通电加速锈蚀后弹卡式连接接头预制桩抗弯性能研究
Study on Flexural Performance of Prestressed Concrete Square Pile with Resilient Clamping Connection Joint After Electricity Accelerates Corrosion
2021年第5期
弹卡式连接;耐久性;加速劣化;受弯性能;破坏形式;预应力混凝土方桩
Resilient clamping connection; Durability; Accelerated deterioration; Flexural behavior; Failure mode; Prestressed concrete square pile
2021年第5期
10.19761/j.1000-4637.2021.05.033.06
刘伟扬1,龚顺风1,徐铨彪2, 3,陈 刚2, 3,刘承斌1,樊 华4
1.浙江大学 土木工程学系,浙江 杭州 310058;2.浙江大学平衡建筑研究中心,浙江 杭州 310028; 3.浙江大学建筑设计研究院有限公司,浙江 杭州 310028;4.嘉兴欣创混凝土制品有限公司, 浙江 嘉兴 314109

刘伟扬1,龚顺风1,徐铨彪2, 3,陈 刚2, 3,刘承斌1,樊 华4

刘伟扬,龚顺风,徐铨彪,等.通电加速锈蚀后弹卡式连接接头预制桩抗弯性能研究[J].混凝土与水泥制品,2021(5):33-38.

LIU W Y,GONG S F,XU Q B,et al.Study on Flexural Performance of Prestressed Concrete Square Pile with Resilient Clamping Connection Joint After Electricity Accelerates Corrosion[J].CHINA CONCRETE AND CEMENT PRODUCTES,2021(5):33-38.

浏览量:
1000
摘   要:为研究弹卡式连接预应力混凝土方桩在滨海环境下长期工作的耐久性能,对弹卡式连接与传统焊接式连接方桩接头试件进行了通电加速锈蚀试验,并对劣化后两种方桩接头试件进行了抗弯性能试验。结果表明:劣化后的弹卡式连接方桩接头试件整体连接性能保持完好,其开裂弯矩和极限弯矩试验值与桩身理论计算值较接近,试件受弯破坏形式为接头底部被拉开,弹卡连接件中插杆从小套筒中拔出而破坏;劣化后的焊接式连接方桩接头试件焊缝连接处锈蚀严重,其开裂弯矩和极限弯矩试验值相较桩身理论计算值下降幅度较大,试件受弯破坏形式为接头底部连接焊缝直接拉开,跨中接头底部两侧端板完全脱离。 Abstract: In order to study the long-term durability of prestressed concrete square piles with resilient clamping connection in coastal environments, the accelerated corrosion tests were conducted on prestressed concrete square piles with resilient clamping connection and traditional welded connection, and the flexural performance tests of two kinds of square pile joint specimens were conducted. The results show that the overall connection performance of the deteriorated square pile joint specimens with resilient clamping connection remains intact and the test values of cracking moment and ultimate moment are close to the theoretical calculation values of the pile body. The flexural failure mode of the specimens is that the bottom of the connection joint is pulled apart, and the inserting rod in resilient clamping connector is pulled out from the small sleeve. However, the weld seam of the welded square pile joint specimens are corroded seriously. Compared to the theoretical values, the cracking and ultimate bending moment of the welded square pile joint specimens after corrosion deterioration are significantly reduced. The flexural failure mode of the specimen is that the connecting weld seam at the bottom of the joint is pulled apart, and the end plates on both sides of the bottom are completely separated.
英文名 : Study on Flexural Performance of Prestressed Concrete Square Pile with Resilient Clamping Connection Joint After Electricity Accelerates Corrosion
刊期 : 2021年第5期
关键词 : 弹卡式连接;耐久性;加速劣化;受弯性能;破坏形式;预应力混凝土方桩
Key words : Resilient clamping connection; Durability; Accelerated deterioration; Flexural behavior; Failure mode; Prestressed concrete square pile
刊期 : 2021年第5期
DOI : 10.19761/j.1000-4637.2021.05.033.06
文章编号 :
基金项目 :
作者 : 刘伟扬1,龚顺风1,徐铨彪2, 3,陈 刚2, 3,刘承斌1,樊 华4
单位 : 1.浙江大学 土木工程学系,浙江 杭州 310058;2.浙江大学平衡建筑研究中心,浙江 杭州 310028; 3.浙江大学建筑设计研究院有限公司,浙江 杭州 310028;4.嘉兴欣创混凝土制品有限公司, 浙江 嘉兴 314109

