再生粗骨料强化处理工艺对再生混凝土性能的影响
Influence of Strengthening Treatment Technology of Recycled Coarse Aggregate on Performance of Recycled Concrete
2015年第6期
再生混凝土;强化处理工艺;用水量;抗压强度;抗渗透;抗碳化
Recycled concrete; Strengthening treatment technology; Water consumption; Compressive strength; Penetration resistance; Carbonation resistance
2015年第6期
1000-4637(2015)06-11-07
国家自然科学基金资助(51378270);山东省高校优秀科研创新团队计划资助。
郭远新,李秋义,孔 哲,岳公冰,韩 帅
蓝色经济区工程建设与安全协同创新中心,青岛理工大学,266033

郭远新,李秋义,孔 哲,岳公冰,韩 帅

郭远新,李秋义,孔哲,等.再生粗骨料强化处理工艺对再生混凝土性能的影响[J].混凝土与水泥制品,2015(6):11-17.

GUO Y X,LI Q Y,KONG Z,et al.Influence of Strengthening Treatment Technology of Recycled Coarse Aggregate on Performance of Recycled Concrete[J].CHINA CONCRETE AND CEMENT PRODUCTS,2015(6):11-17.

浏览量:
1000
摘   要:分别采用物理强化、化学强化和物理-化学复合强化三种不同的强化方式对简单破碎再生粗骨料进行强化处理,并采用100%取代天然碎石制备再生粗骨料混凝土,研究了不同强化处理后的再生粗骨料对混凝土工作性能、力学性能、抗渗透性能和抗碳化性能的影响。结果表明,经过强化处理的再生粗骨料混凝土的各项性能均有不同程度的提高,其中经二次物理强化处理后的再生粗骨料混凝土的用水量较天然碎石混凝土仅增加了6kg/m3,其抗压强度也达到最高值,接近于天然碎石混凝土;经二次物理强化和化学浸渍复合强化处理后的再生混凝土氯离子扩散系数降低了13.6%;三种不同的强化方式处理后,再生混凝土的碳化深度和碳化速度均有所降低。 Abstract: Three kinds of different strengthening technologies of physical enhancement, chemical enhancement and physical-chemical compound enhancement to strengthen the simple crushing recycled coarse aggregate are adopted, with 100% replaced natural gravel preparation of recycled coarse aggregate concrete, and the influences of the recycled coarse aggregate of different strengthening treatment on the working performance, mechanical properties, penetration resistance and carbonation resistance of concrete are studied. The research results show that, through strengthening treatment, recycled coarse aggregate concrete properties are improved to different degrees, the water consumption of recycled coarse aggregate concrete after the secondary physical strengthen treatment is only increased by 6kg/m3 than that of natural gravel concrete. The compressive strength also reached the highest value, close to the natural gravel concrete. The chloride ion diffusion coefficient of recycled concrete after the secondary physical-chemical compound strengthening treatment is reduced by 13.6%. The depth of carbonation and carbonation velocity decrease after three kinds of different strengthening treatments.
英文名 : Influence of Strengthening Treatment Technology of Recycled Coarse Aggregate on Performance of Recycled Concrete
刊期 : 2015年第6期
关键词 : 再生混凝土;强化处理工艺;用水量;抗压强度;抗渗透;抗碳化
Key words : Recycled concrete; Strengthening treatment technology; Water consumption; Compressive strength; Penetration resistance; Carbonation resistance
刊期 : 2015年第6期
DOI :
文章编号 : 1000-4637(2015)06-11-07
基金项目 : 国家自然科学基金资助(51378270);山东省高校优秀科研创新团队计划资助。
作者 : 郭远新,李秋义,孔 哲,岳公冰,韩 帅
单位 : 蓝色经济区工程建设与安全协同创新中心,青岛理工大学,266033

郭远新,李秋义,孔 哲,岳公冰,韩 帅

郭远新,李秋义,孔哲,等.再生粗骨料强化处理工艺对再生混凝土性能的影响[J].混凝土与水泥制品,2015(6):11-17.

GUO Y X,LI Q Y,KONG Z,et al.Influence of Strengthening Treatment Technology of Recycled Coarse Aggregate on Performance of Recycled Concrete[J].CHINA CONCRETE AND CEMENT PRODUCTS,2015(6):11-17.

摘要
参数
结论
参考文献
引用本文

摘   要:分别采用物理强化、化学强化和物理-化学复合强化三种不同的强化方式对简单破碎再生粗骨料进行强化处理,并采用100%取代天然碎石制备再生粗骨料混凝土,研究了不同强化处理后的再生粗骨料对混凝土工作性能、力学性能、抗渗透性能和抗碳化性能的影响。结果表明,经过强化处理的再生粗骨料混凝土的各项性能均有不同程度的提高,其中经二次物理强化处理后的再生粗骨料混凝土的用水量较天然碎石混凝土仅增加了6kg/m3,其抗压强度也达到最高值,接近于天然碎石混凝土;经二次物理强化和化学浸渍复合强化处理后的再生混凝土氯离子扩散系数降低了13.6%;三种不同的强化方式处理后,再生混凝土的碳化深度和碳化速度均有所降低。

