混凝土早强剂低温性能试验研究

Study on the Propery of Early-strength Agent of Concrete at Low Temperature

2021年第7期

低温；早强剂；抗压强度；水化热；耐久性

Low temperature; Early-strength agent; Compressive strength; Hydration heat; Durability

2021年第7期

10.19761/j.1000-4637.2021.07.001.06

国家重点研发计划项目（2018YFC0406702）；国家自然科学基金项目（51739008）；中央级公益性科研院所基本科研业务费专项（Y419004）。

张丰，白银，陈波，宁逢伟，吕乐乐，胡海明

南京水利科学研究院水文水资源与水利工程科学国家重点实验室，江苏南京 210029

张丰，白银，陈波，宁逢伟，吕乐乐，胡海明

张丰,白银,陈波,等.混凝土早强剂低温性能试验研究[J].混凝土与水泥制品,2021(7):1-6.

ZHANG F,BAI Y,CHEN B,et al.Study on the Propery of Early-strength Agent of Concrete at Low Temperature[J].CHINA CONCRETE AND CEMENT PRODUCTS,2021(7):1-6.

浏览量:

1000

摘要：从强度、凝结时间、水化热及混凝土工作性、耐久性等方面比较了5种混凝土早强剂在低温环境下的性能差异，综合评价了市售混凝土早强剂的低温使用效果。结果表明：5 ℃养护下，早强剂使砂浆7 d强度均有一定程度提高，但1 d强度仍比较低，且会使28 d强度倒缩；早强剂的掺入可促进低温下水泥的水化，使水化诱导期缩短，最大放热速率、放热量增大；掺D、E早强剂对混凝土工作性影响不大，满足实际工程施工性能的要求，可一定程度提高混凝土早期强度，但低温早强效果仍有限，且会导致混凝土后期性能下降。 Abstract: The performance differences of five kinds of commercial concrete early-strength agents at low temperature were compared from the perspectives of compressive strength, setting time, hydration heat, and workability and durability of concrete, and the application effect of the early-strength agents currently on the market was evaluated. The results show that under 5 ℃ curing, the early-strength agent can increase the strength of the mortar to a certain extent, but the strength of 1 d is still relatively low, and it will shrink the strength of 28 d. The incorporation of the early-strength agent can promote the hydration of cement at low temperature, shorten the hydration induction period, and increase the maximum heat release rate and heat release. Adding D and E early-strength agents has little effect on the workability of concrete, which meets the requirements of actual engineering construction performance and can increase the early strength of concrete to a certain extent. However, the effect of low-temperature early-strength is still limited, and adding early-strength agents will cause the later performance of concrete to decline.

英文名 : Study on the Propery of Early-strength Agent of Concrete at Low Temperature

刊期 : 2021年第7期

关键词 : 低温；早强剂；抗压强度；水化热；耐久性

Key words : Low temperature; Early-strength agent; Compressive strength; Hydration heat; Durability

刊期 : 2021年第7期

DOI : 10.19761/j.1000-4637.2021.07.001.06

文章编号 :

基金项目 : 国家重点研发计划项目（2018YFC0406702）；国家自然科学基金项目（51739008）；中央级公益性科研院所基本科研业务费专项（Y419004）。

作者 : 张丰，白银，陈波，宁逢伟，吕乐乐，胡海明

单位 : 南京水利科学研究院水文水资源与水利工程科学国家重点实验室，江苏南京 210029

张丰，白银，陈波，宁逢伟，吕乐乐，胡海明

张丰,白银,陈波,等.混凝土早强剂低温性能试验研究[J].混凝土与水泥制品,2021(7):1-6.

ZHANG F,BAI Y,CHEN B,et al.Study on the Propery of Early-strength Agent of Concrete at Low Temperature[J].CHINA CONCRETE AND CEMENT PRODUCTS,2021(7):1-6.





摘要

参数

结论

参考文献

引用本文

Abstract: The performance differences of five kinds of commercial concrete early-strength agents at low temperature were compared from the perspectives of compressive strength, setting time, hydration heat, and workability and durability of concrete, and the application effect of the early-strength agents currently on the market was evaluated. The results show that under 5 ℃ curing, the early-strength agent can increase the strength of the mortar to a certain extent, but the strength of 1 d is still relatively low, and it will shrink the strength of 28 d. The incorporation of the early-strength agent can promote the hydration of cement at low temperature, shorten the hydration induction period, and increase the maximum heat release rate and heat release. Adding D and E early-strength agents has little effect on the workability of concrete, which meets the requirements of actual engineering construction performance and can increase the early strength of concrete to a certain extent. However, the effect of low-temperature early-strength is still limited, and adding early-strength agents will cause the later performance of concrete to decline.