刘伟扬1,龚顺风1,徐铨彪2, 3,陈 刚2, 3,刘承斌1,樊 华4

刘伟扬,龚顺风,徐铨彪,等.通电加速锈蚀后弹卡式连接接头预制桩抗弯性能研究[J].混凝土与水泥制品,2021(5):33-38.

LIU W Y,GONG S F,XU Q B,et al.Study on Flexural Performance of Prestressed Concrete Square Pile with Resilient Clamping Connection Joint After Electricity Accelerates Corrosion[J].CHINA CONCRETE AND CEMENT PRODUCTES,2021(5):33-38.

摘要
参数
结论
参考文献
引用本文

摘   要:为研究弹卡式连接预应力混凝土方桩在滨海环境下长期工作的耐久性能,对弹卡式连接与传统焊接式连接方桩接头试件进行了通电加速锈蚀试验,并对劣化后两种方桩接头试件进行了抗弯性能试验。结果表明:劣化后的弹卡式连接方桩接头试件整体连接性能保持完好,其开裂弯矩和极限弯矩试验值与桩身理论计算值较接近,试件受弯破坏形式为接头底部被拉开,弹卡连接件中插杆从小套筒中拔出而破坏;劣化后的焊接式连接方桩接头试件焊缝连接处锈蚀严重,其开裂弯矩和极限弯矩试验值相较桩身理论计算值下降幅度较大,试件受弯破坏形式为接头底部连接焊缝直接拉开,跨中接头底部两侧端板完全脱离。

Abstract: In order to study the long-term durability of prestressed concrete square piles with resilient clamping connection in coastal environments, the accelerated corrosion tests were conducted on prestressed concrete square piles with resilient clamping connection and traditional welded connection, and the flexural performance tests of two kinds of square pile joint specimens were conducted. The results show that the overall connection performance of the deteriorated square pile joint specimens with resilient clamping connection remains intact and the test values of cracking moment and ultimate moment are close to the theoretical calculation values of the pile body. The flexural failure mode of the specimens is that the bottom of the connection joint is pulled apart, and the inserting rod in resilient clamping connector is pulled out from the small sleeve. However, the weld seam of the welded square pile joint specimens are corroded seriously. Compared to the theoretical values, the cracking and ultimate bending moment of the welded square pile joint specimens after corrosion deterioration are significantly reduced. The flexural failure mode of the specimen is that the connecting weld seam at the bottom of the joint is pulled apart, and the end plates on both sides of the bottom are completely separated.

扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加

(1)劣化后弹卡式连接方桩接头试件接头处结构胶依然紧密地包裹着接头四周,未出现开裂现象,接头试件整体连接性能保持完好;劣化后焊接式连接方桩接头试件焊缝连接处锈蚀严重,原饱满的坡口焊缝在锈蚀作用下呈凹槽状。
(2)劣化后弹卡式连接方桩接头试件开裂弯矩和极限弯矩试验值与桩身受弯承载力理论计算值较接近,而劣化后焊接式连接方桩接头试件开裂弯矩和极限弯矩试验值与理论计算值相比分别下降39%~59%和43%~74%,弹卡式连接预应力混凝土方桩表现出更好的耐久性能。
(3)劣化后弹卡式连接方桩接头试件桩身受弯裂缝数目较多且分布均匀,裂缝主要沿跨中发展,少数裂缝有分叉现象;劣化后焊接式连接方桩接头试件桩身受弯裂缝数目较少,裂缝主要沿竖向发展,破坏前桩身裂缝最大宽度较小。
(4)劣化后弹卡式连接方桩接头试件的受弯破坏形式为接头底部被拉开,弹卡连接件中的插杆从小套筒中拔出而破坏;劣化后焊接式连接方桩接头试件的受弯破坏形式为接头底部连接焊缝直接被拉开,跨中接头底部两侧端板完全脱离而破坏。

