再生细骨料干混砂浆力学性能试验研究
Experimental Study on Mechanical Properties of Dry Mixed Mortar with Recycled Fine Aggregate
2021年第3期
含红砖再生细骨料;干混砂浆;再生粉料;抗压强度
Recycled fine aggregate containing crushed red brick; Dry mixed mortar; Recycled powder; Compressive strength
2021年第3期
10.19761/j.1000-4637.2021.03.093.04
国家自然科学基金项目(51661145023)。
高 琦1,2,3,肖建庄1,赵艳娜2,3,王浩通2,3,王 媛2,3
1.同济大学 土木工程学院,上海 200092;2.许昌金科资源再生股份有限公司,河南 许昌 461000; 3.河南省建筑废弃物再生利用工程技术研究中心,河南 许昌 461000

高 琦1,2,3,肖建庄1,赵艳娜2,3,王浩通2,3,王 媛2,3

高琦,肖建庄,赵艳娜,等.再生细骨料干混砂浆力学性能试验研究[J].混凝土与水泥制品,2021(3):93-96.

GAO Q,XIAO J Z,ZHAO YN,et al.Experimental Study on Mechanical Properties of Dry Mixed Mortar with Recycled Fine Aggregate[J].CHINA CONCRETE AND CEMENT PRODUCTS,2021(3):93-96.

浏览量:
1000
摘   要:利用含红砖的再生细骨料100%替代天然砂,制备生态干混砂浆,研究了用水量、再生粉料掺量和外加剂掺量对干混砂浆力学性能的影响。结果表明:当再生粉料和外加剂掺量不变时,砂浆强度随着用水量的增大而降低,但56 d强度增长率反而增大;当再生粉料掺量和用水量不变时,外加剂掺量的增加对砂浆各龄期的强度均有负面影响;当外加剂掺量和用水量不变时,再生粉料掺量为20%时,对应的砂浆强度最大,低于或高于此掺量均会使砂浆强度降低;含红砖再生细骨料干混砂浆的后期强度(56 d)仍有较大提升空间。 Abstract: The dry mixed mortar was prepared with 100% recycled fine aggregate containing crushed red brick instead of natural sand. The effects of different water addition, recycled powder content and admixture content on the mechanical properties of dry mixed mortar were studied. The results show that when the recycled powder content and admixture content are constant, the strength of the mortar decreases with the increase of water addition, while the growth rate of 56 d strength increases. When the recycled powder content and the water addition remain unchanged, the increase of admixture content has a negative impact on the strength of the mortar at all ages. When the admixture content and the water addition remain unchanged, the mortar with 20% recycled powder has the highest strength, and the strength of the mortar is reduced when the content is lower or higher than 20%. There is still a large increase space in the late strength (56 d) of dry mixed mortar with red brick recycled fine aggregate.
英文名 : Experimental Study on Mechanical Properties of Dry Mixed Mortar with Recycled Fine Aggregate
刊期 : 2021年第3期
关键词 : 含红砖再生细骨料;干混砂浆;再生粉料;抗压强度
Key words : Recycled fine aggregate containing crushed red brick; Dry mixed mortar; Recycled powder; Compressive strength
刊期 : 2021年第3期
DOI : 10.19761/j.1000-4637.2021.03.093.04
文章编号 :
基金项目 : 国家自然科学基金项目(51661145023)。
作者 : 高 琦1,2,3,肖建庄1,赵艳娜2,3,王浩通2,3,王 媛2,3
单位 : 1.同济大学 土木工程学院,上海 200092;2.许昌金科资源再生股份有限公司,河南 许昌 461000; 3.河南省建筑废弃物再生利用工程技术研究中心,河南 许昌 461000

高 琦1,2,3,肖建庄1,赵艳娜2,3,王浩通2,3,王 媛2,3

高琦,肖建庄,赵艳娜,等.再生细骨料干混砂浆力学性能试验研究[J].混凝土与水泥制品,2021(3):93-96.

GAO Q,XIAO J Z,ZHAO YN,et al.Experimental Study on Mechanical Properties of Dry Mixed Mortar with Recycled Fine Aggregate[J].CHINA CONCRETE AND CEMENT PRODUCTS,2021(3):93-96.

