019(8):1-7.
[2] 李振怀,甘洋宇,管民生,等.机制砂物理特性对高强混凝土工作性能和强度的影响[J].混凝土与水泥制品,2018(8):93-96.
[3] 宋少民,程成,杨楠.机制砂岩性对胶砂和混凝土性能影响的研究[J].混凝土,2019(9):67-70.
[4] 魏艺博,陈雷,于蕾,等.机制砂颗粒特性对胶砂综合性能的影响研究[J].公路交通科技(应用技术版),2018,14(7):137-138.
[5] 程成,宋少民,杨楠.高吸附性机制砂细颗粒对胶砂和混凝土性能影响的研究[J].混凝土世界,2018(2):85-88.
[6] 周玉娟,陈三安,占文,等.用于箱梁的凝灰岩机制砂混凝土力学及耐久性能研究[J].施工技术,2015(18):16-18.
[7] 汤晴.石灰岩与凝灰岩机制砂混凝土力学性能对比研究[J].中国水运月刊,2015,15(9):316-318.
[8] 潘菲,姜观荣.机制砂级配对品质参数的影响规律研究[J].粉煤灰综合利用,2016(4):31-34.
[9] 夏龙兴,吴蓉.机制砂与天然砂的性能研究[J].混凝土,2008(7):60-61.
[10] 郭丹,宋少民,李莉.Ⅱ区机制砂不同级配对胶砂和混凝土性能的影响[J].建筑技术,2016,47(9):829-831.
[11] 黄星浩,张欣,李哲,等.基于富勒及泰波理论的机制砂颗粒级配研究[J].混凝土,2019(4):97-101.
[12] 蔡园园,房怀英,余文,等.采用数字图像处理的机制砂粒度级配检测方法[J].华侨大学学报(自然科学版),2019,40(5):567-573.
[13] 赵文久.机制砂级配对高强混凝土工作性能的影响分析[J].住宅与房地产,2019(22):106.
[14] 艾志勇,李娟燕,舒小平,等.机制砂级配对高强混凝土工作性能的影响[J].交通科技,2019(3):135-138.
[15] 刘锦涛.机制砂与聚羧酸减水剂相容性及机理研究[D].北京:北京建筑大学,2019.
[16] 陈军,闵凡飞,王辉.微细粒矿物疏水聚团的研究现状及进展[J].矿物学报,2014,34(2):181-188.

孙星海,刘泽,王军伟,等.不同机制砂微观形貌和胶砂性能研究[J].混凝土与水泥制品,2021(1):85-89.

SUN X H,LIU Z,WANG J W,et al.Study on Microstructure and Mortar Properties of Different Machine-made Sands[J].CHINA CONCRETE AND CEMENT PRODUCTS,2021(1):85-89.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州