[1] 张季超,唐孟雄,马旭,等.预应力混凝土管桩耐久性问题探讨[J].岩土工程学报,2011,33(S2):490-493.
[2] 艾立涛.南方沿海地区蒸压预应力高强混凝土管桩耐久性研究[D].广州:华南理工大学,2013.
[3] 林碧兰,路新瀛,李龙.PHC管桩金属端头在土壤模拟液中的腐蚀行为[J].中南大学学报(自然科学版),2011,42(2):434-440.
[4] ZHAN Y,YANG Y B,WU XH,et al.Experimental study on non-autoclaved PHC pile concrete applying poly-carboxylate superplasticizer[J].Advanced Materials Research,2015,629-630:345-350.
[5] 梁槟星,李龙,魏宜岭.关于PHC管桩在强腐蚀环境应用的探讨[J].混凝土与水泥制品,2009(6):27-28,31.
[6] 岑文杰,董桂洪,熊建波,等.近海环境中PHC管桩防腐蚀对策[J].水运工程,2011(12):131-134.
[7] LI L,GONG W B,LI J P.Service life of prestressed high-strength concrete pile in marine environment considering effects of concrete stratification and temperature [J].Construction and Building Materials,2020,253:119233.
[8] 岳增国,齐金良,夏晋,等.预应力混凝土离心桩劣化后抗拉性能试验研究[J].建筑结构,2015,45(11):87-90.
[9]许顺良.弹卡式连接件以及连接桩:204728323U[P].2015-10-28.
[10] 王云飞,陈刚,徐铨彪,等.弹卡式连接预应力混凝土方桩接头抗拉性能研究[J].防灾减灾工程学报,2018,38(6):1003-1011.
[11] 周家伟,王云飞,龚顺风,等.弹卡式连接预应力混凝土方桩接头受弯性能研究[J].建筑结构,2020,50(13):121-127,133.
[12] 袁迎曙,贾福萍,蔡跃.锈蚀钢筋混凝土梁的结构性能退化模型[J].土木工程学报,2001,34(3):47-52,96.
[13] 浙江省标准化研究院.弹卡式连接预应力混凝土方桩:2017浙G44[S].北京:中国计划出版社,2017.
[14] 中华人民共和国国家质量监督检验检疫总局,中国国家标准化管理委员会.预应力混凝土用钢棒:GB/T 5223.3—2017[S].北京:中国标准出版社,2017.
[15] 中华人民共和国住房和城乡建设部,国家市场监督管理总局.混凝土物理力学性能试验方法标准:GB/T 50081—2019[S].北京:中国建筑工业出版社,2019.
[16] 国家市场监督管理总局,中国国家标准化管理委员会.预应力混凝土用钢材试验方法:GB/T 21839—2019[S].北京:中国标准出版社,2019.
[17]  中华人民共和国国家质量监督检验检疫总局,中国国家标准化管理委员会.先张法预应力混凝土管桩:GB 13476—2009[S].北京:中国标准出版社,2009.
[18] 中华人民共和国住房和城乡建设部,国家市场监督管理总局.混凝土结构设计规范GB 50010—2010[S].北京:中国建筑工业出版社,2011.

刘伟扬,龚顺风,徐铨彪,.通电加速锈蚀后弹卡式连接接头预制桩抗弯性能研究[J].混凝土与水泥制品,2021(5):33-38.

LIU W Y,GONG S F,XU Q B,et al.Study on Flexural Performance of Prestressed Concrete Square Pile with Resilient Clamping Connection Joint After Electricity Accelerates Corrosion[J].CHINA CONCRETE AND CEMENT PRODUCTES,2021(5):33-38.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州