铁尾矿砂对机制砂混凝土性能的影响研究
铁尾矿砂对机制砂混凝土性能的影响研究
  • 刘文燕1,张友来1,李绍纯2,邢卫疆1,孟玉冰1
2020年第12期
摘要
引用本文
摘   要:研究了铁尾矿砂取代率对机制砂混凝土工作性、力学性能和耐久性能的影响。结果表明:当铁尾矿砂取代率为40%时,混合砂的颗粒级配及细度模数与河砂相近,此时,混合砂混凝土的工作性和力学性能最优;随着铁尾矿砂取代率在一定范围内增加,混凝土的抗渗性能和抗氯离子侵蚀性能逐步提升。 Abstract: The effect of iron tailings sand replacement rate on the workability, mechanical properties and durability of machined sand concrete was studied. The results show that when the iron tailings sand replacement rate is 40%, the particle size gradation and fineness modulus of the mixed sand are similar to those of river sand. The concrete prepared by the mixed sand shows good workability and mechanical properties. In addition, as the iron tailings sand replacement rate increases within a certain range, the impermeability and the resistance to chloride ion erosion of concrete are gradually improved.
刘文燕,张友来,李绍纯,等.铁尾矿砂对机制砂混凝土性能的影响研究[J].混凝土与水泥制品,2020(12):84-86. LIU W Y,ZHANG Y L,LI S C,et al.Research on the Influence of Iron Tailings Sand on the Performance of Machined Sand Concrete[J].CHINA CONCRETE AND CEMENT PRODUCTS,2020(12):84-86.
再生混凝土骨料强化方法研究进展
再生混凝土骨料强化方法研究进展
  • 梁超锋1,2,杜孝敏1,裘锦瑜1,高越青1,WORKNEHHAILEAB Meles1
2020年第12期
摘要
引用本文
摘   要:再生混凝土骨料(RCA)表层砂浆的多孔性和高吸水性对再生骨料混凝土的力学性能和耐久性能不利,去除和强化RCA表层砂浆是提高RCA性能的两种主要方法。基于此,总结了聚合物、硅酸钠、微粉、CO2碳化、微生物碳酸盐沉积等RCA表层附着砂浆强化方法的研究现状,分析了各RCA强化方法的优缺点,并提出了有待进一步研究的问题,以推进再生混凝土的应用。 Abstract: The porosity and high water absorption of recycled concrete aggregate (RCA) surface mortar are detrimental to the mechanical properties and durability of recycled aggregate concrete. Removal and modification of RCA surface mortar are the two main ways to improve RCA performance. Based on this, the progress on various modification approaches of RCA surface mortar such as polymer coating, sodium silicate modification, micro-powder filling, CO2 carbonation and microbial carbonate deposition is summarized, the advantages and disadvantages of each RCA modification method are analyzed, and the problems to be further studied are put forward to promote the application of recycled concrete.
梁超锋,杜孝敏,裘锦瑜,等.再生混凝土骨料强化方法研究进展[J].混凝土与水泥制品,2020(12):87-91. LIANG C F,DU X M,QIU J Y,et al.Research Progress on Modification Methods of Recycled Concrete Aggregate[J].CHINA CONCRETE AND CEMENT PRODUCTS,2020(12):87-91.
生活垃圾焚烧炉渣在透水混凝土中的应用
生活垃圾焚烧炉渣在透水混凝土中的应用
  • 张立力1,谢一飞1,刘增喜2,宋奕波3,骆静静1,田 寅1,满丽莹1,蒋 涛1
2020年第12期
摘要
引用本文
摘   要:分析了生活垃圾焚烧炉渣的各项性能指标,并将其经多道水洗、筛分等工艺制成再生骨料,利用再生骨料取代天然砂石制备了透水混凝土。结果表明:生活垃圾焚烧炉渣的粒径分布较优,基本满足Ⅱ类建设用砂标准要求;再生骨料透水混凝土的抗压强度均低于基准组,透水系数均大于10 mm/s;随着再生骨料(处理后)取代率的增加,试件的28 d抗压强度逐渐降低;在取代率为100%的情况下,与未处理再生骨料透水混凝土相比,处理后再生骨料透水混凝土的抗压强度提高了43.1%。 Abstract:  The various indicators of the domestic waste incinerator slag were analyzed, and it was prepared into recycled aggregate through multiple washing, screening and other processes, and the pervious concrete was prepared by using recycled aggregate instead of natural sand. The results show that the domestic waste incinerator slag basically meets the requirements of Type Ⅱ construction sand standard, and the particle size distribution is better. The compressive strength of recycled aggregate pervious concrete is lower than that of reference group. The permeability coefficient of recycled aggregate pervious concrete is greater than 10 mm/s. With the increase of the replacement rate of recycled aggregate (after treatment), the 28 d compressive strength of specimen gradually decreases. When the replacement rate is 100%, compared with the untreated recycled aggregate pervious concrete, the compressive strength of the treated recycled aggregate pervious concrete is increased by 43.1%.
张立力,谢一飞,刘增喜,等.生活垃圾焚烧炉渣在透水混凝土中的应用[J].混凝土与水泥制品,2020(12):92-95. ZHANG L L,XIE Y F,LIU Z X,et al.Experimental Research on Application of Domestic Waste Incinerator Slag in Pervious Concrete[J].CHINA CONCRETE AND CEMENT PRODUCTS,2020(12):92-95.
上一页
1

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州