Abstract: Three kinds of different strengthening technologies of physical enhancement, chemical enhancement and physical-chemical compound enhancement to strengthen the simple crushing recycled coarse aggregate are adopted, with 100% replaced natural gravel preparation of recycled coarse aggregate concrete, and the influences of the recycled coarse aggregate of different strengthening treatment on the working performance, mechanical properties, penetration resistance and carbonation resistance of concrete are studied. The research results show that, through strengthening treatment, recycled coarse aggregate concrete properties are improved to different degrees, the water consumption of recycled coarse aggregate concrete after the secondary physical strengthen treatment is only increased by 6kg/m3 than that of natural gravel concrete. The compressive strength also reached the highest value, close to the natural gravel concrete. The chloride ion diffusion coefficient of recycled concrete after the secondary physical-chemical compound strengthening treatment is reduced by 13.6%. The depth of carbonation and carbonation velocity decrease after three kinds of different strengthening treatments.

扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加

(1)简单破碎再生粗骨料经强化工艺处理后,再生混凝土用水量显著减少,其中在二次物理强化后再生混凝土的用水量较天然碎石混凝土仅增加6kg/m3,其和易性也接近于天然碎石混凝土。
(2)经物理强化和物理-化学复合强化处理后,再生混凝土的抗压强度均得到提高,其中在二次物理强化处理后再生混凝土的3d、7d、14d、28d及56d抗压强度分别较简单破碎增加0.5%、10.1%、16.3%、18.5%及17.2%;而经化学强化处理后再生混凝土的抗压强度有小幅度降低,这与混凝土拌合物的有效水灰比以及有机硅防水剂影响骨料界面的黏结性能有关。
(3)相比简单破碎再生混凝土,二次物理强化处理后,再生混凝土的氯离子扩散系数减小0.84×10-12m2/s,化学强化后氯离子扩散系数有小幅增加,二次物理强化和化学浸渍复合强化后降低了13.6%。
(4)简单破碎再生粗骨料经物理强化和物理-化学复合强化处理后,由其制备的再生混凝土的碳化深度和碳化速度均有所降低,再生混凝土的抗碳化性能得到加强,相比未经强化处理的再生混凝土,其中在二次物理强化和化学浸渍复合强化处理后,再生混凝土的3d、7d、14d及28d的碳化深度分别减少了0.4mm、0.8mm、0.8mm及0.6mm;而经化学强化处理后再生混凝土的抗碳化性能则会有小幅的降低。

[1] 李秋义.建筑垃圾资源化利用技术[M].北京: 中国建材工业出版社,2011.
[2] 王程,施惠生.废弃混凝土再生利用技术的研究进展[J].材料导报,2010, 24(1):120-123.
[3] 嵩英雄. 再生粗骨材の品質が再生骨材コンクリートの強度と耐久性に及ぼす影響に关する实验的研究[C]. 日本建築学会学術講演集, 2003,9: 241-242. 
[4] F. Debieb, L. Courard, S. Kenai, R. Degeimbre. Mechanical and durability properties of concrete using contaminated recycled aggregates[J]. Cement and Concrete Composites, 2010, 32(6): 421-426.
[5] 西祐宜,假屋園礼文,嵩英雄,等.高度化处理による再生骨材の品質改善效果(第2報)[C]. 日本建築学会学術講演集, 2000,9: 143-144.
[6] 李莹.建筑垃圾压得城市喘息[J].中国环境报, 2013(8):24-25. 
[7] 李秋义,李云霞,朱崇绩. 再生混凝土骨料强化技术研究[J].混凝土, 2006(1): 74-77.
[8] 叶禾.高品质再生粗骨料混凝土的力学性能和耐久性能试验研究[D].杭州: 浙江工业大学硕士论文,2009.
[9] 华小巧.建筑废弃物再生粗骨料强化与再生混凝土的研究[D].昆明: 昆明理工大学硕士论文,2009.
[10] 毛高峰.再生粗骨料混凝土试验研究[D].青岛: 青岛理工大学硕士毕业论文,2008.
[11] 李秋义, 李云霞, 朱崇绩.颗粒整形对再生粗骨料性能的影响[J].材料科学与工艺,2005(6): 21-23. 
[12] 朱亚光, 李秋义, 高嵩. 硅烷浸渍对再生骨料及再生骨料混凝土吸水性能的影响[C]. 第三届全国再生混凝土学术交流会论文集, 2012.

郭远新,李秋义,孔哲,等.再生粗骨料强化处理工艺对再生混凝土性能的影响[J].混凝土与水泥制品,2015(6):11-17.

GUO Y X,LI Q Y,KONG Z,et al.Influence of Strengthening Treatment Technology of Recycled Coarse Aggregate on Performance of Recycled Concrete[J].CHINA CONCRETE AND CEMENT PRODUCTS,2015(6):11-17.

相关文件

  • 再生粗骨料强化处理工艺对再生混凝土.pdf

    大小:
    2021-01-20 14:31:21
上一页
1

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州