摘要
参数
结论
参考文献
引用本文

摘   要:利用含红砖的再生细骨料100%替代天然砂,制备生态干混砂浆,研究了用水量、再生粉料掺量和外加剂掺量对干混砂浆力学性能的影响。结果表明:当再生粉料和外加剂掺量不变时,砂浆强度随着用水量的增大而降低,但56 d强度增长率反而增大;当再生粉料掺量和用水量不变时,外加剂掺量的增加对砂浆各龄期的强度均有负面影响;当外加剂掺量和用水量不变时,再生粉料掺量为20%时,对应的砂浆强度最大,低于或高于此掺量均会使砂浆强度降低;含红砖再生细骨料干混砂浆的后期强度(56 d)仍有较大提升空间。

Abstract: The dry mixed mortar was prepared with 100% recycled fine aggregate containing crushed red brick instead of natural sand. The effects of different water addition, recycled powder content and admixture content on the mechanical properties of dry mixed mortar were studied. The results show that when the recycled powder content and admixture content are constant, the strength of the mortar decreases with the increase of water addition, while the growth rate of 56 d strength increases. When the recycled powder content and the water addition remain unchanged, the increase of admixture content has a negative impact on the strength of the mortar at all ages. When the admixture content and the water addition remain unchanged, the mortar with 20% recycled powder has the highest strength, and the strength of the mortar is reduced when the content is lower or higher than 20%. There is still a large increase space in the late strength (56 d) of dry mixed mortar with red brick recycled fine aggregate.

扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加

(1)为保证含红砖再生细骨料砂浆的强度,砌筑砂浆用水量应控制在26%以内,抹灰砂浆可适当提高用水量至28%左右。此外,若要在保证再生细骨料砂浆强度的同时兼顾施工性能,应延长搅拌时间至3~5 min。
(2)复合外加剂对含红砖再生细骨料砂浆的强度有负面影响,应在保证其基本性能的情况下,控制外加剂掺量在1‰以下。
(3)再生细骨料砂浆的保水率较高,在99%左右,这有利于砂浆的施工应用和后期强度的提升。
(4)再生粉料的掺加对提高砂浆的密实度和后期强度具有一定的积极作用,本试验再生粉料的最佳掺量为20%。

[1] 肖建庄.再生混凝土[M].北京:中国建筑工业出版社,2008.
[2] 陶李尧,罗健林,李秋义,等.内掺再生砖粉湿拌砂浆制备与力学强度研究[J].混凝土与水泥制品,2018(12):91-94.
[3] 陈家珑.建筑废弃物(建筑垃圾)的资源化利用及再生工艺[J].混凝土世界,2010(9):44-49.
[4] 孙跃冬,肖建庄.再生混凝土骨料[J].混凝土,2004(6):33-36.
[5] 肖建庄,李佳彬,兰阳.再生混凝土技术研究最新进展与评述[J].混凝土,2003(10):17-20,57.
[6] 张道令,吕常胜,张春涛,等.全组分再生细骨料在干混砂浆中的应用研究[J].混凝土与水泥制品,2017(8):91-94.
[7] 周爱军.废弃混凝土生产普通砂浆性能的试验研究[J].硅酸盐通报,2017(2):620-624.
[8] 石莹,徐仁崇,戴鹏.我国建筑垃圾资源化利用现状[J].粉煤灰,2016(1):27-30,34.
[9] 中华人民共和国住房和城乡建设部.建筑砂浆基本性能试验方法标准:JGJ/T 70—2009 [S].北京:中国建筑工业出版社,2009.
[10] 李丹,张云莲,邓媛媛,等.再生细骨料逐级取代对再生砂浆强度和微观形貌的影响[J].硅酸盐通报,2016(11):3876-3880.
[11] 张小鹏,彭春元,余斌,等.再生细粉对抹灰砂浆力学物理性能影响分析[J].混凝土世界,2018(7):90-92.
[12] 张小鹏.再生细粉对混凝土成熟度及力学性能的影响研究[D].广州:广州大学,2015.
[13] 冯琪.废弃混凝土再生细粉对普通硅酸盐水泥水化的影响[J].混凝土世界,2015(5):78-81.
[14] 陈曦,李滢,庄平英.废弃混凝土再生微粉胶凝性能的试验研究[J].混凝土与水泥制品,2019(11):96-100.
[15] 周文娟,季志远,赵磊,等.建筑垃圾再生微粉基本材性及对水泥胶砂性能的影响[J].混凝土与水泥制品,2019(3):93-96.
[16] 张喜,吴勇生,张剑波,等.建筑废弃混凝土细粉的活性激发及再利用可行性分析[J].江西科学,2011,29(1):70-73.
[17] 刘相阳.再生细骨料内养护自密实混凝土性能的研究[D].济南:山东大学,2019.

高琦,肖建庄,赵艳娜,.再生细骨料干混砂浆力学性能试验研究[J].混凝土与水泥制品,2021(3):93-96.

GAO Q,XIAO J Z,ZHAO YN,et al.Experimental Study on Mechanical Properties of Dry Mixed Mortar with Recycled Fine Aggregate[J].CHINA CONCRETE AND CEMENT PRODUCTS,2021(3):93-96.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州