减缩型聚羧酸系减水剂SRPC-7的合成与性能研究
Study on Synthesis and Properties of Shrinkage Reducing Polycarboxylate Superplasticizer SRPC-7
2021年第2期
减缩;合成;表面张力;聚羧酸系减水剂
Shrinkage reducing; Synthesis; Surface tension; Polycarboxylate superplasticizer
2021年第2期
10.19761/j.1000-4637.2021.02.005.04
北京市自然科学基金资助项目(8182014)。
李崇智,曹莹莹,牛振山,吴慧华
北京建筑大学 土木与交通工程学院,北京 102600

李崇智,曹莹莹,牛振山,吴慧华

李崇智,曹莹莹,牛振山,等.减缩型聚羧酸系减水剂SRPC-7的合成与性能研究[J].混凝土与水泥制品,2021(2):5-7,12.

LI C Z,CAO Y Y,NIU Z S,et al.Study on Synthesis and Properties of Shrinkage Reducing Polycarboxylate Superplasticizer SRPC-7[J].CHINA CONCRETE AND CEMENT PRODUCTS,2021(2):5-7,12.

浏览量:
1000
摘   要:合成了马来酸二乙二醇单丁醚的酯类单体,将其与甲基烯丙基聚乙二醇和丙烯酸(AA)、甲基丙烯磺酸钠(MAS)、过硫酸铵(APS)等共聚成一种具有良好分散性与保坍能力的减缩型聚羧酸系减水剂SRPC-7。结果表明:2.0%的SRPC-7溶液表面张力为35.2 mN/m,低于普通聚羧酸系减水剂PC的表面张力(53.9 mN/m);掺两种聚羧酸减水剂的砂浆与混凝土试件收缩率均低于空白组,掺SRPC-7的砂浆试件28 d收缩率下降了39.5%,掺SRPC-7的混凝土试件28 d收缩率比为55.4%,SRPC-7有利于提高混凝土的抗收缩开裂性能。 Abstract: The ester monomer of maleic acid diethylene glycol monobutyl ether was synthesized, and it was combined with methallyl polyethylene glycol, acrylic acid(AA), sodium methacrylate sulfonate(MAS), ammonium persulfate(APS) and other copolymerization into a shrinkage reducing polycarboxylate superplasticizer SRPC-7, which had good dispersibility and slump retention ability. The results show that the surface tension of the 2.0% SRPC-7 solution is 35.2 mN/m, which is far lower than the 53.9 mN/m of polycarboxylate superplasticizer PC. The shrinkage of the mortar and concrete mixed with PC is lower than that of the blank sample. The 28 d shrinkage rate of the cement mortar test block mixed with SRPC-7 decreases by 39.5%, and the 28 d shrinkage ratio of the concrete mixed with SRPC-7 is 55.4% of the blank group, which is conducive to the shrinkage and cracking resistance of concrete.
英文名 : Study on Synthesis and Properties of Shrinkage Reducing Polycarboxylate Superplasticizer SRPC-7
刊期 : 2021年第2期
关键词 : 减缩;合成;表面张力;聚羧酸系减水剂
Key words : Shrinkage reducing; Synthesis; Surface tension; Polycarboxylate superplasticizer
刊期 : 2021年第2期
DOI : 10.19761/j.1000-4637.2021.02.005.04
文章编号 :
基金项目 : 北京市自然科学基金资助项目(8182014)。
作者 : 李崇智,曹莹莹,牛振山,吴慧华
单位 : 北京建筑大学 土木与交通工程学院,北京 102600

李崇智,曹莹莹,牛振山,吴慧华

李崇智,曹莹莹,牛振山,等.减缩型聚羧酸系减水剂SRPC-7的合成与性能研究[J].混凝土与水泥制品,2021(2):5-7,12.

LI C Z,CAO Y Y,NIU Z S,et al.Study on Synthesis and Properties of Shrinkage Reducing Polycarboxylate Superplasticizer SRPC-7[J].CHINA CONCRETE AND CEMENT PRODUCTS,2021(2):5-7,12.

