张兆文,周茗如,魏琴玲,等.基于冻融损伤下的高性能混凝土力学性能衰减规律研究[J].混凝土与水泥制品,2019(4):16-19.
ZHANG Z W,ZHOU M R,WEI Q L,et al.Research of Degradation Law on Mechanical Properties of High-performance Concrete Based on Freeze-thaw Cycles[J].China Concrete and Cement Products,2019(4):16-19.
基于冻融损伤下的高性能混凝土力学性能 衰减规律研究
张兆文1,周茗如2,魏琴玲2,谢国鑫2
张兆文,周茗如,魏琴玲,等.基于冻融损伤下的高性能混凝土力学性能衰减规律研究[J].混凝土与水泥制品,2019(4):16-19.
ZHANG Z W,ZHOU M R,WEI Q L,et al.Research of Degradation Law on Mechanical Properties of High-performance Concrete Based on Freeze-thaw Cycles[J].China Concrete and Cement Products,2019(4):16-19.
摘 要:为研究冻融损伤对高性能混凝土力学性能损失的影响,将混凝土置于水或盐溶液中快速冻融400次后,测其动弹性模量、抗折、抗压及劈裂抗拉强度。定性分析了冻融循环次数与上述四个评价指标间的关系,并分析了损伤度与相对剩余抗折强度及抗压强度之间的关系,建立了抗折强度的衰减方程。试验结果表明:随着冻融循环次数的增加,混凝土的动弹性模量、抗压、抗折和劈裂抗拉强度均逐步降低,抗压强度的衰减速率先增大后减小,动弹性模量、抗折、劈裂抗拉强度则是不断增大;相同冻融循环条件下,含气量越低、水胶比越大,冻融损失越大;冻融介质对混凝土的强度损失有一定影响,盐溶液对强度造成的损失更大;损伤度与相对剩余抗折强度间具有良好的相关性,但与抗压强度间不具有相关性。
Abstrat: In order to study the effect of freeze-thaw damage on the loss of mechanical properties of high-performance concrete, the concrete was placed in water and salt solution for 400 freeze-thaw cycles. Then, the dynamic modulus, flexural, compressive and splitting tensile strengths were measured. The relationship between freeze-thaw cycle times and the above four evaluation indicators was qualitatively analyzed, and the relationship between damage degree and relative residual flexural strength and compressive strength was also studied, and the attenuation equation of flexural strength was established. The test results show that with the increase of freeze-thaw cycles, the dynamic elastic modulus, compressive strength, flexural and splitting tensile strength of concrete are gradually reduced. The decay rate of compressive strength first increases and then decreases, but the dynamic elastic modulus, flexural resistance, splitting, and tensile strength increase continuously. Under the same freeze-thaw cycle conditions, the lower the gas content and the greater the W/B, the greater the loss of specimen quality, freeze-thaw medium has a certain influence on the strength loss of concrete. The strength loss of the specimen in the salt solution is greater. There is a good correlation between the degree of damage and the relative remaining flexural strength, however, there is correlation with the compressive strength.