石粉对预制沉管机制砂混凝土性能的影响研究
Influence of Stone Powder on the Performance of Sand Concrete for Precast Immersed Tube Manufactured
2021年第8期
预制沉管;机制砂混凝土;石粉;混凝土性能
Precast immersed tube; Manufactured-sand concrete; Stone powder; Concrete performance
2021年第8期
10.19761/j.1000-4637.2021.08.041.04
徐 延,刘 行,李 超,胡文刚
中交四航工程研究院有限公司,广东 广州 510230

徐 延,刘 行,李 超,胡文刚

徐延,刘行,李超,等.石粉对预制沉管机制砂混凝土性能的影响研究[J].混凝土与水泥制品,2021(8):41-44.

XU Y,LIU H,LI C,et al.Influence of Stone Powder on the Performance of Sand Concrete for Precast Immersed Tube Manufactured[J].CHINA CONCRETE AND CEMENT PRODUCTS,2021(8):41-44.

浏览量:
1000
摘   要:研究了石粉含量对预制沉管机制砂混凝土工作性、力学性能等的影响。结果表明:石粉含量过大会导致混凝土拌和物含气量下降、黏聚性提高、流动性降低;石粉在混凝土中主要起填充作用,当石粉含量在10%左右时,混凝土的力学性能和抗氯离子渗透性较好;石粉含量过大会导致混凝土塑性开裂敏感性提高,但在合适养护条件下,机制砂可提高混凝土的抗裂性能;混凝土的干燥收缩率随石粉含量和龄期增加而上升,石粉含量为10%时,混凝土的60 d干燥收缩率为311×10-6;石粉对引气高性能混凝土抗冻性的影响不显著,但随石粉含量增加而下降。 Abstract: The effect of stone powder on the workability and mechanical properties of precast immersed tube manufactured-sand concrete was studied. The results show that stone powder reduces the entrained air content of concrete, increases cohesiveness and reduces fluidity. Stone powder primarily plays a role of micro-aggregate filling. When the stone powder content is about 10%, the mechanical performance and the resistance to chloride ion diffusion are the best. Stone powder enhances the plastic cracking sensitivity of concrete, but the manufactured sand is beneficial to advance the crack resistance of concrete under good curing. The drying shrinkage rate of concrete rises with stone powder content increasing. When the stone powder content is 10%, the 60 d drying shrinkage rate is 311×10-6. The influence of stone powder on the frost resistance of air-entrained high performance concrete is not significant, but it appears to decrease with the increase of stone powder content.
英文名 : Influence of Stone Powder on the Performance of Sand Concrete for Precast Immersed Tube Manufactured
刊期 : 2021年第8期
关键词 : 预制沉管;机制砂混凝土;石粉;混凝土性能
Key words : Precast immersed tube; Manufactured-sand concrete; Stone powder; Concrete performance
刊期 : 2021年第8期
DOI : 10.19761/j.1000-4637.2021.08.041.04
文章编号 :
基金项目 :
作者 : 徐 延,刘 行,李 超,胡文刚
单位 : 中交四航工程研究院有限公司,广东 广州 510230

徐 延,刘 行,李 超,胡文刚

徐延,刘行,李超,等.石粉对预制沉管机制砂混凝土性能的影响研究[J].混凝土与水泥制品,2021(8):41-44.

XU Y,LIU H,LI C,et al.Influence of Stone Powder on the Performance of Sand Concrete for Precast Immersed Tube Manufactured[J].CHINA CONCRETE AND CEMENT PRODUCTS,2021(8):41-44.

摘要
参数
结论
参考文献
引用本文

摘   要:研究了石粉含量对预制沉管机制砂混凝土工作性、力学性能等的影响。结果表明:石粉含量过大会导致混凝土拌和物含气量下降、黏聚性提高、流动性降低;石粉在混凝土中主要起填充作用,当石粉含量在10%左右时,混凝土的力学性能和抗氯离子渗透性较好;石粉含量过大会导致混凝土塑性开裂敏感性提高,但在合适养护条件下,机制砂可提高混凝土的抗裂性能;混凝土的干燥收缩率随石粉含量和龄期增加而上升,石粉含量为10%时,混凝土的60 d干燥收缩率为311×10-6;石粉对引气高性能混凝土抗冻性的影响不显著,但随石粉含量增加而下降。