摘要
参数
结论
参考文献
引用本文

摘   要:合成了马来酸二乙二醇单丁醚的酯类单体,将其与甲基烯丙基聚乙二醇和丙烯酸(AA)、甲基丙烯磺酸钠(MAS)、过硫酸铵(APS)等共聚成一种具有良好分散性与保坍能力的减缩型聚羧酸系减水剂SRPC-7。结果表明:2.0%的SRPC-7溶液表面张力为35.2 mN/m,低于普通聚羧酸系减水剂PC的表面张力(53.9 mN/m);掺两种聚羧酸减水剂的砂浆与混凝土试件收缩率均低于空白组,掺SRPC-7的砂浆试件28 d收缩率下降了39.5%,掺SRPC-7的混凝土试件28 d收缩率比为55.4%,SRPC-7有利于提高混凝土的抗收缩开裂性能。

Abstract: The ester monomer of maleic acid diethylene glycol monobutyl ether was synthesized, and it was combined with methallyl polyethylene glycol, acrylic acid(AA), sodium methacrylate sulfonate(MAS), ammonium persulfate(APS) and other copolymerization into a shrinkage reducing polycarboxylate superplasticizer SRPC-7, which had good dispersibility and slump retention ability. The results show that the surface tension of the 2.0% SRPC-7 solution is 35.2 mN/m, which is far lower than the 53.9 mN/m of polycarboxylate superplasticizer PC. The shrinkage of the mortar and concrete mixed with PC is lower than that of the blank sample. The 28 d shrinkage rate of the cement mortar test block mixed with SRPC-7 decreases by 39.5%, and the 28 d shrinkage ratio of the concrete mixed with SRPC-7 is 55.4% of the blank group, which is conducive to the shrinkage and cracking resistance of concrete.

扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加

(1)用MAH、DGBE合成了MD减缩单体,将MD与烯丙基聚乙二醇和APS、AA、MAS等共聚,合成减缩型聚羧酸系减水剂SRPC-7。当溶液浓度为2.0%时,PC、SRPC-7可将表面张力从72.5 mN/m降至54.3 mN/m、35.6 mN/m。净浆流动度试验结果表明,SRPC-7的低表面张力有利于分散性能保持,与普通水泥具有良好的适应性。
(2)与空白组相比,掺SRPC-7的砂浆试件28 d收缩率降低了39.5%,表明SRPC-7能降低胶砂干燥收缩。
(3)掺SRPC-7混凝土具有较好的抗收缩能力,28 d的收缩率比为55.4%,相较于PC,收缩率比又降低了32.9%。可见SRPC-7更有利于混凝土的抗收缩性能。
(4)聚羧酸减水剂PC有一定的降低溶液表面张力作用,而SRPC-7因为在减水剂分子结构中引入了-COO(CH2CH2O)2C4H9基团侧链,使得混凝土孔溶液的表面张力降低,降低了混凝土浆体的收缩。

[1] 缪昌文.现代混凝土早期收缩裂缝及控制技术[J].徐州工程学院学报(自然科学版),2018,33(3):1-8.
[2] 王海骄.酯类聚羧酸减缩剂的研制与性能研究[D].北京:北京建筑大学,2013.
[3] 孙振平,杨辉.国内聚羧酸系减水剂的研究进展与展望[J].混凝土世界,2013(3):31-35.
[4] FERRARI L,KAUFMANN J,WINNEFELD F,et al.Muti-method approach to study influence of superplasticizers on cement susupensions[J].Cement and Concrete Research,2011,41:1058-1066.
[5] 徐雪峰,蔡跃波,孙红尧,等.一种多功能聚羧酸系减水剂的研制[J].新型建筑材料,2009,36(2):13-15.
[6] 李崇智,马健,葛挺林,等.缓释型聚羧酸系减水剂TP2000的试验研究[J].混凝土,2013(2):50-53.
[7] 冉千平,游有鲲,丁蓓.低引气性聚羧酸类高效减水剂的制备及其性能研究[J].新型建筑材料,2003(6):33-35.

李崇智,曹莹莹,牛振山,.减缩型聚羧酸系减水剂SRPC-7的合成与性能研究[J].混凝土与水泥制品,2021(2):5-7,12.

LI C Z,CAO Y Y,NIU Z S,et al.Study on Synthesis and Properties of Shrinkage Reducing Polycarboxylate Superplasticizer SRPC-7[J].CHINA CONCRETE AND CEMENT PRODUCTS,2021(2):5-7,12.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州