扫二维码用手机看

[1] 谢兴建.混凝土早强剂应用技术研究[J].新型建筑材料,2005(5):33-35.
[2] LEUNG C,PHEERAPHAN T.Very high early strength of microwave cured concrete[J].Cement and Concrete Research,1995,25(1):136-146.
[3] 吴蓬,吕宪俊,梁志强,等.混凝土早强剂的作用机理及应用现状[J].金属矿山,2014(12):20-25.
[4] 王宗廷,俞然刚.固体醇胺混凝土早强剂研制[J].混凝土与水泥制品,1999(2):19-20.
[5] 张云理,卞葆芝,阮晓蔚,等.硫酸钠系早强外加剂对混凝土耐久性影响的研究(下)[J].混凝土与水泥制品,1992(4):8-11.
[6] 李献民,谭金海,雷成慧.三乙醇胺在混凝土工程中的应用[J].电力建设,1995(2):40-41.
[7] 卞葆芝,张云理.金星系列早强外加剂性能的研究[J].混凝土,1992(5):37-48.
[8] DACZKO J A,KURTZ M A,DULZER M.High early-strength fiber reinforced cementitious composition:6942727[P].2005-09-13.
[9] 陈子川.低温混凝土早强剂:201110049598[P].2011-03-02.
[10] 詹镇峰,陈峭卉,李从波,等.一种混凝土复合超早强剂及其使用方法:201510894979.6[P].2015-12-07.
[11] 朱江林,冯克满,王同友,等.一种深水固井用低温早强剂：201010293396[P].2010-09-27.
[12] 刘庆旺,徐卫强,高亭松,等.新型油井水泥低温早强剂QZ-1性能评价[J].科学技术与工程,2010,10(34):8521-8523.
[13] 步玉环,侯献海,郭胜来.低温固井水泥浆体系的室内研究[J].钻井液与完井液,2016,33(1):79-83.
[14] KNTOLEONTOS F,TSAKIRIDIS P E,MARINOS A.Influence of colloidal nanosilica on ultrafine cement hydration: Physicochemical and microstructural characterization[J].Construction and Building Materials,2012,35:347-360.
[15] 黄天勇.微量化学外加剂对硅酸盐水泥强度的影响及作用机理[D].北京:中国矿业大学,2014.
[16] 王璁.盐类对混凝土早期收缩性能的影响[D].哈尔滨:哈尔滨工业大学,2009.
[17] 尤启俊,于冬勋,黄爱平.混凝土收缩开裂与减缩防裂剂的研究[J].混凝土,2000(7):29-31.
[18] 巴恒静,刘志国,陈文松,等.硫酸钠掺量对混凝土早期收缩开裂的影响[J].硅酸盐学报,2005,33(1):36-41.
[19] 张丰,白银,蔡跃波,等.混凝土低温早强剂研究现状[J].材料导报,2017,31(21):106-113.
[20] HUANG Y H,ZHANG T C.Nitrite reduction and formation of corrosion coating in zerovalent iron systems[J].Water Research,2006,40(16):3075-3082.
[21] 刘浪涛,邵式亮,许金余,等.混凝土防冻剂的研究进展[J]. 材料导报,2015,29(7):102-107.
[22] 王玉锁,叶跃忠,钟新樵,等.新型混凝土早强剂的应用研究现状[J].四川建筑,2005(4):105-106.
[23] 柳俊哲,太星镐,野口贵文.掺防冻剂混凝土中亚硝酸盐的长期阻锈效果[J].混凝土,2004(9):14-17.
[24] 曹忠露,肖鹏,日比野诚.亚硝酸钙阻锈剂的应用研究综述[J].混凝土,2011(10):49-54.
[25] 姜梅芬,吕宪俊.混凝土早强剂的研究与应用进展[J].硅酸盐通报,2014,33(10):2527-2533.
[26] 陈银洲,马保国.复合外加剂对混凝土性能的影响[J].武汉工业大学学报,1998,20(4):47-51.
[27] 黄政宇,祖天钰.纳米CaCO3对超高性能混凝土性能影响的研究[J].硅酸盐通报,2013,32(6):1103-1109.
[28] 钱峰.DSP改性水泥基灌浆材料性能研究[D].长沙:湖南大学,2009.

上一个

生态型混凝土人工鱼礁研究进展

下一个

碱激发胶凝材料的研究现状

头部文案

混凝土早强剂低温性能试验研究

相关文件