Abstract: The effect of stone powder on the workability and mechanical properties of precast immersed tube manufactured-sand concrete was studied. The results show that stone powder reduces the entrained air content of concrete, increases cohesiveness and reduces fluidity. Stone powder primarily plays a role of micro-aggregate filling. When the stone powder content is about 10%, the mechanical performance and the resistance to chloride ion diffusion are the best. Stone powder enhances the plastic cracking sensitivity of concrete, but the manufactured sand is beneficial to advance the crack resistance of concrete under good curing. The drying shrinkage rate of concrete rises with stone powder content increasing. When the stone powder content is 10%, the 60 d drying shrinkage rate is 311×10-6. The influence of stone powder on the frost resistance of air-entrained high performance concrete is not significant, but it appears to decrease with the increase of stone powder content.

扫二维码用手机看
未找到相应参数组,请于后台属性模板中添加

(1)石粉会降低混凝土拌和物的含气量,含气量每降低1%,表观密度提高22 kg/m3。石粉能够提高拌和物的黏聚性和保水性,有利于改善混凝土离析、泌水、表观粗涩的现象。
(2)机制砂混凝土的抗压强度和劈裂抗拉强度随石粉含量增加先上升后下降,氯离子扩散系数随石粉含量增加先降低后上升,石粉含量在10%左右达到最佳。
(3)石粉会增加混凝土塑形开裂敏感性,石粉含量超过7%时裂缝出现时间大幅提前,宽度显著增加。相同配合比的河砂混凝土3 d劈裂抗拉强度较10%石粉含量的机制砂混凝土低25.7%,机制砂有利于提高混凝土的抗裂性。
(4)石粉含量越大,混凝土的浆体含量越多,骨架对水泥石变形的限制能力减弱,干燥收缩越大,石粉含量为10%的机制砂混凝土60 d干燥收缩值为311×10-6。
(5)石粉含量对抗冻性的影响不明显,但抗冻性表现出随石粉含量的增加而减弱的趋势。

[1] 张礼华,刘来宝,周永生,等.石粉含量对机制砂混凝土力学性能与微观结构的影响[J].混凝土与水泥制品,2011(12):22-26.
[2] 郭育霞,贡金鑫,李晶.石粉掺量对混凝土力学性能及耐久性的影响[J].建筑材料学报,2009(3):266-271.
[3] ZHOU M K,PENG S M,XU J,et al.Effect of Stone Powder on Stone Chippings Concrete[J].Journal of Wuhan University of Technology,1996,11(4):29-34.
[4] 蒋正武,梅世龙,任强.机制砂高性能混凝土[M].北京:化学工业出版社,2020.
[5] 郭庆伟.岩石基矿物掺合料对水泥基胶凝材料性能影响研究[D].长沙:中南大学,2014.
[6] 王稷良,田波,柯国炬,等.机制砂及石粉含量对路面水泥混凝土耐磨性的影响研究[J].公路,2011(7):213-217.
[7] 鲁铂特·斯普林根施密特.混凝土早期温度裂缝的预防[M].赵筠,译.北京:中国建材工业出版社,2019.
[8] 周丰.机制砂混凝土早龄期热膨胀系数研究[D].福州:福州大学,2013.
[9] KIM J K,LEE C S,PARK C K,et al.The fracture characteristics of crushed limestone sand concrete[J].Cement and Concrete Research,1997,27(11):1719-1729.
[10] CELIK T, MARAR K.Effects of crushed stone dust on some properties of concrete[J].Cement and Concrete Research,1996, 26(7):1121-1130.

徐延,刘行,李超,.石粉对预制沉管机制砂混凝土性能的影响研究[J].混凝土与水泥制品,2021(8):41-44.

XU Y,LIU H,LI C,et al.Influence of Stone Powder on the Performance of Sand Concrete for Precast Immersed Tube Manufactured[J].CHINA CONCRETE AND CEMENT PRODUCTS,2021(8):41-44.

相关文件

暂时没有内容信息显示
请先在网站后台添加数据记录。

关注《混凝土与水泥制品》

总访问量 468,401   网站统计

官方微信公众号关闭
苏州混凝土水泥制品研究院有限公司

关于我们    |    联系我们    |    订购杂志    |    回到顶部

版权所有:中国混凝土与水泥制品网  苏ICP备10086386号   网站建设:中企动力 苏州

版权所有:中国混凝土与水泥制品网

苏ICP备10086386号

网站建设:中企动力 苏州